Direct observation of compressive deformation of PBO fibre in the SEM

  • C. C. Chau
  • M. H. Thomsen
  • V. L. St Jeor
Papers

Abstract

Polybenzobisoxazole fibres were compressed uniaxially in a tension-compression stage for direct observation of deformation in a scanning electron microscope. Kink bands were observed to develop on the fibre surface at early stages of deformation. They seemed to initiate heterogeneously and propagate across a large part of the fibre. Both the length and thickness of the band increased dramatically with slight compression. Upon continued deformation, cracks or openings were seen to develop from surface irregularities near the kink bands. The cracks or openings extended along the fibre length while new bands continued to develop adjacent to them. Cracks and kink bands seemed to be mutually inducible to result in a localized bulge at later stages of deformation. In Kevlar 49 fibres, cracks or openings seemed to develop at higher compressive strains notably at intersections of kink bands.

Keywords

Polymer Electron Microscope Scanning Electron Microscope Direct Observation Fibre Length 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    S. Kumar, SAMPE Q. 3 (January) (1989).Google Scholar
  2. 2.
    S. J. DeTeresa, Air Force Report, AFWAL-TR-85-4013, March (1985) Ch. III, p. 34.Google Scholar
  3. 3.
    B. W. Rosen, “Mechanics of Composite Strengthening” (ASM Seminar, Philadelphia, 1964).Google Scholar
  4. 4.
    W. W. Adams and R. K. Eby, MRS Bull. 16 November/31 December (1987) p. 22.Google Scholar
  5. 5.
    S. J. DeTeresa, S. R. Allen, R. J. Farris and R. S. Porter, J. Mater. Sci. 19 (1984) 57.Google Scholar
  6. 6.
    M. G. Dobb, D. J. Johnson and B. P. Saville, Polymer 22 (1981) 960.Google Scholar
  7. 7.
    J. M. Greenwood and P. G. Rose, J. Mater. Sci. 9 (1974) 1809.Google Scholar
  8. 8.
    S. R. Allen, A. G. Filippov, R. J. Farris, E. L. Thomas, C. P. Wong, G. C. Berry and E. C. Chenevey, Macromolecules 14 (1981) 1135.Google Scholar
  9. 9.
    M. G. Dobb, D. J. Johnson and B. P. Saville, Polymer 22 (1981) 960.Google Scholar
  10. 10.
    V. L. St Jeor, C. C. Chau and M. H. Thomsen, in “Proceedings of the 12th International Congress for Electron Microscopy”, Vol. 4 (San Francisco Press, San Francisco, CA, 1990) p. 544.Google Scholar
  11. 11.
    S. J. DeTeresa, R. S. Porter and R. J. Farris, J. Mater. Sci. 23 (1988) 1886.Google Scholar
  12. 12.
    R. E. Robertson, J. Polym. Sci. A-2 7 (1969) 1315.Google Scholar
  13. 13.
    C. C. Chau and J. C. M. Li, J. Mater. Sci. 17 (1982) 652.Google Scholar
  14. 14.
    R. B. Pond, in “Proceedings of the ASM Seminar on the Inhomogeneity of Plastic Deformation”, 1971 (American Society for Metals, Metals Park, OH, 1973) pp. 1–16.Google Scholar
  15. 15.
    S. Kumar, Int. Fibre J. (February) (1989) 4.Google Scholar
  16. 16.
    J. B. C. Wu and J. C. M. Li, J. Mater. Sci. 11 (1976) 434.Google Scholar
  17. 17.
    J. C. M. Li and J. B. C. Wu, ibid. 11 (1976) 445.Google Scholar

Copyright information

© Chapman & Hall 1992

Authors and Affiliations

  • C. C. Chau
    • 1
  • M. H. Thomsen
    • 1
  • V. L. St Jeor
    • 1
  1. 1.Central ResearchThe Dow Chemical CompanyMidlandUSA

Personalised recommendations