Abstract
In an effort to clarify the role of controlled oxygen exposure in the synthesis of LaBa2Cu3Oy samples which achieve zero resistivity above 90 K, we have prepared samples of La(1+x)Ba(2−x)Cu3Oy with x approximately equal to 0 and with y varying between 6.22 and 7.00. We find that for large values of y, 6.88<y<7.00, the value of the superconductive critical temperature is strongly dependent on synthetic conditions. Synthetic conditions promoting orthorhombic crystal structures consistent with oxygen ordering in the basal planes of the crystal produce materials with the highest values of the zero-resistance temperature.
Similar content being viewed by others
References
S.G. Brass, M.H. Ghandehari: Appl. Phys. Lett.53, 2235 (1988)
T. Wada, N. Suzuki, T. Maeda, A. Maeda, S. Uchida, K. Uchinokura, S. Tanaka: Appl. Phys. Lett.52, 1989 (1988)
R.L. Meng, P.H. Hor, Y.Q. Wang, Z.J. Juang, Y.Y. Sun, L. Gao, J. Bechtold, C.W. Chu: “Extended Abstracts High Temperature Superconductors II”, Reno, NV (April 1988) pp.223–225
A. Maeda, T. Nobe, H. Matsumoto, T. Wada, M. Izumi, T. Yabe, K. Uchinokura, S. Tanaka: J. Appl. Phys.64, 4095 (1988)
If samples are not sintered in an oxygen atmosphere immediately after being sintered in a nitrogen atmosphere, their phase composition is substantially altered.
T. Wada, N. Suzuki, T. Maeda, A. Maeda, S. Uchida, K. Uchinokura, S. Tananka: Phys. Rev. B38, 7080 (1988)
Y. Song, J.P. Golben, X.D. Chen, J.R. Gaines, M.S. Wong, E.R. Kreidler: Phys. Rev. B38, 2858 (1988)
C.U. Segre, B. Dabrowski, D.G. Hinks, K. Zhang, J.D. Jorgensen, M.A. Beno, I.K. Schuller: Nature329, 237 (1987)
Y. Song, J.P. Golben, S. Chittipeddi, J.R. Gaines, A.J. Epstein: Phys. Rev. B38, 4605 (1988)
S.G. Brass, M.H. Ghandehari: unpublished
J.D. Jorgensen, B.W. Veal, W.K. Kwok, G.W. Crabtree, A. Umezawa, L.J. Nowicki, A.P. Paulikas: Phys. Rev. B36, 5731 (1937)
R.J. Cava, B. Batlogg, C.H. Chen, E.A. Rietman, S.M. Zahurak, D. Werder: Phys. Rev. B36, 5719 (1987)
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Brass, S.G., Ghandehari, M.H. The effect of oxygen ordering through controlled exposure to oxygen on the superconductive properties of LaBa2Cu3Oy . Appl. Phys. A 48, 401–404 (1989). https://doi.org/10.1007/BF00618906
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00618906