Abstract
The effect of oxide dopant on the structure of 62ZrF4-30BaF2-8LaF3 (mol%) glass by equimolar substitution of BaO for BaF2 was studied by X-ray photoelectron spectroscopy (XPS). The XPS spectra of La 3d, Ba 3d, F 1s, O 1s and Zr 3d were measured. From the deconvoluted results for the XPS spectra of elements in the glass, it was proposed that the oxide ions added to the glass mainly bond to Zr4+ and replace the bridging fluoride ions resulting in the formation of the F-Zr-O bond. Further analyses indicated that the oxide ions mainly play a non-bridging role instead of a bridging role in the glass structure.
Similar content being viewed by others
References
M. G. Drexhage, C. T. Monihan, B. Bendow, E. Gboji, K. H. Chung and M. Saleh-Boulos, Mater. Res. Bull. 16 (1981) 943.
Hu Hefang and J. D. Mackenzie, J. Non-Cryst. Solids 80 (1986) 495.
G. W. Tasker, D. R. Uhlmann, P. I. K. Onorato, M. N. Alexander and C. W. Struck, J. Phys. C8 (1985) 273.
P. I. K. Onorato, M. N. Alexander, C. W. Struck, G. W. Tasker and D. R. Uhlmann, J. Am. Ceram. SoC. 68 (1985) C148.
A. Osaka, Y. H. Wang, Y. Miura and T. Tsugaru, J. Mater. Sci. 26 (1991) 87.
Y. H. Wang, A. Osaka, Y. Miura and T. Tsugaru, J. Mater. Sci. Lett. 8 (1988) 421.
J. Fu, A. Osaka, T. Nanba, Y. Miura and H. Yamanaka, Mater. Lett. 15 (1992) 264.
R. M. Almeida, J. Lau and J. D. Mackenzie, ibid. 69 (1984) 161.
T. Buyuklimanli and J. H. Simmons, J. Non-Cryst. Solids 120 (1989) 262.
G. M. Renlund, S. Prochazka and R. H. Doremus, J. Mater. Res. 6 (1991) 2723.
G. C. Nelson, J. Vac. Sci. Technol. A2 (1984) 1141.
C. M. Baldwin, R. M. Almeida and J. D. Mackenzie, J. Non-Cryst. Solids 43 (1981) 309.
C. A. Angell and C. C. Phifer, in “Proceedings of the 5th International Symposium on Halide Glasses”, Shizuoka, Japan, 1988, p. 282.
Lipeng Zhang and Fuxi Gan, Glass Technol. 33 (1992) 47.
C. D. Wager, W. M. Riggs, L. E. Davis, J. F. Moulder and G. E. Muilenberg (eds) “Handbook of X-ray photoelectron Spectroscopy” (Perkin-Elmer Corp., Eden Prairie, MN, 1979) pp. 42, 100.
C. G. Pantano and R. K. Brow, J. Am. Ceram. Soc. 71 (1988) 577.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Zhang, L., Fan, T. & Wang, P.W. Effect of oxide dopant on the structure of fluorozirconate glasses studied by X-ray photoelectron spectroscopy. Journal of Materials Science 30, 1445–1448 (1995). https://doi.org/10.1007/BF00375246
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00375246