Hydrothermal corrosion of magnesiapartially-stabilized zirconia

Abstract

Changes in the phase compositions and microstructures of magnesia-partially-stabilized zirconia (Mg-PSZ) were studied in water at 80–300 °C, 1 m HCl solutions at 80–140 °C and 1 m CH₃COOH-CH₃COONa buffer solutions at pH 3 and 80–140 °C for 10–40 days. The tetragonal to monoclinic phase transformation and the degradation of the fracture strength occurred in water above 200 °C. On the other hand, although no noticeable tetragonal to monoclinic phase transformation proceeded in 1 m HCl solutions and 1 m CH₃COOH-CH₃-COONa buffer solutions at pH 3 below 140 °C, the fracture strength of Mg-PSZ greatly degraded. The dissolution of Mg²⁺ ion was observed in water above 200 °C and in 1 m HCl solutions above 80 °C.