Abstract
The interface structure in Gr/Al composites fabricated with liquid metal infiltration has been studied using transmission electron microscopy (TEM). Morphologies of interfacial reaction product, aluminium carbide Al4C3, formed at different manufacturing parameters were compared and, the growth mechanism of the carbide was studied by means of high resolution electron microscopy (HREM). It has been shown that the morphology of the carbide is intimately related to the processing parameters with which the composites were produced. There are two kinds of interfaces between the carbide and the aluminium matrix. They have different growth mechanisms and relative growth rates under different growth driving forces. Several crystal orientation relationships between the carbide and the aluminium matrix have been observed.
Similar content being viewed by others
References
H. Nayeb-Hashemi and J. Seyyedi, Metall. Trans. A 20A (1989) 727.
M. F. Amatean, J. Compos. Mater. 10 (1976) 279.
A. P. Diwanji and I. W. Hall, J. Mater. Sci. 27 (1992) 2093.
S. J. Baker and W. Bonfield, ibid.— 13 (1978) 1329.
T. A. Chemyshova and L. I. Kobeleva ibid.— 20 (1985) 3524.
W. C. Jr. Harrigan, Metall. Trans. A 9A (1978) 503.
J. J. Masson, K. Schulte, F. Girot and Y. Le Petitcorps, Mater Sci. Eng. A135 (1991) 59.
V. D. Scott, R. L. Trumper and Ming Yang, Compos. Sci. Tech. 42 (1991) 251.
M. Yang and V. D. Scott, J. Mater. Sci. 26 (1991) 1069.
I. H. Khan, Metall. Trans. 7A (1976) 1281.
A. Okura and H. Asanuma, Compos. Sci. Eng. 24 (1985) 243.
Min Nai-Ben, “Physical Basis of Crystal Growth” (Shanghai Science & Technical Pub., Shanghai, 1983) p. 434 (in Chinese).
G. A. Jeffrey and V. Y. Wu, Acta Crystallogr. 16 (1963) 559.
Chen Rong, Doctoral Dissertation, Shanghai Jiao Tong University (1989) p. 71.
L. F. Mondolfo, “Aluminium Alloys: Structures and Properties” (Butterworth & Co. Ltd., England, 1976) p. 236.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Yang, H., Gu, M., Jiang, W. et al. Interface microstructure and reaction in Gr/Al metal matrix composites. Journal of Materials Science 31, 1903–1907 (1996). https://doi.org/10.1007/BF00372206
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00372206