We prepared alumina tubes by an anodic oxidation process. The tube obtained was mechanically tough against a pressure of about 1 MPa from the outside of the tube. The tube was characterized by scanning electron microscopy (SEM) and a gas permeability measurement. The SEM observations revealed that this has uniform straight channels penetrating through the tube wall. The channels are vertical to the tube surface and their diameter is about 150 nm. The permeability of gas was measured with H2, He, N2, O2 and CO2 in the range of 0–100 kPa. The gas flow was mainly governed by Knudsen flow. This indicates the absence of big cracks in the tube.
Similar content being viewed by others
References
S.-T. Hwang and K. Kammermeyer “Membrane in Separations” (John Wiley & Sons, 1975).
W. S. W. Ho and K. K. Sirkar (eds) “Membrane Handbook” (Van Nostrand Reinhold, New York, 1992).
O. Shinji, M. Misono and Y. Yoneda, Bull. Chem. Soc. Jpn. 55 (1982) 2760.
N. Ito, Y. Shindo, K. Haraya and T. Hakuta, J. Chem. Eng. Jpn. 21 (1988) 399.
Y.-M. Sun and S.-J. Khang, Ind. Eng. Chem. Res. 27 (1988) 1136.
T. Okubo, K. Haruta, K. Kusakabe, S. Morooka, H. Anzai and S. Akiyama, Ind. Eng. Chem. Res. 30 (1991) 614.
V. T. Zaspalis, W. van Praag, K. Keizer, J. G. van Ommen, J. R. H. Ross and A. J. Burggraaf, J. Appl. Catal. 74 (1991) 205.
A. M. Champagnie, T. T. Tsotsis, R. G. Minet and E. Wagner, J. Catal. 134 (1992) 713.
J. N. Armor, Appl. Catal. 49 (1989) 1
K. Itaya, S. Sugawara, K. Arai and S. Saito, J. Chem. Eng. Jpn. 17 (1984) 514.
K. Wada, S. Ono, K. Wada, T. Yoshino, N. Baba, K. Kuroda, O. Takahashi, Z. Kawahara and S. Yabushita, Hyoumengijutu 40 (1989) 1388.
S.-T. Hwang and K. Kammermeyer, Can. J. Chem. Eng. 44 (1966) 82.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kobayashi, Y., Iwasaki, K., Kyotani, T. et al. Preparation of tubular alumina membrane with uniform straight channels by anodic oxidation process. JOURNAL OF MATERIALS SCIENCE 31, 6185–6187 (1996). https://doi.org/10.1007/BF00354436
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00354436