Abstract
The effect of cathodic charging on the mechanical behaviour of Al-4Zn-1Mg alloy was studied. Hardening of the Al-4Zn-1Mg alloy surface, due to the hydrogen absorption, was observed. The ultimate tensile stress of the charged aluminium alloy was noted to be a non-linear function of the charging current density. The cathodically charged aluminium alloy exhibited brittle transgranular fracture at the surface layer, whereas ductile intergranular fracture was observed at the deeper layers of the same alloy.
Similar content being viewed by others
References
I. O. SHIM and J. G. BYRNE, Mater. Sci. Eng. 74 (1985) 174.
V. KERLINS, “Metals Handbook, Vol. 12, Fractography”, 9th edition (ASM, Metals Park, OH, 1987) p. 13.
G. M. BOND, I. M. ROBERTSON and H. K. BIRNBAUM, Acta Metall. 36 (1988) 2193.
J. W. WATSON, Y. Z. SHEN and M. MESHII, Met. Trans. 19A (1988) 2299.
L. CHRISTODOULOU and H. M. FLOWER, Acta. Metall. 28 (1980) 481.
S. P. LYNCH, Corrosion Sci. 22 (1982) 925.
S. NAKAHARA and Y. OKINAKA, J. Electrochem. Soc. 136 (1989) 1892.
A. KIMURA and H. K. BIRNBAUM, Acta Metall. 35 (1987) 1077.
L. CHEN, W. CHEN, Z. LIU, Y. SHAO and Z. HU, Met. Trans. 24A (1993) 1355.
R. M. LATANISION and M. KURKELA, Corrosion 39 (1983) 174.
J. ALBRECHT, A. W. THOMPSON and I. M. BERNSTEIN, Met. Trans. 10A (1979) 1759.
Y. IIJIMA, S. I. YOSHIDA, H. SAITOH, H. TANAKA and K. I. HIRANO, J. Mater. Sci. 27 (1992) 5735.
R. K. VISWANADHAM, T. S. SUN and J. A. S. GREEN, Met. Trans. 11A (1980) 85.
J. YAO, S. A. MEGUID and J. R. CAHOON, ibid. 24 A (1993) 105.
F. ZEIDES and I. ROMAN, Mater. Sci. Eng. A125 (1990) 21.
D. KWON, S. LEE and R. J. ASARO, Met. Trans. 23A (1991) 1375.
H. P. van LEEUWEN, Corrosion 29 (1973) 197.
S. P. LYNCH, Acta Metall. 29 (1981) 325.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Panagopoulos, C., Papapanayiotou, P. The influence of cathodic hydrogen charging on the mechanical behaviour of Al-4Zn-1Mg alloy. Journal of Materials Science 30, 3449–3456 (1995). https://doi.org/10.1007/BF00349893
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00349893