Trace analysis of zinc and bismuth in high purity tin by polarized zeeman atomic absorption spectrometry with direct atomization of solid samples

  • K. Takada
  • T. Shoji
Original Papers Trace Element Analysis

Summary

Traces of zinc and bismuth in small amounts of high purity tin (0.5 ∼ 25 mg) were determined by polarized Zeeman AAS with direct atomization of a solid sample in a electrothermal graphite-cup cuvette. Standard solutions of zinc and bismuth were employed for the calibration curve. Absorption intensities (peak areas of the absorption signals) for zinc and bismuth were not influenced by the residual tin in a graphite-cup cuvette, up to 25 mg for zinc and up to 10 mg for bismuth. The relative standard deviations of analytical results were 9 ∼ 43% for 0.002 ∼ 0.05 ppm of zinc and 5 ∼ 10 % for 0.06 ∼ 1.3 ppm of bismuth. Detection limits were 0.012 ng for zinc and 0.03ng for bismuth. These values correspond to 0.0005 ppm of zinc in 25 mg of tin and 0.03 ppm of bismuth in 10 mg of tin. Time (incl. weighing the sample) required for analyzing one sample was about 5 min.

Keywords

Zinc Bismuth Atomic Absorption Spectrometry Absorption Intensity Solid Sample 

Spurenanalyse von Zink und Bismut in hochreinem Zinn durch polarisierte Zeeman-Atomabsorptionsspektrometrie mit direkter Atomisierung fester Proben

Zusammenfassung

Spuren Zink (0,002 ∼ 0,05 ppm) und Bismut (0,06 ∼ 1,3 ppm) wurden in reinem Zinn mit polarisierter Zeeman-AAS bestimmt. Eine kleine Menge der Probe (0,5 ∼ 25 mg) in fester Form wurde direkt mit Hilfe einer elektrothermischen Graphit-Becherküvette atomisiert. Eichkurven von Zn und Bi wurden mit Standardlösungen aufgestellt. Sn in der Graphit-Becherküvette beeinflusst die Absorptionsintensität von Zn bis zu 25 mg und von Bi bis zu 10mg nicht. Die relative Standardabweichung betrug 9 ∼ 43% für 0,002 ∼ 0,05 ppm Zn und 5 ∼ 10% für 0,06 ∼ 1,3 ppm Bi, die Nachweisgrenzen 0,012 ng für Zn und 0,03ng für Bi. Diese Werte entsprechen 0,005 ppm Zn in 25 mg Sn und 0,03 ppm Bi in 10 mg Sn. Die Durchführung einer Analyse benötigt etwa 5 min.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    Arpadian S, Alexandrowa I (1979) Fresenius Z Anal Chem 298:159Google Scholar
  2. 2.
    Bäckman S, Karlsson RW (1979) Analyst 104:1017Google Scholar
  3. 3.
    Busheina IS, Headridge JB (1982) Anal Chim Acta 142:197Google Scholar
  4. 4.
    Frech W, Lundberg E, Barbooti MM (1981) Anal Chim Acta 131:45Google Scholar
  5. 5.
    Hirokawa K, Takada K (1980) Bunseki Kagaku 29:675Google Scholar
  6. 6.
    Kobayashi T, Ido K, Sudo E (1982) J Jap Inst Metals 46:603Google Scholar
  7. 7.
    Koizumi H, Yasuda K (1976) Spectrochim Acta 31B:523Google Scholar
  8. 8.
    Koizumi H, Yasuda K, Katayama M (1977) Anal Chem 49:1106Google Scholar
  9. 9.
    Koizumi H (1982) Hitachi S I News 25:25Google Scholar
  10. 10.
    Langmyhr FJ (1979) Analyst 104:993Google Scholar
  11. 11.
    Takada K, Hirokawa K (1982) Fresenius Z Anal Chem 312:109Google Scholar
  12. 12.
    Takada K, Hirokawa K (1982) Talanta 29:849Google Scholar
  13. 13.
    Takada K, Hirokawa K (submitted)Google Scholar
  14. 14.
    Takada K, submitted to Bunseki KagakuGoogle Scholar

Copyright information

© Springer-Verlag 1983

Authors and Affiliations

  • K. Takada
    • 1
  • T. Shoji
    • 1
  1. 1.The Research Institute for Iron, Steel and Other MetalsTohoku UniversitySendaiJapan

Personalised recommendations