Abstract
Cu-44Ni-5Cr alloy has been subjected to thermomechanical treatment which consisted of plastic deformation of as-quenched material by 50, 65 and 80% reduction in thickness followed by ageing in the interval of 500 to 650 °C for various durations of time. Progress in age-hardening was studied by means of hardness measurement and X-ray diffraction studies. The wavelength of composition modulation and strain amplitude were measured. It was found that age-hardening was a result of interaction between spinodal decomposition and recovery processes. Prior deformation was found to enhance the kinetics of both spinodal decomposition and coarsening. It was concluded that this resulted from increased vacancy concentration and increased coherency strain in the cold-worked material.
Similar content being viewed by others
References
L. H. Schwartz, S. Mahajan and J. T. Plewes, Acta Metall. 22 (1974) 601.
L. H. Schwartz and J. T. Plewes, ibid. 22 (1974) 911.
E. P. Butler and G. Thomas; ibid. 18 (1970) 347.
R. J. Livak and G. Thomas, ibid. 19 (1971) 497.
T. Miyazaki, T. Shinozawa, H. Murayama and H. Mori, Trans. JIM 17 (1976) 181.
R. Knight and P. Wilkes, Metall. Trans. 4 (1973) 2389.
C. K. Wu and G. Thomas, ibid. 8A (1977) 1911.
R. I. Saunderson, P. Wilkes and G. W. Lorimer, Acta Metall. 26 (1978) 1357.
A. Chou, A. Datta, G. H. Meier and W. A. Soffa, J. Mater. Sci. 13 (1978) 541.
D. Bower, G. W. Lorimer, I. Saunderson and P. Wilkes, Met. Technol. 7 (1980) 120.
J. T. Plewes, Metall. Trans. 6A (1975) 537.
F. M. Helmi and L. Zsoldon, Scripta Metall. 11 (1977) 899.
S. Chandranarayanan, R. K. Ray and S. Devaraj, Trans. IIM 38 (1985) 81.
S. Spooner and B. G. Lefevre, Metall. Trans. 11A (1980) 1085.
H. Kreye and P. Pech, Z. Metallkunde. 64 (1973) 765.
P. Prasad Rao, B. K. Agarwal and A. M. Rao, Trans. IIM 36 (1983) 264.
Idem, J. Mater. Sci. 21 (1986) 3759.
Idem, Mater. Sci. Engng 92 (1987) 199.
Idem, J. Mater. Sci. 26 (1991) 1485.
V. Daniel and H. Lipson, Proc. Roy. Soc. A181 (1943) 368.
B. Ditchek and L. H. Schwartz, Acta Metall 28 (1980) 807.
J. E. Hilliard, in “Phase Transformations”, edited by H. I. Aaronson (ASM, Metals Park, Ohio, 1970) p. 497.
A. C. Damask, “Point Defects in Metals” (Gordon & Breach, New York, 1971) p. 290.
J. W. Cahn, Trans. Met. Soc. AIME 242 (1968) 166.
D. E. Laughlin and J. W. Cahn, Acta Metall. 23 (1975) 329.
T. Miyazaki, S. Takagishi, H. Mori and T. Kozakori, ibid. 28 (1980) 1143.
B. Golding and S. C. Moss, Acta Metall. 15 (1967) 1239.
J. Dutkiewicz, Metall. Trans. 8A (1977) 751.
G. C. Weatherly and R. B. Nicholson, Phil. Mag. 17 (1968) 801.
J. W. Cahn, Acta Metall. 11 (1963) 1275.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Raghavendra Bhat, R., Prasad Rao, P. Effect of thermomechanical treatment on the phase transformation in Cu-44Ni-5Cr alloy. Journal of Materials Science 29, 4808–4818 (1994). https://doi.org/10.1007/BF00356527
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00356527