Journal of Materials Science

, Volume 26, Issue 7, pp 1788–1792 | Cite as

Effects of a binder on properties of taeniolite-acriflavine complex films before and after carbonization

  • Asao Ōya
  • Toshihiro Arai
  • Sugio Ōtani
  • Hirokazu Hanaoka


Taeniolite-acriflavine complex films (about 10 Μm in thickness) with less than 2 wt % of aluminium phosphate binder were prepared, followed by heat treatment (carbonization) below 1073 K under nitrogen in order to examine the effects of the binder on properties of the films. The results obtained are as follows.

(1) The binder made the film more dense without structural change on X-ray diffraction analysis. (2) The tensile strength of the film, especially after heating to high temperature, was improved by adding the binder. (3) The modulus of toughness was scarcely influenced by the binder. (4) No change was observed in the electric resistivity by adding the binder.


Nitrogen Polymer Aluminium Phosphate Heat Treatment 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.


Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.


  1. 1.
    D. G. H. Ballard and G. R. Rideal, J. Mater. Sci. 18 (1983) 545–561.CrossRefGoogle Scholar
  2. 2.
    M. Uehara and T. Suzuki, J. Ceram. Soc. Jpn 93 (1985) 491–497.Google Scholar
  3. 3.
    A. Ōya, K. Matsunaga, A. Satou, H. Mita and S. Ōtani, J. Mater. Sci. Lett. 7 (1988) 985–986.CrossRefGoogle Scholar
  4. 4.
    A. Ōya, A. Sato, H. Hanaoka and S. Ōtani, J. Amer. Ceram. Soc. 73 (1990) 689–693.CrossRefGoogle Scholar
  5. 5.
    K. Sugimori and N. Kagaku J. Clay Sci. Soc. Jpn 26 (1986) 127–137.Google Scholar
  6. 6.
    Taki Chemical Co. Ltd. (Japan), Catalogue of aluminum phosphate binder.Google Scholar

Copyright information

© Chapman and Hall Ltd 1991

Authors and Affiliations

  • Asao Ōya
    • 1
  • Toshihiro Arai
    • 1
  • Sugio Ōtani
    • 1
  • Hirokazu Hanaoka
    • 2
  1. 1.Faculty of TechnologyGunma UniversityGunmaJapan
  2. 2.Gunmaken Industrial Research InstituteGunmaJapan

Personalised recommendations