Abstract
To investigate enhancement of matrix-dominated properties (such as interlaminar fracture toughness) of a composite laminate, two different bead-filled epoxies were used as matrices for the bead-filled epoxy/glass fibre hybrid composites. The plane strain fracture toughness of two different bead-filled epoxies have been measured using compact tension specimens. Significant increases in toughness were observed. Based on these results the interlaminar fracture toughness and fracture behaviour of hybrid composites, fabricated using bead-filled epoxy matrices, have been investigated using double cantilever beam and end notch flexure specimens for Mode I and Mode II tests, respectively. The hybrid composites based on carbon bead-filled matrix shows an increase in both G IC initiation and G IIC values as compared to a glass fibre reinforced plastic laminate with unmodified epoxy matrix. The optimum bead volume fraction for the hybrid composite is between 15% and 20%. However, the unmodified epoxy glass-fibre composite shows a higher G IC propagation value than that of hybrid composites, due to fibre bridging, which is less pronounced in the hybrids as the presence of the beads results in a matrix-rich interply region.
Similar content being viewed by others
References
C. Y. Kam and J. V. Walker, in “Toughened composite”, edited by N. J. Johnston, ASTM STP 937 (American Society for Testing and Material, Philadelphia, PA, 1987) p. 9.
P. K. Mallic and S. Newman, “Composite Materials Technology” (Hanser, Munich,Vienna, New York, 1990) Ch. 1, p. 10.
R. C. Tennyson, in “Proceedings of the International Conference on Composite Engineering (ICCE/I)”, edited by David Hui (ICCE, New Orleans, 1994) p. 11
W. M. Jordan and W. L. Bradley, in “Toughened composite”, edited by N. J. Johnston, ASTM STP 937 (American Society for Testing and Material, Philadelphia, PA, 1987) p. 95
B. Z. Jang, J. Y. Liau, L. R. Hwang and W. K. Shih, J. Reinf. Plast, Compos. 8 (1989) 312.
J. Kim, C. Baillie, J. Poh and Y. W. Mai, Compos. Sci. Technol. 43 (1992) 283.
D. Hull, J. Mater. Sci. Eng. A184 (1994) 173.
F. N. Cogswell and M. Hopper, Composites 3 (1983) 251.
F. N. Cogswell and D. C. Leach, Plast. Rubber Proc. Applic. 4 (1984) 271.
A. C. Garg and Y. W. Mai, Compos. Sci. Technol. 37 (1988) 179.
F. N. Cogswell, “Thermoplastic aromatic polymer composites” (Butterworth-Heinemann, Oxford, 1992) Ch. 3, p. 51.
W. D. Bascom, R. Y. Ting, R. J. Moulton and A. R. Siebert, J. Mater. Sci. 16 (1981) 2657.
W. L. Bradley, Key Eng. Mater. 37 (1989) 101.
R. E. Evans and J. E. Master, in “Toughened composite”, edited by N. J. Johnston, ASTM STP 937 (American Society for Testing and Material, Philadelphia, PA, 1987) p. 413.
F. F. Lange, Philos. Mag. 22 (1970) 983.
J. S. Spanoudakis and R. J. Young, J. Mater. Sci. 19 (1984) 473.
A. C. Moloney, H. H. Kausch and H. R. Stieger, ibid. 18 (1983) 208.
A. C. Moloney, H. H. Karsch, T. Kaiser and H. R. Beer, ibid. 22 (1987) 381.
B. Z. Jang, J. Y. Liau, L. R. Hwang and W. K. Shih, J. Reinf. Plast. Compos. 9 (1990) 314.
J. K. Kim and P. E. Robertson, J. Mater. Sci. 21 (1992) 161.
C. Doran, S. L. Ogin and P. A. Smith, in “Advanced Composites in Emerging Technologies”, edited by S. A. Paipetis and T. P. Philippidis (AMATEC, Patras, Greece, 1991) p. 181.
Manufacturer's technical data, “Spherical carbon powder” (1989).
J. J. Lee, S. L. Ogin and P. A. Smith, “Proceedings of the 5th PRI International Conference on Fibre Reinforced Composites”, FRC '92, University of Newcastle upon Tyne, 24–26 March 1992 p. 22/1.
J. J. Lee, Ph D thesis, University of Surrey (1992).
“Protocols for Interlaminar Fracture Testing of Composites”, edited by P. Davies, European Structural Integrity Society Polymers and Composite Task Group, March (1992 revision).
R. M. L. Foote and V. T. Buchwald, Int. J. Fract. 29 (1985) 125.
J. K. Kim, C. A. Baillie, J. Poh and Y. M. Mai, Compos. Sci. Technol. 43 (1992) 283.
G. M. Newas, Eng. Frac. Mech. 29 (1988) 31.
A. J. Russel and K. N. Street, in “Delamination and debonding of materials”, edited by W. S. Johnston, ASTM STP 876 (American Society for Testing and Material, Philadelphia, PA, 1985) p. 349.
S. Hashemi, A. J. Kinloch and J. G. Williams, Compos. Sci. Technol. 37 (1990) 429.
M. F. Hipps, M. K. Tse and W. L. Bradley, in “Toughened composite”, edited by N. J. Johnston, ASTM STP 937 (American Society for Testing and Materials, Philadelphia, PA, 1989) p. 115.
W. L. Bradley, in “Application of fracture mechanics to composite materials”, Composite material series, edited by K. Friedrich, (Elsevier Science, 1989) p. 159.
A. J. Kinloch, S. J. Shaw and D. A. Tod, Polymer 24 (1983) 1341.
D. L. Hunston and R. Dehl, “The role of polymer toughness in matrix dominated composite fracture”, Paper EM87-355 (Society of Manufacturing Engineers, Dearbon, MI, 1987).
H. J. Sue, R. E. Jones and E. I. Garcia-Meitin, J. Mater. Sci. 28 (1993) 6381.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Lee, J.J., Suh, C.M. Interlaminar fracture toughness and associated fracture behaviour of bead-filled epoxy/glass fibre hybrid composites. Journal of Materials Science 30, 6179–6191 (1995). https://doi.org/10.1007/BF00369665
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00369665