Abstract
The oxidation behaviour of WC-Co sintered carbides with 3–5 μm grain size of WC and 6–15 vol.% of cobalt have been studied in air in the temperature range 650–800 °C. The intensive swelling of up to 350% of initial specimen size and linear kinetics of the growth of the porous WO3 layer were observed during the oxidation. The final shape of the specimen after oxidation was dependent on its initial shape. The apparent activation energy of the dimension and weight gain kinetics were within the range 32–67 kJ mol−1 and the process was proposed to be controlled by the reaction at the interface. The oxidation rates and swelling coefficients increased when the mean size of WC grains was decreased and cobalt content increased. The possible model of WC-Co alloys' oxidation and swelling was proposed for the observed shape development and kinetics of oxidation.
Similar content being viewed by others
References
K. J. A. Brookes, “World Directory and Handbook of Hardmetals” (Int. Carbide Data, 4th edition, 1987).
J. Dusza, L'. Parilak, M. Šlesar and J. Diblifk, Ceram. Int. 9 (1983) 2.
J. Dusza, L' Parilak and M. Šlesar, Ceram. Int. 13 (1987) 133.
N. Tsuchiya, M. Fukuda, T. Nakai and H. Suzuki, J. Jap. Soc. Powder met. 6 (1991) 505.
R. Kieffer, and F. Kolbl, Z. Anorg. Chem. 262 (1950) 97.
G. V. Samsonov, “Tugoplavkije sojedinenija” (Metallurgizdat, Moskva, 1963).
R. F. Vojtovich and E. A. Pugach, Poroshkovaya Metallurgija (1973) 59.
R. F. Vojtovich and E. A. Pugach, “Okislenije tugoplavkich soedinenij” (Metallurgizdat, Moskva, 1978).
Yu. F. Kots, V. S. Panov, N. V. Shipkov and A. A. Filimonova, Poroshkovaya Metallurgija (1990) 62.
B. O. Haglund and B. Lehtinen, in “Proceedings of 3rd International Conference on Thermal Analysis” ICTA, Davos, Vol. 3 (1971) p. 545.
S. Shimada and M. Kozeki, J. Mat. Sci. 27 (1992) 1869.
R. F. Vojtovich “Okislenie karbidov i nitridov” (Naukova dumka, Kiev, 1981).
G. S. Kreimer, in “Strength of Hard Alloys” (Consultant Bureau, Plenum Press, New York, 1968) in B. Johannesson, “The Fracture Behavior of Hardmetals”, PhD. Thesis (Chalmers University of Technology, Göteborg, 1987) p.7.
N. Bouaoaudja, G. Orange, G. Fantozzi, F. Thevenot and P. Goeuriot, J. de Physique 47 (1986) C1–739.
E. A. Almond, in “Science of Hard Materials” edited by R. K. Wisandham, P. J. Rowcliffe and J. Gurland (Plenum Press, New York, 1983) p. 517.
S. Lay, F. Osterstock, “Deformation of Ceramic Materials II.”, Mat. Sci. Res. 18 (Plenum Press, New York, 1984) p. 463.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Lofaj, F., Kaganovskii, Y.S. Kinetics of WC-Co oxidation accompanied by swelling. JOURNAL OF MATERIALS SCIENCE 30, 1811–1817 (1995). https://doi.org/10.1007/BF00351615
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00351615