Journal of Wood Science

, Volume 45, Issue 6, pp 502–514 | Cite as

Weathering durability of CCB-impregnated wood for clear varnish coatings

  • Mustafa Kemal Yalinkiliç
  • Rifat Ilhan
  • Yuji Imamura
  • Munezoh Takahashi
  • Zafer Demirci
  • Ahmet Cihangir Yalmkiliç
  • Huseyin Peker


Outdoor performances of a polyurethane varnish and an alkyd-based synthetic varnish coated over chromium-copper-boron (CCB)-impregnated Scots pine (Pinus sylvestris L.) and chestnut (Castanea sativa Mill.) [10 (R) × 100 (T) × 150 (L) mm] were investigated. These varnishes were also applied to the wood surface as sole coatings or impregnated into wood as water-repellent (WR) solutions. Outdoor exposure was performed in the Black Sea region of northern Turkey (41°N, 39.43°E) where humid weather predominates throughout the year and accelerates decomposition of coated wood surfaces. The wood panels were exposed at 45° south on their tangential surfaces. After 9 months of exposure to summer, autumn, and the following winter season, the color and glossiness changes of the exposed surface, adhesion of the coating layer to the wood surface, water absorption through the coating layers, mass loss, and the hardness of the board surface were studied. CCB impregnation greatly stabilized the surface color of varnish-coated panels of both wood species. Gradual decreases of adhesion between varnished layers and preimpregnated surfaces were attributed to probable weakening of interactions at the interface of the treated wood and the film layer. A superficial cleaning process of treated wood is suggested to improve glossiness and adhesion. The coated wood surface became harder with time on outdoor exposure until a maximum hardness occurred followed by softening, whereas the uncoated surface softened steadily. Polyurethane varnish yielded a harder surface than synthetic varnish. Mass losses of wood panels after 9 months of exposure were negligible for all treatments compared with the untreated controls, which were totally discolored and eroded on the surface. It is concluded that long-term exterior wood protection has been achieved by a successful combination of an appropriate preservative treatment followed by a compatible surface-coating process.

Key words

Weathering CCB Varnish coating Exterior wood Chromium Boron 


Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.


  1. 1.
    NZFRI Research Directions (1996) New Zealand Forest Research Institute, No. 13, p 11Google Scholar
  2. 2.
    Evans PD, Michell AJ, Schmalzl KJ (1992) Studies of the degradation and protection of wood surfaces. Wood Sci Technol 26:151–163CrossRefGoogle Scholar
  3. 3.
    Williams RS, Knaebe MT, Feist WC (1996) Finishes for exterior wood: selection, application, and maintenance. Forest Products Society, USDA Forest Service, p 127Google Scholar
  4. 4.
    Maclead IT, Scully AD, Ghiggino KP, Ritchie PJA, Paravagna OM, Leary B (1995) Photodegradation at the wood-clearcoat interface. Wood Sci Technol 29:183–189Google Scholar
  5. 5.
    Hicks HR, Householder DF (1968) Trade sales paints. In: Martens CR (ed) Technology of paints, varnishes and laquers. Reinhold, New York, pp 531–553Google Scholar
  6. 6.
    Wilkinson JG (1979) Industrial timber preservation. The Rentokil Library, Associated Business Press, London, p 532Google Scholar
  7. 7.
    Williams RS, Feist WC (1988) Performance of finishes on wood modified with chromium nitrate versus chromic acid. For Prod J 38 (11/12):32–35Google Scholar
  8. 8.
    Feist WC, Williams RS (1991) Weathering durability of chromiumtreated southern pine. For Prod J 41(1):8–14Google Scholar
  9. 9.
    Pizzi A (1980) Wood waterproofing and lignin cross-linking by means of chromium trioxide/guaiacol units complexes. J Appl Polym Sci 25:2547–2553CrossRefGoogle Scholar
  10. 10.
    Ostemeyer JG, Elder TJ, Winandy JE (1989) Spectroscopic analysis of southern pine treated chromated copper arsenate. II. Diffuse reflectance Fourier transform infrared spectroscopy (DRIFT). Wood Chem Technol 9:105–122CrossRefGoogle Scholar
  11. 11.
    Pandey KK, Chauhan SS, Aggarwal PK (1998) Reaction of wood with inorganic salts. Holz Roh Werkstoff 56:412–415CrossRefGoogle Scholar
  12. 12.
    Schmalzl KJ, Forsyth CM, Evans PD (1995) The reaction of guaiacol with iron III and chromium VI compounds as a model for wood surface modification. Wood Sci Technol 29:307–319CrossRefGoogle Scholar
  13. 13.
    Sell J, Muster WJ, Wälchli O (1974) Investigations on weathered wood surfaces. Part V. The efficiency of Cr-Cu-B-salt-solutions for surface treatment. Holz Roh Werkstoff 32:45–51CrossRefGoogle Scholar
  14. 14.
    Sell J, Feist WC (1985) Weathering behavior of chromium-copperboron-treated wood. Holz Roh Werkstoff 43:518CrossRefGoogle Scholar
  15. 15.
    Harrow KM (1951) Leachability of some water-soluble wood preservatives. NZ J Sci Technol B 32(6):33–40Google Scholar
  16. 16.
    Peylo A, Willeitner H (1995) The problem of reducing the leachability of boron by water repellents. Holzforschung 49:211–216CrossRefGoogle Scholar
  17. 17.
    Yalinkilic MK, Ilhan R, Imamura Y, Takahashi M, Demirci Z, Yalinkilic AC (1998) FT-IR studies of the effects of outdoor exposure on varnish-coated wood pretreated with CCB. In: Proceedings of the fourth Pacific Rim bio-based composites symposium, Nov 2–5, Bogor, Indonesia, pp 345–357Google Scholar
  18. 18.
    ASTM D 358-55 (1970) Standard specifications for wood to be used panels in weathering tests of paints and varnishes (reproved 1968). American Society for Testing and Materials, PhiladelphiaGoogle Scholar
  19. 19.
    Feist WC, Hon DS-S (1984) Chemistry of weathering and protection. In: Rowell RM (ed) The chemistry of solid wood: advances in chemistry series No. 207. American Chemical Society, pp 401–451Google Scholar
  20. 20.
    ASTM D 1536-58 T (1964) Tentative method of test for color difference using the colormaster differential colorimeter. American Society for Testing and Materials, PhiladelphiaGoogle Scholar
  21. 21.
    Park BS, Fruno T, Uehara T (1996) Histochemical changes of wood surfaces irradiated with ultraviolet light. Mokuzai Gakkaishi 42:1–9Google Scholar
  22. 22.
    ASTM D 523-67 (1970) Standard method of test for specular gloss. American Society for Testing and Materials, PhiladelphiaGoogle Scholar
  23. 23.
    ASTM D 3359-95 (1995) Standard test methods for measuring adhesion by tape test. American Society for Testing and Materials, PhiladelphiaGoogle Scholar
  24. 24.
    ASTM D 4366-95 (1995) Standard test methods for hardness of organic coatings by pendulum test. American Society for Testing and Materials, PhiladelphiaGoogle Scholar
  25. 25.
    Scheffer TC (1973) Microbial degradation and the casual organisms. In: Nicholas DD (ed) Wood deterioration and its prevention by preservative treatments, Vol 1: Degradation and protection of wood. Syracuse University Press, Syracuse, NY, pp 31–106Google Scholar
  26. 26.
    Bobalek EG (1967) Methods of wood finishing. In: Marchessault RH, Skaar C (eds) Surfaces and coating related to paper and wood. Syracuse University Press, Syracuse, NY, pp 415–462Google Scholar
  27. 27.
    Damusis A, Frisch KC (1967) Urethane coatings. In: Myers RR, Long JS (eds) Film-forming compositions. Part 1. Marcel Dekker, New York, pp 435–516Google Scholar
  28. 28.
    Cassens DL, Feist WC, Johnson BR, DeGroot RC (1995) Selection and use of preservative-treated wood. Forest Products Society Publication No. 7299, p 104Google Scholar
  29. 29.
    Kraft WM, Janusz EG, Sughrue DJ (1967) Alkyd resins. In: Myers RR, Long JS (eds) Film-forming compositions. Part 1. Marcel Dekker, New York, pp 71–98Google Scholar
  30. 30.
    Feist WC (1987) Weathering performance of finished yellowpoplar siding. For Prod J 37(3):15–22Google Scholar
  31. 31.
    Dahlgren S-E, Hartford WH (1972) Kinetics and mechanism of fixation of Cu-Cr-As wood preservatives. Holzforschung26:62–69, 105–113, 142–149CrossRefGoogle Scholar
  32. 32.
    Dahlgren S-E (1973) Variability in colour intensity of C.C.A. treated wood. J Inst Wood Sci 6(4):28–30Google Scholar
  33. 33.
    Pizzi A, Kubel H (1982) The chemistry and kinetic behavior of Cu-Cr-As/B wood preservatives. Part 6. Fixation of CCB in wood and physical and chemical comparison of CCB and CCA. Holzforsch Holzverwert 34(5):80–86Google Scholar
  34. 34.
    Majumdar S, Kumar D, Nirvan YPS (1998) Acrylate grafted dehydrated castor oil alkyd: a binder for exterior paints. J Coatings Technol 70(879):27–33CrossRefGoogle Scholar
  35. 35.
    Bardage SL, Bjurman J (1998) Adhesion of waterborne paints to wood. J Coatings Technol 70(878):39–47CrossRefGoogle Scholar
  36. 36.
    Lewis AF, Forrestal LJ (1969) Adhesion of coatings. In: Myers RR, Long JS (eds) Characterization of coatings; physical techniques, part 1, vol 2. Marcel Dekker, New York, pp 57–98Google Scholar
  37. 37.
    Yalinkilic MK, Baysal E, Demirci Z (1995) Effect of boron preservatives on hygroscopicity of Brutia pine wood. Eng Sci J Pamukkale Univ Turkey 1(2–3):161–168Google Scholar
  38. 38.
    Blumstein A (1969) Photoelastic coatings. In: Myers RR, Long JS (eds) Treatise on coatings, vol 2: Characterization of coatings: physical techniques, part 1. Marcel Dekker, New York, pp 597–637Google Scholar
  39. 39.
    Skaar C (1984) Wood-water relationships. In: Rowell RM (ed) The chemistry of solid wood: advances in chemistry series 207. American Chemical Society, pp 127–172Google Scholar
  40. 40.
    Athawale VD, Bhabhe MD (1998) Chemoenzymatic synthesis and characterization of urethane oils for surface coatings. J Coatings Technol 70(879):43–48CrossRefGoogle Scholar
  41. 41.
    Haseebuddin S, Raju KVSN, Yaseen M (1998) Crosslink density and cure window of oligourethane diol/melamine high-solids coatings. J Coatings Technol 70(879):35–42CrossRefGoogle Scholar
  42. 42.
    Seymour RB, Mark HF (1990) Handbook of organic coatings: a comprehensive guide for the coatings industry. Elsevier Science Publishing, New York, p 350Google Scholar
  43. 43.
    Filson AC (1967) Polyethers and polyesters. In: Raymond RM, Long JS (eds) Treatise on coatings, vol I: Film-forming compositions, part 1. Marcel Dekker, New York, pp 391–434Google Scholar
  44. 44.
    Kraft WM, Janusz EG, Sughrue DJ (1967) Alkyd resins. In: Raymond RM, Long JS (eds) Treatise on coatings, vol I: Filmforming compositions, part 1. Marcel Dekker, New York, pp 71–98Google Scholar

Copyright information

© The Japan Wood Research Society 1999

Authors and Affiliations

  • Mustafa Kemal Yalinkiliç
    • 1
  • Rifat Ilhan
    • 2
  • Yuji Imamura
    • 1
  • Munezoh Takahashi
    • 1
  • Zafer Demirci
    • 2
  • Ahmet Cihangir Yalmkiliç
    • 2
  • Huseyin Peker
    • 2
  1. 1.Wood Research InstituteKyoto UniversityUji, Kyoto 611Japan
  2. 2.Technical Education FacultyMugla UniversityMuğlaTurkey

Personalised recommendations