Anwendung der Taylor-Theorie auf die Regelung von kubischen Mineralen

  • Heinrich Siemes
Article

Application of the Taylor theory on the development of preferred orientation of cubic minerals

Abstract

After compressive axialsymmetric deformation galena, halite, fluorite, sphalerite and magnetite show preferred orientation of the lattice. In all minerals the 〈110〉 direction is aligned with the axis of compression, but halite shows a second component with 〈100〉 parallel to the axis of compression. In extension tests of halite the 〈111〉 direction is aligned with the axis of the specimen. All these preferred orientations are consistent with the Taylor-theory of preferred orientation for axialsymmetric flow of metals.

In order to make use of the extended and improved versions of the Taylor-theory it is necessary to get more data on the behaviour of single crystals during deformation and to have complete quantitative polefigures of deformed mineral specimens which permit the calculaton of the orientation distribution function and inverse polefigures.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

Literatur

  1. Baker, D., W., Wenk, H. R., Christie, J. M.: X-ray analysis of preferred orientation in finegrained quartz aggregates. J. Geol.77, 144–172 (1969)Google Scholar
  2. Bunge, H. J.: Mathematische Methoden der Texturanalyse, 330 S. Berlin: Akademie-Verlag, 1969Google Scholar
  3. Bunge, H. J.: Some applications of the taylortheory of polycrystal plasticity. Kristall u. Technik5, 145–175 (1970)Google Scholar
  4. Carter, N. L., Heard, H. C.: Temperature and rate dependent deformation of halite. Am. J. Sci.269, 193–249 (1970)Google Scholar
  5. Chin, G. Y.: Tension and compression textures. In: Textures in research and practice. J. Grewen, G. Wassermann eds., p. 51–80. Berlin-Heidelberg-New York: Springer 1969Google Scholar
  6. Chin, G. Y., Mammel, W. L., Dolan, M. T.: Taylor's theory of texture for axisymmetric flow in body centered metals. Trans. Met. Soc. AIME239, 1854–1855 (1967)Google Scholar
  7. Dwiggins, L. J., Rogers, W. J., Williams, R. O.: Effect of strain rate and temperature on the compression texture of aluminium. Trans. Met. Soc. AIME218, 1133–1134 (1960)Google Scholar
  8. Groves, G. W., Kelly, A.: Independent slip systems. Phil. Mag.8, 877–878 (1963)Google Scholar
  9. Grühn, A.: Künstliche Zwillingsbildung des Magnetits. Neues Jahrb. Mineral. Geol. Paläont. 99–112 (1918)Google Scholar
  10. Kern, H., Braun, G.: Deformation und Gefügeregelung von Steinsalz im Temperaturbereich 20–200° C. Contr. Mineral and Petrol.40, 169–181 (1973)Google Scholar
  11. Kleinstück, K., Tobisch, J.: Die Methode der Texturuntersuchung mittels Neutronenbeugung und ihre besonderen Anwendungsvorteile. Kristall u. Technik3, 455–466 (1968)Google Scholar
  12. Lang, H.: Stauchversuche mit polykristallinen Kupferkiesen und deren Ergebnisse unter Berücksichtigung der Gefügeregelung. Dissertation TH-Aachen, 211 S. (1968)Google Scholar
  13. Lyall, K. D., Paterson, M. S.: Plastic deformation of galena (lead sulphide). Acta Met.14, 371–383 (1969)Google Scholar
  14. Mises, R. v.: Mechanik der plastischen Formänderung von Kristallen. Z. Angew. Math. Mech,8, 161–185 (1928)Google Scholar
  15. Müller, P., Siemes, H.: Zur Festigkeit und Gefügeregelung von experimentell verformten Magnetiterzen. Neues Jahrb. Mineral. Abhandl.117, 39–60 (1972)Google Scholar
  16. Pauly, H., Siemes, H.: Microhardness of galena related to Ag-Bi-content, orientation and deformation. Bull. Geol. Soc. Denmark22, 50–78 (1973)Google Scholar
  17. Roy, C.: Plasticity of calcium fluoride. Ph. D.-Thesis, London (1962)Google Scholar
  18. Saynisch, H. J.: Festigkeits- und Gefügeuntersuchungen an Zinkblenden. Dissertation THA-achen, 102 S. (1967)Google Scholar
  19. Saynisch, H. J.: Festigkeits- und Gefügeuntersuchungen an experimentell und natürlich verformten Zinkblendeerzen, In: Experimentelle und natürliche Gesteinsverformung, P. Paulitsch Hrsg., S. 209–252. Berlin-Heidelberg-New York: Springer 1970Google Scholar
  20. Siemes, H.: Die Endlagen bei der Stauch- und Zugverformung von polykristallinen Metallen. Z. Metallk.58, 228–230 (1967)Google Scholar
  21. Siemes, H.: Experimentelle Stauchverformung von polykristallinen Bleiglanzen — Bestimmung der Festigkeitseigenschaften unter allseitigem Druck zwischen 1 und 5000 bar sowie röntgenographische Untersuchung der auftretenden Texturen. — Habil. Schrift, TH-Aachen, 115 S. (1967)Google Scholar
  22. Siemes, H.: Experimental deformation of galena ores. In: P. Paulitsch, ed., Experimental and natural rock deformation, p. 165–208, Berlin-Heidelberg-New York: Springer 1970Google Scholar
  23. Siemes, H.: Anfertigung von quantitativen Gefügediagrammen mit Hilfe von Messungen mit dem Röntgentexturgoniometer. Clausthaler Tekt. Hefte10, 293–298 (1970)Google Scholar
  24. Siemes, H., Saynisch, H. J., Borges, B.: Experimentelle Verformung von Zinkblendeeinkristallen bei Raumtemperatur und 5000 bar Manteldruck. Neues Jahrb. Mineral. Abhandl.119, 65–82 (1973)Google Scholar
  25. Taylor, G. I.: Plastic strain in metals. J. Inst. Metals62, 307–324 (1938)Google Scholar
  26. Taylor, G. I.: Strains in crystalline aggregate IUTAM. Colloquium, Madrid 1955, p. 3–12. In: Verformung und Fließen des Festkörpers. Berlin-Heidelberg-New York: Springer (1956)Google Scholar
  27. Wassermann, G., Grewen, J.: Texturen metallischer Werkstoffe, 2. Aufl., 808 S. Berlin-Heidelberg-New York: Springer 1962Google Scholar

Copyright information

© Springer-Verlag 1974

Authors and Affiliations

  • Heinrich Siemes
    • 1
  1. 1.Institut für Mineralogie und LagerstättenlehreTechn. Hochschule AachenBundesrepublik Deutschland

Personalised recommendations