Conclusions
-
1.
Plastic deformation together with rapid coding of KhN77TYuR, VT3-1, and 1Kh12N2VMF alloys leads to a considerable improvement of the mechanical properties. This improvement results from the fragmentation of particles of the strengthening phases, a more complete decomposition of the solid solution, and the change in the structure of the alloy.
-
2.
Combined treatment increases the diffusion rate of elements in the alloys, which prohibits the use of this method of strengthening at high temperatures.
Similar content being viewed by others
Literature cited
L. V. Smirnov, E. N. Sokolkov, and V. D. Sadovskii, Trudy Instituta fiziki metallov UFAN SSSR, No. 18 (1956).
E. N. Sokolkov, M. G. Lozinskii, and E. I. Antipova, MiTOM, No. 11 (1958).
É. L. Demina, Dai Tu-Fu, and M. L. Bernshtein, in Coll: Reports of the Conference on Heat Resistance Alloys, Izd. AN SSSR (1961).
S. T. Kishkin, S. Z. Bokshtein, et al., MiTOM, No. 1 (1962).
D. Ya. Kogan, MiTOM, No. 1 (1962).
S. A. Shigarev, MiTOM, No. 1 (1962).
I. A. Oding and É. G. Fridman, Izd. AN SSSR, OTN, Metallurgiya i toplivo, No. 5 (1961).
Additional information
Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 5, pp. 40–44, May, 1963
This work was done in collaboration with V. M. Arzhakov, A. V. Bulanov, L. G. Vertyukova, Korableva, L. M. Mirskii, O. N. Podvoiskaya, T. N. Sazonova, O. P. Solonina, I. I. Titarenko, L. P. Rink, M. N. Kozlova, M. I. Ermolova, and L. M. Moroz.
Rights and permissions
About this article
Cite this article
Bokshtein, S.Z., Kishkin, S.T., Nikishov, A.S. et al. Aging of plastically deformed alloys. Met Sci Heat Treat 5, 282–286 (1963). https://doi.org/10.1007/BF00649338
Issue Date:
DOI: https://doi.org/10.1007/BF00649338