Conclusions
-
1.
Annealing of hot-rolled steel Kh15N5D2T at 580–700°C leads to the α→γ transformation, accompanied by higher plasticity.
-
2.
After normalization and low-temperature aging the steel is strengthened as the result of the martensitic transformation and the precipitation of excess intermetallic phase.