Abstract
The measurement of J-resistence curves and their proof values at crack initiations are carried out with the method of three curves from a single specimen by using 12CrlMoV, 1.25Cr0. 5MoSi, 16MnR steels and two weld metals. The results of the single specimen are in agreement with those of the standard multi-specimen method. It shows from the experiments that the connected analyses of the three curves from a single specimen are in accordance with the physical fracture processes of precracked three point bending specimens. The ductile crack extension of the materials tested follows the power law relation.
Similar content being viewed by others
References
ASTM E813-87.
J.A. Joyce, in Fracture Mechanics, ASTM STP 791 (1983) I543–I560.
G.A. Clark, W.R. Andrews, P.C. Paris and D.W. Schmidt, in Mechanics of Crack Growth, ASTM STP 590 (1976) 27–42.
H. Herrera, and J.D. Landes, in Fracture Mechanics: 21 st Symposium, ASTM STP 1074 (1990) 24–43.
X.W. Li and Y. Liu, Engineering Fracture Mechanics 30(4) (1988) 445–450.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Hang, M., Zheng, W. & Liang, Z. The measurement of J-R curves and J-integral values at crack initiations for metallic materials with three curve method of single specimen. Int J Fract 68, 45–54 (1994). https://doi.org/10.1007/BF00032325
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00032325