Abstract
A silicon nitride fibre-reinforced cordierite glass ceramic matrix composite has been brazed to titanium and stainless steel in argon with four different interlayer materials, copper, nickel, tungsten and a metal matrix composite (mmc). Joints were tested in shear and all but one failed in the ceramic composite. The highest strength joint, using a metal matrix interlayer to join cmc to stainless steel failed in the mmc at 106 MPa. Silver-copper eutectic braze and aluminium braze can be used to join metals to titanium-coated cmc, producing joints with low levels of interfacial defects. Some joints, however, show debonding at the edges where residual shear stresses are highest.
Similar content being viewed by others
References
M. Doyama, S. Somiya and R. P. Chang (eds), “Metal Ceramic Joints” (MRS Pittsburg, PA, 1979).
R. E. Loehman and A. P. Tomsia, Ceram. Bull. 67 (1988) 375.
M. G. Nicholas, Br. Ceram. Trans. J. 85 (1986) 144.
M. L. Santella, Adv. Ceram. Mater. 3 (1988) 457.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Dixon, D.G. Ceramic matrix composite-metal brazed joints. Journal of Materials Science 30, 1539–1544 (1995). https://doi.org/10.1007/BF00375261
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00375261