, Volume 25, Issue 12, pp 5063–5069 | Cite as

Solute partitioning on solidification of nickel-base ternary alloys

  • A. Kagawa
  • M. Hirata
  • Y. Sakamoto
Papers

Abstract

The coefficients for equilibrium partition of solute elements between solid and liquid were determined in nickel-base ternary alloys rapidly quenched from a coexisting solid-liquid state. A satisfactory accordance was observed between experimentally and theoretically determined partition coefficients, and factors influencing the ternary partition coefficients were clarified by a thermodynamic procedure. The availability of thermodynamic evaluation of the equilibrium partition coefficient was elucidated for application to nickel-base multicomponent alloys.

Keywords

Polymer Partition Coefficient Solute Element Ternary Alloy Equilibrium Partition 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    R. Sellamuthu andA. F. Giamei,Met. Trans. 17A (1986) 419.Google Scholar
  2. 2.
    M. A. Taha andW. Kurz,Z. Metallkde 72 (1981) 546.Google Scholar
  3. 3.
    I. L. Svetlov, N. V. Petrushin, V. A. Fedorov andN. P. Abalakin,Phys. Met. Metall. 57 (1984) 111.Google Scholar
  4. 4.
    K. M. Delargy andG. D. W. Smith,Met. Trans. 14A (1983) 1771.Google Scholar
  5. 5.
    M. Sittner,J. Crystal Growth 65 (1983) 299.Google Scholar
  6. 6.
    A. Kagawa, S. Moriyama andT. Okamoto,J. Mater. Sci. 17 (1982) 135.Google Scholar
  7. 7.
    T. B. Massalsky, “Binary Alloy Phase Diagrams” (ASM, New York, 1986) p. 1756.Google Scholar
  8. 8.
    E. Scheil,Z. Metallkde 34 (1942) 70.Google Scholar
  9. 9.
    T. Okamoto, Z. Morita, A. Kagawa andT. Tanaka,Trans. Iron Steel Inst. Jpn 23 (1983) 266.Google Scholar
  10. 10.
    L. Kaufman andH. Nessor,Z. Metallkde 64 (1973) 249.Google Scholar
  11. 11.
    Idem, CALPHAD 2 (1978) 55.Google Scholar
  12. 12.
    Idem, ibid. 2 (1978) 81.Google Scholar
  13. 13.
    Idem, ibid. 2 (1978) 325.Google Scholar
  14. 14.
    Idem, ibid. 3 (1979) 45.Google Scholar

Copyright information

© Chapman and Hall Ltd. 1990

Authors and Affiliations

  • A. Kagawa
    • 1
  • M. Hirata
    • 1
  • Y. Sakamoto
    • 1
  1. 1.Department of Materials Science and EngineeringNagasaki UniversityNagasakiJapan

Personalised recommendations