Synthesis and electrical properties of poly[2-(2-(4-trifluoromethyl)phenyl)ethenyl-1,4-phenylenevinylene] and PPV copolymers

Summary

Poly[2-(2-(4-(trifluoromethyl)phenyl)ethenyl)-5-methoxy-1,4-phenylenevinylene] (PFEMPV) and a series of PPV copolymers containing 1,4-phenylenevinylene (PV) units were synthesized through a water-soluble precursor route, and their electrical and third-order nonlinear optical properties were studied. The PFEMPV films could not be doped with I₂, but FeCl₃-doped films showed an electrical conductivity of 5.0x10^-4 S/cm. The conductivities of FeCl₃-doped copolymer films ranged from 2.0x10^-3 to 2.0 S/cm depending on their copolymer compositions. The third-order nonlinear optical susceptibility, χ⁽³⁾(−ω;ω,ω,−ω), was also investigated by the degenerate four wave mixing technique at 602 nm. The χ⁽³⁾ value of PFEMPV was 6.9x10^-11 esu. The photoluminescence spectrum of PFEMPV shows its emission maximum at 550 nm.