Abstract
The Warren Averbach technique was used to determine the RMS strain profile in the Al2O3 matrix surrounding ZrO2 particles in zirconia toughened alumina. The X-ray domain size was found to be ∼100nm in all but the most severely microcracked sample. The RMS strain, averaged over all domains, decreased nearly linearly from the edge of the domain (presumably from the ZrO2 particle), except when microcracking was detected and then the RMS strain level was reduced near the surface of the domain. The maximum RMS strain level increased with increasing ZrO2 particle size up to the point where microcracking occurred then decreased. The results were explained by noting that the maximum RMS strain was directly related to the monoclinic content of the sample.
Similar content being viewed by others
References
A. H. Heuer andM. Ruhle,Ada Metall. 33 (1985) 761.
F. F. Lange,J. Mater. Sci. 17 (1982) 225.
K. R. Wilfinger andW. R. Cannon,J. Am. Ceram. Soc. 72 (1989) 1256.
I-Wie Chen andP. E. Reyes-Morel, in “Mater. Res. Soc. Symp. Proceedings, Vol. 78,Advanced Structural Ceramics, edited by P. F. Becher, M. V. Swain, and S. Somiya, (Materials Research Society, Pittsburgh, 1987).
A. G. Evans, N. Burlingame, M. Drory andW. M. Kriven,Acta Metall. 29 (1981) 447.
I.-W Chen andY.-H. Chiao,Acta Metall. 13 (1983) 1627.
S. Schmauder, W. Mader andM. Ruhle, in “Advances of Ceramics, 12”, edited by N. Claussen, M. Ruhle, and A. H. Heuer, (Am. Ceram. Soc. (1984)) p. 251.
T. Tsakalakos, “Micromechanics and Inhomogeneities”, edited by G. J. Wang (Springer-Verlag, New York, 1990) p. 469.
W. M. Kriven, in “Advances of Ceramics 12”, edited by N. Claussen, M. Ruhle, and A. H. Heuer, (Am. Ceram. Soc. 1984) p. 64.
B. E. Warren andB. L. Averbach,J. Appl. Phys. 21 (1950) 595–99.
M. C. Bhardwaj, Company Publication, Ultran Laboratories Inc., State College, PA (1985).
D. L. Porter andA. H. Heuer,J. Am. Ceram. Soc. 62 (1979) 298.
M. Ruhle, private communications.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Wilfinger, K.R., Cannon, W.R. & Tsakalakos, T. RMS matrix strains in transformation toughened alumina. J Mater Sci 25, 4401–4404 (1990). https://doi.org/10.1007/BF00581099
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00581099