The behaviour of 316L stainless steel in hydrogen

  • D. Eliezer
Papers

Abstract

Hydrogen embrittlement of 316L type austenitic stainless steel has been studied by charging thin tensile specimens (0.2 mm thick) with hydrogen through cathodic polarization. The effects of hydrogen on the phase transition and the relative role of the metallurgical variables is discussed. Room temperature cathodic charging of unstressed specimens produces intergranular and secondary transgranular cracks along crystallographic planes. Severe grain boundary spelling has been observed at longer times of charging indicating that high stresses were formed. The surface cracking that was observed during the ageing is consistent with the development of high tensile surface stresses. TEM studies of the fracture surfaces of both annealed and sensitized, fine and coarse grain size, have revealed high dislocation structure. Thin plates of hydrogen inducedε (h c p)-martensite was observed. These plates appear in a heavily faulted region. The evidence of faults withinε-plates indicates that the overlapping stacking fault mechanism for the austenite toε transformation is in agreement with strain inducedε. The results of the tensile tests while undergoing cathodic charging show that the additional sensitization treatment and coarse-grained samples, lower the mechanical properties. The fracture surfaces of the sensitized steel contains regions of intergranular fracture where the micromechanism of the failure is microvoid nucleation and coalescence along grain boundaries. Finally, the microstructures are connected to various modes of cracking.

Keywords

Austenite Martensite Austenitic Stainless Steel Hydrogen Embrittlement Intergranular Fracture 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    J. Kolts, ASTM Publication ASTM STP 610 (ASTM, Pennsylvania, 1976) p. 336.Google Scholar
  2. 2.
    M. R. Louthan Jr, “Hydrogen in Metals”, edited by I. M. Bernstein and A. W. Thompson (ASM, Metals Park, Ohio, 1974) p. 54.Google Scholar
  3. 3.
    A. W. Thompson, “Environment-Sensitive Fracture of Engineering Materials”, edited by A. Z. Foroulis (AIME, Warrendale, PA. 1979) p. 379.Google Scholar
  4. 4.
    D. Eliezer, D. G. Chakrpani, C. J. Altstetter andE. N. Pugh,Met. Trans. 10A (1979) 935.Google Scholar
  5. 5.
    E. Minkovitz andD. Eliezer,J. Mater. Sci. 17 (1982) 3165.Google Scholar
  6. 6.
    N. Narita, C. J. Altstetter andH. K. Birnbaum,Met. Trans. 13A (1982) 1355.Google Scholar
  7. 7.
    R. B. Benson, R. K. Dann andL. W. Roberts Jr,Trans. TMS-AIME 272 (1967) 2199.Google Scholar
  8. 8.
    C. L. Briant,Metall. Trans. 10A (1979) 181.Google Scholar
  9. 9.
    E. Minkovitz andD. Eliezer,J. Mater. Sci. Lett. 1 (1982) 192.Google Scholar
  10. 10.
    B. C. Odegard, J. A. Brooks andA. J. West, “Effect of Hydrogen on Behavior of Materials”, edited by A. W. Thompson and I. M. Bernstein (TMS, New York, NY, 1976) p. 116.Google Scholar
  11. 11.
    A. J. West andM. R. Louthan Jr,Metall. Trans. 10A (1979) 1675.Google Scholar
  12. 12.
    M. R. Louthan Jr, G. R. Caskey Jr, J. A. Donovan andD. E. Rawl Jr,Mater. Sci. Eng. 10 (1972) 357.Google Scholar
  13. 13.
    J. A. Brooks andM. R. Louthan Jr,Metall. Trans. 11A (1980) 1981.Google Scholar
  14. 14.
    A. W. Thompson andJ. A. Brooks,Metall. Tram. 6A (1975) 1931.Google Scholar
  15. 15.
    E. Minkovitz andD. Eliezer,Scripta Metall. 16 (1982) 981.Google Scholar
  16. 16.
    R. M. Vennet andG. S. Ansell,Trans. ASM 60 (1967) 242.Google Scholar
  17. 17.
    N. Narita andH. K. Birnbaum,Scripta Metall. 14 (1980) 1355.Google Scholar
  18. 18.
    T. Takayama andM. Takano,Corrosion 38 (1982) 1.Google Scholar
  19. 19.
    A. Indue, Y. Hossoya andT. Nasumoto,Trans. Iron Steel Inst., Jpn. 19 (1979) 170.Google Scholar
  20. 20.
    M. L. Holzworth,Corrosion 25 (1969) 107.Google Scholar
  21. 21.
    R. Lagneborg,J. Iron Steel Inst. 207 (1969) 363.Google Scholar
  22. 22.
    H. E. Hanninen,Int. Met. Rev. 27 (1979) 85.Google Scholar
  23. 23.
    A. J. West Jr andM. R. Louthan Jr,Metall. Tran 13A (1982) 2049.Google Scholar
  24. 24.
    A. W. Thompson, “Environmental Degradation of Engineering Materials”, edited by M. R. Louthan Jr and R. P. McNitt (Virginia Polytechnic Institute, Blacksburg, VA, 1977.Google Scholar
  25. 25.
    C. L. Briant, “Hydrogen Effects in Metals”, edited by I. M. Bernstein and A. W. Thompson (TMS-AIME, Pennsylvania, 1980) p. 527.Google Scholar
  26. 26.
    H. Hanninen, T. Hakkarainen andP. Nenonen,ibid.“ p. 575.Google Scholar
  27. 27.
    C. L. Briant andA. M. Ritter,Scripta Metall. 13 (1979) 177.Google Scholar
  28. 28.
    ASTM Standard Number E8.Google Scholar
  29. 29.
    M. Rigsbee,Metallography 11 (1978) 493.Google Scholar
  30. 30.
    D. Eliezer, “Hydrogen Effects in Metals”, edited by I. M. Bernstein and A. W. Thompson (AIME, Warrendale, PA, 1981) p. 565.Google Scholar
  31. 31.
    P. Rozenak, L. Zevin andD. Eliezer,J. Mater. Sci. Lett. in press.Google Scholar
  32. 32.
    Idem, to be published.Google Scholar
  33. 33.
    A. Kummick andH. Johnson,Metall. Trans. 6A (1975) 1087.Google Scholar
  34. 34.
    M. Louthan andR. Derrick,Corros. Sci. 15 (1975) 565.Google Scholar
  35. 35.
    P. Studebaker, C. Altstetter andW. Conley, “Hydrogen Effects in Metals”, edited by I. M. Bernstein and A. W. Thompson (AIME Warrendale, PA, 1981) p. 169.Google Scholar
  36. 36.
    A. Atrens, J. Bellina, N. Fiore andR. Coyle, “The Metal Science of Stainless Steels”, edited by E. Collings and H. King (AIME, New York, NY, 1979) p. 54.Google Scholar
  37. 37.
    C. L. Briant,Scripta Metall. 12 (1978) 541.Google Scholar
  38. 38.
    I. M. Bernstein andA. W. Thompson, “Alloy and Microstructural Design”, edited by J. K. Tien and G. S. Ansell (Academic Press, New York, 1976) Chap. 9, p. 303.Google Scholar
  39. 39.
    E. Minkovitz, M. Talianker andD. Eliezer,J. Mater. Sci. 16 (1981) 3506.Google Scholar
  40. 40.
    J. B. Brooks, N. H. Loretto andR. E. Smallman,Acta Metall. 27 (1979) 1839.Google Scholar
  41. 41.
    R. Lagneborg,ibid. 12 (1964) 823.Google Scholar

Copyright information

© Chapman and Hall Ltd. 1984

Authors and Affiliations

  • D. Eliezer
    • 1
  1. 1.Department of Materials EngineeringBen-Gurion University of the NegevBeer ShevaIsrael

Personalised recommendations