Diffusion of Au and Cu in amorphous Fe₈₀B₂₀ and Fe₈₂B₁₈ alloys

Abstract

Diffusion rates (D) of Au in two amorphous alloys, Fe₈₀B₂₀ and Fe₈₂B₁₈, and of Cu in amorphous Fe₈₂B₁₈ alloy were measured in the temperature range 546–645 K by using the technique of Rutherford backscattering spectrometry (RBS) and Auger electron spectroscopy (AES), respectively. The diffusion of Au was found to be ∼3 to 6 times faster in Fe₈₀B₂₀ than in Fe₈₂B₁₈, though both the alloys had almost similar crystallization temperatures. The observed differences in the diffusion rates corroborate the fact that Fe₈₀B₂₀ has a more open structure than Fe₈₂B₁₈ as revealed from the reported values of the metal packing fractions of these two alloys. Also, the diffusivities of smaller sized Cu atoms (radius: 0.128 nm) were found to be higher by more than an order of magnitude than those of larger sized Au atoms (radius: 0.146 nm), suggesting a dependence ofD on the size of the diffusing species.