Conclusions
By x-ray analysis, we have confirmed the previously expressed hypothesis of a forced deformation of SÉVA on flow of an SÉVA—SPA mixture as a result of specific interaction of the components at the interface: the degree of orientation of the SÉVA macromolecules in the microfibres is higher than in a monofilament from the starting polymer.
It has been shown that ultrathin SÉVA fibres are characterized by a porosity, caused by micro- and macro-hollows, which causes a decrease in their strength as compared with the strength of ordinary SÉVA fibres.
Similar content being viewed by others
Literature cited
M. V. Tsebrenko, A. I. Benzar, and A. V. Yudin, Khim. Volokna, No. 4, 48–50 (1978).
M. V. Tsebrenko, Khim. Volokna, No. 5, 33–34 (1980).
N. M. Rezanova and M. V. Tsebrenko, Izv. Vuzov. Ser. “Tekhnol. Leg. Prom-sti,” No. 1, 41–45 (1982).
M. V. Tsebrenko, Vysokomol. Soed., Ser. A,30, No. 2, 355–357 (1988).
M. V. Tsebrenko and N. M. Rezanova, Khim. Volokna, No. 4, 14–16 (1990).
M. A. Martynov and K. A. Vylegzhanina, X-Ray Analysis of Polymers [in Russian], Khimiya, Leningrad (1972).
D. Ya. Tsvankin, Vysokomol. Soed., Ser. A,6, No. 11, 2078–2079 (1964).
M. A. Genzalov, V. S. Kuksenko, and L. I. Slutsker, Vysokomol. Soed., Ser. A,12, No. 8, 1787–1793 (1970).
Additional information
Kiev Technological Institute for Light Industry. Translated from Khimicheskie Volokna, No. 2, pp. 39–41, March–April, 1992.
Rights and permissions
About this article
Cite this article
Rezanova, N.M., Tsebrenko, M.V. & Khalfin, R.L. Structural features and properties of fibres based on mixtures of an ethylene-vinylacetate copolymer with a copolyamide. Fibre Chem 24, 134–137 (1993). https://doi.org/10.1007/BF00555032
Issue Date:
DOI: https://doi.org/10.1007/BF00555032