, Volume 27, Issue 3, pp 580–586 | Cite as

Influence of rapid quenching of the melt on structure and properties of maraging steel

  • T. A. Chernyshova
  • T. V. Lyulkina
Papers
  • 31 Downloads

Abstract

Peculiarities of structure, properties and phase transformations in the maraging steel were investigated while quenching from the liquid state. Depending on the solidification rates and subsequent cooling, the formation of highly dispersed structures in the solid phase was possible. The structures were of the following types: fully martensite, fully ferrite; a mixture of ferrite and martensite or martensite and austenite.

Keywords

Polymer Ferrite Austenite Martensite Phase Transformation 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    C. Hayzelden, J. J. Rayment andB. Cantor,Acta Metall. 31 (1983) 379.Google Scholar
  2. 2.
    J. V. Wood andC. Gagg, in “Rapidly Solidified Metastable Materials” Boston, MA, 14–17 November 1983 (1984) pp. 151–5.Google Scholar
  3. 3.
    J. V. Wood andR. W. K. Honeycombe,Phil. Mag. A 37 (1978) 501.Google Scholar
  4. 4.
    Idem., Mater. Sci. Engng23 (1976) 107.Google Scholar
  5. 5.
    Idem., ibid. 38 (1979) 217.Google Scholar
  6. 6.
    B. Cantor, in “Rapidly solidified amorphous and crystalline alloys”, edited by B. H. Kear, B. C. Giessen and M. Cohen (Elsevier Science, North Holland, NY, 1982) pp. 317–30.Google Scholar
  7. 7.
    Y. Inokuti andB. Cantor,Acta Metall. 30 (1982) 343.Google Scholar
  8. 8.
    J. V. Wood andR. W. K. Honeycombe,J. Mater. Sci. 9 (1974) 1183.Google Scholar
  9. 9.
    F. Duflos andB. Cantor, in “Rapidly quenched metals”, edited by B. Cantor (Metallurgia, Moscow, 1983) pp. 81–8.Google Scholar
  10. 10.
    Y. Lhang, F. Dubkovsky, S. Kangand andN. J. Grant,Powder Metall Int. 1 (1985) 17.Google Scholar
  11. 11.
    Y. Inokuti andB. Cantor,Scripta Metall. 10 (1976) 655.Google Scholar
  12. 12.
    Idem., J. Mater. Sci. 12 (1977) 946.Google Scholar
  13. 13.
    C. Hayzelden andB. Cantor,Int. J. Rapid. Solid. 1 (1985) 237.Google Scholar
  14. 14.
    Idem., in “Solid-Solid Phase Transformations”, edited by H. I. Aaronson, D. E. Laughlin, R. F. Sekera and C. M. Wayman (AIME, 1983) pp. 1397–1401.Google Scholar

Copyright information

© Chapman & Hall 1992

Authors and Affiliations

  • T. A. Chernyshova
    • 1
  • T. V. Lyulkina
    • 1
  1. 1.Baikov Institute of MetallurgyUSSR Academy of SciencesMoscowUSSR

Personalised recommendations