On the influence of the chromium content on the evolution of rolling textures in ferritic stainless steels

  • Published:
Journal of Materials Science Aims and scope Submit manuscript

Abstract

The crystallographic hot and cold rolling textures of various ferritic stainless steels with 10.5–16.5 wt% Cr content were investigated by use of quantitative texture analysis. The hot-rolled specimens revealed a texture gradient through the sheet thickness. In the centre layers they revealed a cold-rolling type texture (α-fibre) and close to the surface layers a strong Goss orientation. The texture maximum as well as the through-thickness texture gradient of the hot-rolled specimens increased with the Cr content. During cold rolling the textures inherited from the hot rolling process sharpened in the centre layers and decreased in the sub-surface layers. The hot band textures from which this inhomogeneity proceeded were explained in terms of the strong through-thickness profile of the shear strains. The fact that the textures were not randomized by phase transformation during hot rolling was attributed to the elevated Cr content which stabilizes the ferritic regime.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. H. J. BUNGE, Z. Metallkde 56 (1965) 872.

    CAS  Google Scholar 

  2. Idem, “Texture Analysis in Materials Science” (Butterworths, London, 1982).

    Google Scholar 

  3. J. D. DEFILIPPI and H. C. CHAO, Met. Trans. 2 (1971) 3209.

    Article  CAS  Google Scholar 

  4. R. M. DAVISON, Met. Trans. 6A (1975) 2243.

    Article  CAS  Google Scholar 

  5. M. HÖLSCHER, D. RAABE and K. LÜCKE, Steel Res. 62 (1991) 567.

    Article  Google Scholar 

  6. D. RAABE and K. LÜCKE, Scripta Metall. 26 (1992) 1221.

    Article  CAS  Google Scholar 

  7. Idem, in Proceedings of the 10th International Conference on Textures of Materials ICOTOM 10, Clausthal, September 1993, Mater. Sci. Forum 157–162 (1994) 597.

    Article  Google Scholar 

  8. Idem, Mater. Sci. Technol. 91 (1993) 302.

    Article  Google Scholar 

  9. M. HÖLSCHER, D. RAABE and K. LÜCKE, Acta Metall. 42 (1994) 879.

    Article  Google Scholar 

  10. A. FEDOSSEEV and D. RAABE, Scripta Metall. 30 (1992) 1.

    Google Scholar 

  11. D. RAABE and K. LÜCKE, Steel Res. 63 (1992) 457.

    Article  CAS  Google Scholar 

  12. D. RAABE, M. HÖLSCHER, M. DUBKE, H. PFEIFER, H. HANKE and K. LÜCKE, ibid. 64 (1993) 359.

    Article  CAS  Google Scholar 

  13. D. RAABE and K. LÜCKE, in Proceedings of the International Conference on Strip Casting, Hot and Cold Working of Stainless Steels, Quebec, Canada, 1993, edited by N. D. RYAN, A. J. BROWN, H. J. MCQUEEN (The Metallurgical Society of CIM, Quebec, 1993) p. 3 and p. 221.

    Google Scholar 

  14. D. RAABE and K. LÜCKE, in Proceedings of the 10th International Conference on Textures of Materials ICOTOM 10, Clausthal, September 1993, Mater. Sci. Forum 157–162 (1994) 1469.

    Article  Google Scholar 

  15. H. HONNEFF and H. MECKING, in Proceedings of the 6th International Conference on Textures of Materials ICOTOM 6, Japan, September 1981 edited by S. Nagashima (Iron and Steel Institute of Japan, 1981) p. 347.

  16. U. F. KOCKS and H. CHANDRA, Acta Metall. 30 (1982) 695.

    Article  CAS  Google Scholar 

  17. J. L. RAPHANEL and P. V. HOUTTE, ibid. 33 (1985) 1481.

    Article  CAS  Google Scholar 

  18. A. FEDOSSEEV, D. RAABE and G. GOTTSTEIN, in Proceedings of the 10th International Conference on Textures of Materials ICOTOM 10, Clausthal, September 1993, Mater. Sci. Forum 157–162 (1994) 1771.

    Article  Google Scholar 

  19. D. RAABE, Mater. Sci. Technol. in press.

  20. M. HÖLSCHER, PhD thesis, Technical University of Aachen, Germany (1987).

    Google Scholar 

  21. D. RAABE, PhD thesis, Technical University of Aachen, Germany (1992).

    Google Scholar 

  22. L. G. SCHULZ, J. Appl. Phys. 20 (1949) 1030.

    Article  Google Scholar 

  23. C. DÄRMANN, S. MISHRA and K. LÜCKE, Acta Metall. 32 (1984) 2185.

    Article  Google Scholar 

  24. U. V. SCHLIPPENBACH, F. EMREN and K. LÜCKE, ibid. 34 (1986) 1289.

    Article  Google Scholar 

  25. M. MATSUO, ISIJ Int. 29 (1989) 809.

    Article  CAS  Google Scholar 

  26. W. HUTCHINSON, Int. Mater. Rev. 29 (1984) 25.

    CAS  Google Scholar 

  27. D. RAABE, G. SCHLENKERT, H. WEISSHAUPT and K. LÜCKE, Mater. Sci. Technol. 10 (1994) 229.

    Article  Google Scholar 

  28. D. RAABE and K. LÜCKE, Z. Metallkde 85 (1994) 302.

    CAS  Google Scholar 

  29. L. SEIDEL, M. HÖLSCHER and K. LÜCKE, Textures Microstruct. 11 (1989) 171.

    Article  Google Scholar 

  30. A. J. MCLAREN and C. M. SELLARS, in Proceedings of the International Conference on Strip Casting, Hot and Cold Working of Stainless Steels, Quebec, Canada, 1993, edited by N. D. RYAN, A. J. BROWN, H. J. MCQUEEN (The Metallurgical Society of CIM, Quebec, 1993) p. 107.

    Google Scholar 

  31. J. H. BEYNON, A. R. S. PONTER and C. M. SELLARS, in Proceeding of the Modelling of Metal Forming (Kluwer Acad. Publ, 1988) p. 321.

  32. A. J. MCLAREN and C. M. SELLARS, Mater. Sci. Technol. 8 (1992) 1090.

    Article  CAS  Google Scholar 

  33. E. HOUDREMONT, Handb. Sonderstahlkunde, 3. Aufl. (Springer Verlag 1, 1956) p. 623.

  34. K. BUNGARDT, E. KUNZE and E. HORN, Arch. Eisenhüttenw. 29 (1958) 193.

    Article  CAS  Google Scholar 

  35. D. RAABE, Unpublished work.

  36. C. KLINKENBERG, D. RAABE and K. LÜCKE, Steel Res. 63 (1992) 227.

    Article  Google Scholar 

  37. Y.B. PARK, S. K. CHANG, D. RAABE and K. LÜCKE, Mater. Sci. Forum 157–162 (1994) 571.

    Article  Google Scholar 

  38. O. KUBASCHEWSKI, “Binary Phase Diagrams of Iron” (Springer Verlag, Verlag Stahleisen m.b.H., 1982) p. 31.

  39. E. SCHÜRMANN and J. BRAUCKMANN, Arch. Eisenhüttenw. 48 (1977) 3.

    Article  Google Scholar 

  40. E. BAERLECKEN, W. A. FISCHER and K. LORENZ, Stahl Eisen. 81 (1961) 768.

    CAS  Google Scholar 

  41. H. ETTWIG and W. PEPPERHOFF, Arch. Eisenhüttenw. 41 (1970) 471.

    Article  CAS  Google Scholar 

  42. G. KIRCHNER, T. NISHIZAWA and B. UHRENIUS, Met. Trans. 4 (1973) 167.

    Article  CAS  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Institut für Metallkunde und Metallphysik, RWTH Aachen, Kopernikusstr. 14, 52056, Aachen, Germany

    D. Raabe

Authors
  1. D. Raabe
    View author publications

    You can also search for this author in PubMed Google Scholar

Rights and permissions

Reprints and permissions

About this article

Cite this article

Raabe, D. On the influence of the chromium content on the evolution of rolling textures in ferritic stainless steels. JOURNAL OF MATERIALS SCIENCE 31, 3839–3845 (1996). https://doi.org/10.1007/BF00352800

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/BF00352800

Keywords

Search

Navigation