Abstract
The effects of NaF additive upon the sintering temperature of Ba(Mg1/3Ta2/3)O3 dielectric ceramics were investigated, and the densification of the present ceramics could be performed well at lower temperatures, even around 1200 ‡C, when the concentration of NaF additive was equal or greater than 2 wt %. Moreover, no secondary phase was observed in such ceramics, except the limited surface layers.
Similar content being viewed by others
References
s.nomura, k.toyama and k.kaneta, Jpn J. Appl. Phys. 21 (1982) L624.
k.matsumoto, t.hiuga, k.takada and h.ichimura, in Proceedings of the 6th IEEE International Symposium on Applied Ferroelectrics, Bethlehem, June 1986 (Westerville. The American Ceramic Society, 1986) p. 118.
x. m.chen, y.suzuki and n.sato, J. Mater. Sci. Mater. Elec. 6 (1994) 244.
x. m. chen, J. Mater. Sci. (in press).
e. s.kim and k. h.yoon, Ferroelectrics 133 (1992) 187.
e.smethurst and d. w.budworth, Trans. Br. Ceram. Soc. 71 (1972) 51.
j. m.haussonne, g.desgardin, p. h.bajolet and b.raveau, J. Amer. Ceram. Soc. 66 (1983) 801.
o.renoult, j.-p.boilot, f.chaput, r.papiernik, l. g.hubert-Pfalzgraf and m.lejeune, J. Amer. Ceram. Soc. 75 (1992) 3337.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Chen, X.M., Wu, Y.J. Effects of NaF upon sintering temperature of Ba(Mg1/3Ta2/3)O3 dielectric ceramics. J Mater Sci: Mater Electron 7, 427–431 (1996). https://doi.org/10.1007/BF00180781
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00180781