Abstract
Interfacial segregation in bright nitrided binary α-iron alloys containing 3.0 at% Cr, 2.4 at % Mo and 3.6 at % Si were studied by Auger electron spectroscopy. Chromium, molybdenum and silicon were found to segregate to interfaces in these alloys. Segregation of chromium and molybdenum is, however, partly reduced by the formation of clusters or precipitate between nitrogen and solute atoms. Segregation of silicon is slight owing to the repulsive interaction between silicon and nitrogen atoms. It was not found that such surface active elements as sulphur and phosphorus had segregated to the interfaces in the bright nitrided alloys studied.
Similar content being viewed by others
References
C. L. Briant and S. K. Banerji, Int. Met. Rev. 23 (1978) 164.
C. Lea, M. P. Seah and E. D. Hondros, Mater. Sci. Eng. 42 (1980) 233.
G. Tauber and H. J. Grabke, Ber. Bunsenges. 82 (1978) 298.
Ph. Dumoulin and M. Guttmann, Mater. Sci. Eng. 42 (1980) 249.
M. Guttmann, Ph. Dumoulin and M. Wayman, Metall. Trans. 13A (1982) 1693.
L. E. Davis, N. C. MacDonald, P. W. Palmberg, G. E. Riach and R. E. Weber, “Handbook of Auger Electron Spectroscopy” (Physical Electronics Industries, Minnesota, 1976).
M. P. Seah and W. A. Dench, Surf. Interf. Anal. 1 (1979) 2.
M. A. Krishtal, “Diffusion Processes in Iron Alloys” (US Dept. Commerce, NBS, Washington, 1970) pp. 50–56.
K. H. Jack, in “Heat Treatment '73” (Metals Society, London, 1975) p. 39.
N. J. Pipkin, W. Roberts, D. L. Speirs, P. Grieveson and K. H. Jack, in “Chemical Metallurgy of Iron and Steel” (The Iron and Steel Institute, London, 1973) p. 351.
Ph. Dumoulin, M. Guttmann, M. Foucault, M. Palmier, M. Wayman and M. Biscondi Met. Sci. 14 (1980) 1.
Ph. Lemblé, A. Pineau, J. L. Castagne, Ph. Dumoulin and M. Guttmann, ibid. 13 (1979) 496.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Pulkkinen, R.E.E., Lähdeniemi, M. Grain boundary segregation in bright nitrided α-irons alloyed with chromium, molybdenum and silicon. J Mater Sci 18, 3421–3426 (1983). https://doi.org/10.1007/BF00544170
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00544170