Abstract
A series of glass samples were prepared from a mixtures of B2O3, Na2O and NiO. The role of nickel oxide in a glass matrix was studied by using infrared spectra, optical absorption, magnetic susceptibility, density, and differential thermal analysis (DTA). It was shown that the addition of nickel oxide at different concentrations to the glass batches causes some deformation in the glass structure. The values of ligand field strength and Racah parameter indicated an increasing degree of covalency. The glass samples exhibited diamagnetic behaviour with NiO content up to 1 g, then paramagnetic behaviour. The densities and glass transition temperatures decreased with increase in the NiO content up to 0.2 g and then increased again. This tendency may be related to changes in the glass structure.
Similar content being viewed by others
References
S. ANDERSON, R. L. BOHON and D. D. KIMPTON, J. Am. Ceram. Soc., 38, 10, 370 (1955).
I. KASHIF, H. FAROUK, S. A. ALY, F. A. MOUSTAFA, A. M. SANAD and Y. M. ABO-ZEID, J. Mater. Sci. Mater. Elec. 2 (1991) 216.
K. TANAKA, K. HIRAO and N. SOGA, J. Non-Cryst. Solids 85 (1986) 228.
A. L. HUSSEIN, F. A. MOUSTAFFA, Z. ABD EL HADI and A. G. MOUSTAFA, Indian J. Pure Appl. Phys. 21 (1983) 137.
H. MOORE and H. WINKELMANN, J. Soc. Glass. Technol. 39 (1955) 213.
A. KARKI, S. FELLER, Hun P. LIM, J. STARK, SANCHEZ and M. SHIBATA, J. Non-Cryst. Solids 92 (1987) 11.
A. A. AHMED and A. F. ABBAS, ibid. J. Non-Cryst. Solids 80 (1986) 371.
T. MEOLLER, “Inorganic chemistry” (Asia Publishing House, New York, 1968).
A. G. MOSTAFA, Ph. D. Thesis, Al-Azhar University Egypt (1975).
A. S. TENNY and J. WONG, J. Chem. Phys. 56 (1972) 5516.
K. J. MOE, Phys. Chem. Glass 6 (1965) 46.
P. E. JELLYMAN and J. P. PROCTER, J. Soc. Glass Technol. 175T (1960).
B. D. P. BUTTON, R. TANDON, C. KING, M. H. VELEZ, H. TULLER and D. R. UHLMANN, J. Non-Cryst. Solids 49 (1982) 1117.
J. M. HUNT, M. P. WISHERD and L. C. BONHOM, Anal. Chem. 22 (1950) 1478.
A. M. SANAD, T. Z. ABOU EL-NASR, M. F. FAHMY and I. KASHIF, Egypt J. Solid., 5 (1984) 70–89.
I. KASHIF, H. FAROUK, A. M. SANAD, S. A. ALY and H. FARHAN, Phys. an glasses 3 (1991) 3.
T. ABE, J. Am. Ceram. Soc. 49 (1966) 11.
R. L. MOZZI and B. E. WARREN, J. Appl. Crystollogr. 3 (1970) 25.
I. KASHIF, A. M. ABO EL-AZM, S. S. GOMAA, A. M. SANAD and E. E. ASSEM, Phys. Chem. Glasses 30 (1989) 5.
N. TOHGE and J. D. MACKENZIE, J. Non-Cryst. Solids, 68 (1984) 411.
M. IRION, M. CAUZI, A. LEVASSEUR, J. M. REAW and J. C. BRETHOUS, J. Solid State Chem. 31 (1980) 285.
S. RAN and K. RAM, J. Mater. Sci. 23 (1988) 4541.
J. S. BERKES and W. B. WHITE, Phys. Chem. Glasses 7 (1966) 6.
O. S. DYMSHITS, A. A. ZHILIN, T. I. CHUVAEVA and M. P, SHEPILOV J. Non-Cryst. Solids 127 (1991) 44.
R. OYAMADA, A. KISHIOKA and K. SAMI J. Non-Cryst. Solids 95 (1987) 709.
W. H. TURNER and I. A. TURNER, J. Mater. Sci. 55 (1972) 201.
K. TANAKA, K. HIRAO and N. SOGA, Phys. Chem. Glasses 34 (1993) 3.
E. BALOCCHI, A. MANTENERO, M. BETTINELLI and A. SATGIU, J. Non-Cryst. Solids 46 (1981) 203.
B. N. FIGGIS and I. LEWIS, “The magnetic properties of transition metal complexes” (John Wiley and Sons, New York, 1964).
B. U. R. CHOWDARI, K. L. TAN, W. T. CHIA and R. GOPALOKRISHNASS J. Non-Cryst. Solids 128 (1991) 18.
A. MAROTTA, P. PERNIC, A. ARONNE and BARI, J.Non-Cryst. Solids 127 (1991) 159.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Farouk, H., Abo-Zeid, Y.M., Khaled, M.A. et al. Structure and physical properties of sodium borate glasses containing nickel oxide. J Mater Sci: Mater Electron 6, 393–396 (1995). https://doi.org/10.1007/BF00144640
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00144640