Abstract
An interesting cubic-shaped precipitate was observed in the matrix of a squeeze-cast Al-4.3 wt % Cu-2.0 wt % Mg/SiC composite which was heat-treated to a T7 condition. Although this phase had been observed by a few investigators in the past, it had never been examined in detail until now. This cubic phase generally had an edge length ranging from 30 to 50 nm and existed in volume fractions as high as 3.8%. Theoretical strengthening models predicted this phase to have good potential for precipitate strengthening. In addition, the cubic phase exhibited a low rate of coarsening at temperatures as high as 250 °C; apparently due to its low interfacial energy. Consequently, this cubic precipitate shows potential for increasing the useful temperature range of aluminium alloys and composites and could be of great importance to the aerospace and automotive industries.
Similar content being viewed by others
References
G. C. Weatherly, PhD thesis, University of Cambridge (1966).
R. N. Wilson, D. M. Moore and P. J. E. Forsyth, J. Inst. Met. 95 (1967) 177.
H. Suzuki, M. Kanno and O. Kanoh, J. Jpn. Inst. Light Met. 44 (1980) 1139.
R. D. Schueller, A. K. Sachdev and F. E. Wawner, Scripta Metall. 27 (1992) 617.
S. Samson, Acta Chem. Scand. 3 (1949) 809.
L. F. Mondolfo, “Aluminum Alloys: Structure and Properties” (Butterworth, London-Boston, 1976), p. 502.
R. N. Wilson and P. G. Partridge, Acta Metall. 13 (1965) 1321.
R. M. Akin Jr, Nasa Contract Report 4365 (1991) p. 55.
C. P. Blankenship Jr, PhD dissertation, University of Virginia (1992).
J. A. Nock Jr, in “Aluminum: Properties and Physical Metallurgy”, edited by J. Hatch (ASM, 1984) p. 178.
R. J. Schueller, A. K. Sachdev and F. E. Wawner, J. Mater. Sci. 28 (1993).
A. J. Ardell, Met. Trans. A 16A (1985) 2131.
V. Gerold and H. Haberkorn, Phys. Status Solidi 16 (1966) 675.
E. Hornbogen and K. H. Gahr, Metallography 8 (1975) 181.
Guillet and Leroux, in “Intermetallic Compounds”, edited by J. H. Westbrook and R. E. Krieger (R. E. Krieger Pub. Co., New York, 1977) p. 453.
C. L. Reynolds, P. R. Couchman and F. E. Karasz, Phil. Mag. 34 (1976) 659.
J. W. Martin, “Micromechanisms in Particle-Hardened Alloys” (Cambridge University Press, Cambridge, UK, 1980) p. 62.
K. C. Russell and L. M. Brown, Acta Metall. 20 (1972) 969.
E. Nembach, Phys. Status Solidi (a) 78 (1983) 571.
J. Friedel, “Les Dislocations” (Gauthier-Villars, Paris, 1956) p. 205.
J. W. Martin, “Micromechanisms in Particle-Hardened Alloys” (Cambridge University Press, Cambridge, UK, 1980) p. 53.
M. Witt and V. Gerold, Scripta Metall. 3 (1969) 371.
E. Orowan in Proceedings of Symposium on Internal Stresses (Institute of Metals, London, 1947) p. 451.
D. Gould, PhD thesis, Oxford University (1971).
M. C. Chaturvedi, D. J. Lloyd and D. W. Chung, J. Mater. Sci. 10 (1976) 373.
J. E. Hatch (ed.), “Aluminum: Properties and Physical Metallurgy” (ASM 1984) p. 395.
G. T. Hahn and A. R. Rosenfield, ASTM STP 432 (American Society for Testing and Materials, Philadelphia, 1968) p. 5.
G. Lutjering and S. Weissmann, Acta Metall. 18 (1970) 785.
C. Wagner, Z. Elektrochem. 65 (1961) 581.
I. M. Lifshitz and V. V. Slyozov, I. Phys. Chem. Solids 19 (1961) 35.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Schueller, R.D., Wawner, F.E. & Sachdev, A.K. Strengthening potential of the cubic σ precipitate in Al-Cu-Mg-Si alloys. JOURNAL OF MATERIALS SCIENCE 29, 239–249 (1994). https://doi.org/10.1007/BF00356599
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00356599