Preparation of lithium aluminosilicate glass-ceramic monolith from metal alkoxide solution

Part II Conversion of gel to glass-ceramic monoliths and their properties
  • Joong-Sik Yang
  • Sumio Sakka
  • Toshinobu Yoko
  • Hiromitsu Kozuka
Papers

Abstract

Glass-ceramic monoliths with a composition of Li2O·Al2O3·4SiO2 have been synthesized by the sol-gel technique using metal alkoxides as starting materials. Heating dried gel monoliths of about 36 mm diameter and height to appropriate temperatures gave glass-ceramic monoliths of about 20 mm diameter and height without the occurrence of cracks, while a melt-derived glass body of the same composition was cracked or softened on heating. The glass-ceramic monoliths obtained by heating gel monoliths at 1000 ‡C for 40 h were a porous body, whose bulk density and porosity were 1.62 g cm−3 and 34%, respectively. On heating gel monoliths, Β-eucryptite crystals were first precipitated around 750 ‡C, followed by precipitation of Β-spodumene crystals at 830 ‡C. At higher temperatures the latter grew at the expense of the former phase. The crystallized specimens exhibited very low thermal expansion coefficient ranging from −13-12×10−7 ‡C−1 at temperatures from room temperature to 700 ‡C depending on the heat-treatment temperature of gels, indicating that a porous glass-ceramic monolith with ultra-low thermal expansion can be prepared using the present sol-gel method.

Keywords

Al2O3 Thermal Expansion Aluminosilicate Thermal Expansion Coefficient Alkoxide 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    P. W. McMillan, Glass Ceramics (Academic Press, New York, 1979).Google Scholar
  2. 2.
    J. Phalippou, M. Prassas and J. Zarzycki, J. Non-Cryst. Solids 48 (1982) 17.Google Scholar
  3. 3.
    G. Orcel, J. Phalippou and L. L. Hench, ibid. 82 (1986) 301.Google Scholar
  4. 4.
    G. Orcel and L. L. Hench, in “Science of Ceramic Chemical Processing”, edited by L. L. Hench and D. R. Ulrich (Wiley, New York, 1986) p. 224.Google Scholar
  5. 5.
    J. Covino, F. G. A. De Laat and R. A. Welsbie, J. Non-Cryst. Solids 82 (1986) 329.Google Scholar
  6. 6.
    H. De Lambilly and L. C. Klein, ibid. 102 (1988) 269.Google Scholar
  7. 7.
    J. S. Yang, S. Sakka, T. Yoko and H. Kozuka, J. Mater. Sci. 25 (1990) 1773.Google Scholar
  8. 8.
    T. Adachi and S. Sakka, ibid. 99 (1988) 118.Google Scholar
  9. 9.
    C. E. Brackbill, H. A. McKinstry and F. A. Hummel, J. Amer. Ceram. Soc. 34 (1951) 107.Google Scholar
  10. 10.
    P. F. James, “Nucleation and Crystallization in Glasses”, “Advances in Ceramics”, Vol. 4, edited by J. H. Simmons, D. R. Uhlmann and G. H. Beall (American Ceramic Society, Columbus, Ohio, 1982) p. 1.Google Scholar
  11. 11.
    P. E. Doherty, D. W. Lee and R. S. Davis, J. Amer. Ceram. Soc. 50 (1967) 77.Google Scholar
  12. 12.
    N. Nakagawa and T. Izumitani, J. Non-Cryst. Solids 7 (1972) 168.Google Scholar
  13. 13.
    F. A. Hummel, J. Am. Ceram. Soc. 34 (1951) 236.Google Scholar
  14. 14.
    W. Ostertag, G. R. Fisher and J. P. Williams, ibid. 51 (1968) 651.Google Scholar
  15. 15.
    H. Schulz, ibid. 57 (1972) 313.Google Scholar

Copyright information

© Chapman and Hall Ltd 1991

Authors and Affiliations

  • Joong-Sik Yang
    • 1
  • Sumio Sakka
    • 1
  • Toshinobu Yoko
    • 1
  • Hiromitsu Kozuka
    • 1
  1. 1.Institute for Chemical ResearchKyoto UniversityKyoto-fuJapan

Personalised recommendations