SN Applied Sciences

, 1:159 | Cite as

CeO2–TiFe2O4 nanocomposite for effective removal of uranium ions from aqueous waste solutions

  • El Said A. Nouh
  • T. A. Lasheen
  • Rabab M. El-sherif
  • N. A. Abdel Ghany
  • E. A. Jebril
Research Article
Part of the following topical collections:
  1. 1. Chemistry (general)


The present work deals with the preparation of Cerium oxide Titanium Ferrite (CTF) nanocomposite using a simple solvothermal method. The synthesized CTF nanocomposites were characterized using FT-IR, XRD, BET surface area, VSM and TEM. The adsorption action of CTF nanocomposite towards U(VI) was optimized using batch experiments by varying solution pH, initial concentration, sorbent dosage and rate of adsorption. The loaded uranium was efficiently desorbed using 0.1 M HNO3. The Kinetic studies indicated that the adsorption process follows pseudo-second-order equation. Freundlich and Halsey adsorption isotherm was modeled, it proves the multilayers adsorption process. The calculated thermodynamic parameters show that the adsorption process of U(VI) onto CTF nanocomposite was spontaneous and endothermic in nature. The fabricated nanocomposite was applied successfully for removal of uranium species from waste solutions. The obtained results indicated that CTF nanocomposite was a promising and excellent adsorbent for uranium ions removal in comparison with other reported ones. Moreover, the process was very simple, fast and easily reusable several times.


Uranium Magnetic Nanocomposite Adsorption Waste solutions 

1 Introduction

Uranium is a radioactive metal that is found in a variety of rocks, soils and aqueous sources. It is released into environment naturally or as contaminant through mining processing, fuel manufactures and other related industrial activities [1, 2]. In some contaminated regions waste disposal sites can attain as high as several tens of mg/L which eventually may found their way into soil, drinking water and human beings [3]. It leads to dangerous pollution and severe effect to human health [4, 5, 6], including, kidney tubular cells damage, liver disease and thyroid. Also, it affects bone development and maintenance, especially in children [7]. Due to uranium radioactivity may cause damage of DNA and can lead to several types of cancer [7, 8]. Over the past decades, several traditional methods have been developed to remove uranium ions from aqueous waste solutions such as membrane dialysis, precipitation, ion exchange, solid phase extraction and solvent extraction [9, 10, 11, 12, 13, 14]. In this context, adsorption procedures have been found to offer much greater extraction capacity and efficiency.

Nanomaterials continue to attract much interest because of their properties differ greatly from those of atoms and molecules as well as from those of bulk Materials [15]. Using of nanoparticles (NPs) as adsorbents have been extensively studied because of their unique chemical and physical properties such as high surface area and chemical activity, compared to classical adsorbent materials [16]. Synthesis of nanometer scale mixed oxide particles, such as spinel ferrite, magnetite, titanium-based various binary and ternary mixed oxides have been reported for their remarkable magnetic and conducting properties [17, 18, 19, 20]. The use of iron oxide NPs has found many applications in a variety of fields. Both forms of magnetic iron oxide NPs, Fe2O3 and Fe3O4, have superparamagnetic properties, enabling them to behave as a giant paramagnetic atom with a fast response to the external magnetic field. Magnetic NPs are suitable sorbents due to their good dispersion in solution, their high specific surface area and their ability to controlled and separated with an external magnetic field [16, 17]. Also, TiO2 exhibits very favorable sorption properties through inner- sphere complex formation [21, 22].The incorporation of titanium and cerium ions with ferrites NPs leads to an increase of coercivity due to the coupling of the spins between titanium and cerium ions on hand and iron ions on other [23, 24]. This behavior makes the NPs to be more efficient and attractive in separation of impurities from different effluents.

Lichao Tan et al. [25] suggested cobalt ferrite/multiwalled carbon nanotubes magnetic hybrids for removal U(VI) from wastewater. They pointed out that the maximum capacity for U(VI) was 212.7 mg/g under optimum conditions. Magnetic nanocomposite (Fe3O4@C@Ni–Al LDH) of U(VI) adsorption capacity of 174.1 mg g−1 was reported by Zhang et al. [26]. Fan et al. [27] investigated removal of U(VI) from aqueous solutions by magnetic composite of Fe3O4@SiO2, showing maximum adsorption capacity of uranyl ions of 52 mg g−1. Other reported modified magnetic nanoparticles showed moderate sorption capacities for uranyl ions and radioactive species [28, 29, 30, 31].

In our previous work we reported the synthesis of TiO2–CeO2–Fe2O3 nanoparticles (NPs) using co-precipitation method for using in U(VI) removal from aqueous solutions [32]. Herein, we extended our study for preparation of an efficient magnetic nanocomposite (CeO2–TiFe2O4) using simple and fast solvothermal method in order to use for removal of uranium ions from waste samples solutions. The prepared CTF nanocomposites were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM), Brauner Emette Teller surface area (BET), Fourier Transform Infra-Red spectroscopy (FTIR) and vibrating sample magnetometer (VSM). The optimum parameters that influence the adsorption of U(VI) by CTF NPs, including pH, contact time, adsorbent dosage, U(VI) initial concentration and temperature were discussed. Isotherm models were proposed to explain the sorption characteristics of nanoadsorbents. Kinetic and thermodynamic parameters of the adsorption process were also calculated to discuss the adsorption process.

2 Experimental

2.1 Materials

All chemicals and reagents were of an analytical grade. TiCl4 (≥ 99%, Merck Co.Ltd., France), CeCl3.7H2O (Sigma Chemical Co. Ltd., USA), FeSO4.7H2O, (> 98%, Nice Chemicals Pvt. Ltd. India) ethanol (absolute, (Sigma Aldrich Co. Ltd., USA) were used without further purification. Uranium (IV) stock solution (1000 mg L−1) was prepared by dissolving 2.11 g of UO2(NO3)2·6H2O (Sigma-Aldrich, Germany) in 1 L of 0.05 M HNO3.

2.2 Synthesis of CeO2–TiFe2O4 nanoadsorbent

CeO2–TiFe2O4 NPs were prepared by using solvothermal method. Stoichiometric amounts of 2 M FeSO4·7H2O, 0.5 M TiCl4 and CeCl3·7H2O were dissolved in a mixture of 60 mL of ethylene glycol and 40 mL of de-ionized water while stirring for 30 min then sonicated using an ultrasonic processor for 15 min. To the latter, ammonia solution was added drop wisely, sonicated for 15 min, then heated to 180 °C for 24 h in a Teflon-lined autoclave. After cooling down to room temperature, the precipitate was centrifuged, collected and washed repeatedly with de-ionized water and ethanol then dried for 12 h at 60 °C.

2.3 Characterization

XRD characterization of the prepared nancomposite was carried out using (X, PERT—PRO—PANalytical—Netherland) with CuKα radiation operating at 40 kV and 30 mA. FT-IR measurements were made with JASCO FTIR 460 plus spectrometer over wavenumber range of 4000–400 cm−1. The spectra of magnetic nanomaterials were taken as KBr pellets.

The size and morphology of the nanocompsites before and after sorption were examined by high resolution transmission electron microscopy (A JEOL-2100) and scanning electron microscopy equipped with EDX (ESEM model Philips XL 30).

The surface area and pore volume of magnetic nanoadsorbents were measured by performing N2 adsorption and desorption using surface area and porosity analyzer (AUTOSORB-1, Model No = AS1 MPV6-11, USA) and the surface area was calculated by Brunauer–Emmett–Teller (BET) equation as well. However, pore size distributions were calculated from the adsorption branch of the N2 adsorption/desorption isotherms using the Barret–Joyner–Halenda (BJH) method. Magnetic characteristics of the prepared nanocomposites were measured by vibrating sample magnetometer (VSM).

2.4 Batch adsorption experiments

To achieve adsorption equilibrium, an amount of the adsorbent (0.005 g) was added into U(VI) solution in polyethylene tube. The pH was adjusted to the desired value by 0.1 M HNO3 and NaOH solutions. The mixture was shaken for 2 h in a temperature controlled water bath shaker. After equilibrium, the supernatant liquids were centrifuged. The residual U(VI) concentration in supernatant was spectrophotometerically determined using arsenazo-III at wavelength 655 nm [33]. The effects of pH, contact time, initial concentrations and temperature on adsorption of uranium (VI) were investigated to obtain the maximum efficiency.

The removal efficiency (%) and the adsorption capacity (mg g−1) of U(VI) were determined using.

Equations (1) and (2), respectively:
$${\text{R}} = \frac{{{\text{C}}_{0} - {\text{C}}_{e} }}{{C_{0} }} \times 100\%$$
$$q_{e} = \frac{{\left( {{\text{C}}_{0} - {\text{C}}_{e} } \right){\text{V}}}}{\text{W}}$$
where R is the removal efficiency, Co, Ce is the initial and equilibrium U(VI) concentration (mg L−1), respectively, qe is adsorption capacity, V is the volume of uranium solution (L) and W is the weight of CTF nanoadsorbent (g).

2.5 Desorption and regeneration

Firstly, Uranium(VI) loaded CTF nancomposite was washed several times with de-ionized water then 0.1 mol L−1 HNO3 was used as eluting agent to desorb U(VI). The adsorbents were separated from the solution by centrifugation, then the CTF nancomposites were dried and reused in adsorption experiments. The above procedure was repeated six times to test the reusability of the magnetic nanoadsorbents until U(VI) were not detected in the rinsing solution. The desorption efficiencies were calculated from the concentration of adsorbed U(VI) onto CTF nanoadsorbent and the final U(VI) concentration in the desorption medium.

3 Results and discussions

3.1 Characterization of nanoadsorbent

A typical X-ray diffraction pattern of the prepared CTF nanocomposite is shown in Fig. 1. As can be seen, the major characteristic peaks of TiFe2O4 were found at 2θ = 18.102, 25.535, 32.522, 36.550, 37.345, 41.03, 45.9, 48.791, 59.8, 65.5, 69.3 and 76.7, references code (04-008-6392). On the other hand the cubic CeO2 peaks were identified at 2θ = 28.550, 33.077, 47.490 and 56.328 corresponding to references code (00-04-0593). Additional peaks observed at 2θ = 54.02 and 72.2 are due to Fe2O3. According to the above mentioned XRD results, we can conclude that the structure of the nanocomposite is CeO2–TiFe2O4.
Fig. 1

XRD patterns of synthesized CTF nanocomposite

FT-IR spectrum of CTF nanocomposite before and after loading by uranium species were presented in Fig. 2. The two broad bands observed at 3431 cm−1 and 1631 cm−1 were due to the O–H stretching vibrations, however, the small peaks observed at 2924 and 1451 cm−1 were due to C–H stretching vibration and C–H bending, respectively, they were attributed to presence of ethylene glycol on the surface of CTF nanocomposite [34, 35]. The band at 1120 cm−1 was due to presence of CeO2 [36]. While the absorption band located at 589 cm−1 was assigned to the stretching vibration band of Fe–O bond. As a consequence of uranium adsorption onto nanocomposite surface, a new band was appeared at 880 cm−1 which may be attributed to antisymmetric stretching vibration of O=U=O bands, confirming a successful U(VI) sorption as uranyl ions or uranyl complexes [37].The lack of the strong peak at 1380 and 1530 cm−1 for CTF nanoadsorbent after loading with U(VI) clearly indicates that no nitrate ions as counter ions or chelating agent was co-sorbed with U(VI) [38]. In such case, the U(VI) ions were probably sorbed in hydroxide complex form or positive charge species by cation-exchange mode [38]. Also, the nanocomposite charateristic bands were slightly shifted and become less intense after uranium adsorption onto CTF nanocomposite, Fig. 2b. After adsorption process, the formed uranium layers on the surface of the nanoadsorbent reduces the intensities of the characteristic bands of CTF nanocomposite as well as causing a shift of their positions. The bands of Fe–O, CeO2, C–H and O–H were shifted from 589, 1120, 1451, 1631 cm−1 to be 566, 1057, 1438 and 1629 cm−1, respectively, after uranium loading on to CTF nanoadsorbent. The shift of bands due to adsorption of uranium was also reported by others [14, 39].
Fig. 2

FT-IR of CTF nanoparticles (A) before U(VI) adsorption (black line) and (B) after U(VI) adsorption (red line)

The size, distribution and morphology of the prepared nanoparticles (NPs) were examined by, TEM, HRTEM and EDX techniques as shown in Fig. 3. The TEM images show that CTF NPs are polydispersed with particle size ranged from 1.91 to 19 nm. The measured inter-planar spacing and the lattice d-spacing of CeO2–TiFe2O4 were 0.12 nm and 1.1 nm, respectively. The agglomeration of the nanoparticles can be well observed, pertaining to the high surface energy and magnetic interactions between them [40].
Fig. 3

TEM images of CTF nanoparticles

The presence of uranium in the loaded CeO2–TiFe2O4 nanoadsorbent was confirmed from (EDX) measurement, Fig. 4. It shows distinct signals at 3.3 and 3.4 keV corresponding to uranium species, it was sufficient for providing a qualitative idea of the homogeneous distribution of U ions at the surface of the sorbent, the percentage (in mass) of U was 30.72 and 26.78%, respectively.
Fig. 4

EDX spectrum analysis of CeO2–TiFe2O4 nanocomposite loaded by U(VI)

BET surface area measurements are performed and summarized in Table 1. The surface area, pore volume, and pore size of CeO2–TiFe2O4 are 72.459 m2/g, 0.118 cc/g, and 1.925 nm, respectively. Also, BET results confirmed the formation of nano-scale size CeO2–TiFe2O4 particles. The obtained parameters assured the good adsorption behavior of the CTF nanocomposite.
Table 1

Physical parameters of CTF nanoadsorbent

Particles size (nm)

Surface area (m2/g)

Pore volume (CC/g)

Pore radius (nm)

Magnetization (emu/g)

Remenance (emu/g)

Coercivity (Hci) (G)








3.2 Magnetic properties

Chemical composition of magnetic materials, cation distribution and average size have a significant role in the determination of the magnetic properties of the NPs and the possible applications [41]. The magnetic properties of CTF NPs are investigated at the ambient temperature under an applied field using the VSM technique. Figure 5 shows the hysteresis loops of the CTF nanocomposite. It exhibited superparamagnetic behavior with a high magnetic saturation MS value of 24.193 emu/g at room temperature. The magnetic properties of CTF NPs were found good in comparison with that of TiO2–CeO2–Fe2O3 NPs previously reported by us [32], where the saturation magnetization of the latter was 0.32096 emu/g. The hysteresis loop of TiO2–CeO2–Fe2O3 showed paramagnetic behavior. In addition, it was observed that the magnetization of TiO2-CeO2–Fe2O3 is not saturated, as it is probably due to the coexistence of paramagnetic atoms in the particles. On the other side CeO2–TiFe2O4 nanoparticles exhibited good magnetic properties (MS 24.193 emu/g).The hysteresis loop of CeO2–TiFe2O4 confirmed its ferromagnetic behavior as the magnetization reached saturation. Furthermore, the calculated normalized remanence values (Mr) and the coercivity (Hc) were 2.367 and 97.961 G, respectively. These results indicate that CeO2–TiFe2O4 NPs possesses a high magnetic responsively and can be easily separated during the sorption experiments.
Fig. 5

VSM hysteresis loops of CeO2–TiFe2O4 nanohybrid oxide

3.3 Adsorption process

3.3.1 Effect of initial pH

A series of experiments were performed to investigate the effect of solution pH on uranium uptake by CTF NPs. The obtained results in Fig. 6 showed that the adsorption capacity of uranium increased from 17.08 to 79 mg g−1 as the pH increased from 2.00 to 6.00. By increasing the pH more than 6.00, the adsorption capacity was slightly decreased to reach 71.6 mg g−1 at pH 12.00. The lower adsorption capacity at low acidic conditions is due to competition of H+ for binding sites of CTF nanocomposite with UO22+ ions. However, the adsorption capacity reaches maximum at pH 6. At such pH the NPs surface became negatively charged due to deprotonation reaction [42] and the electrostatic attraction increased between uranium species and negative charge on nanoparticles surface which led to an increase of U(VI) adsorption capacity. The distribution of uranium chemical species is represented in scheme S1 [43]. It is obvious that uranyl ions may present as positively charged cationic species, such as UO22+ monomer, [(UO2)2(OH)2]2+ dimer and [(UO2)3(OH)5]+ trimer [44, 45]. Multi-nuclear hydroxide complexes such as [(UO2)3(OH) 5] + are the predominate species at pH 6 and no insoluble species were observed. These species may be more favored by the sorbent, since the maximum sorption of U(VI) in many different sorbents occurred at pH 6–8 [46, 47]. The deprotonated sites of CTF nanoadsorbent are more available to retain uranium ions and surface complexation between uranium species and CTF nanoparticles is facilitated. At pH > 6.00 uranium ions exist in an anionic forms such as UO2(CO3) 3 4− , (UO2)2CO3(OH) 3 , UO2(OH) 3 etc. [48], these anions have a relatively low adsorption affinity. Thus, pH 6.00 was chosen as optimum for adsorption process.
Fig. 6

Effect of initial pH on adsorption capacity of CeO2–TiFe2O4 (amount of adsorbent 0.005 g, U(VI)initial = 20 mg L−1, shaking time 120 min at 25 °C)

3.3.2 Effect of CTF composite dose

The dependence of U(VI) removal on amount of adsorbent was studied at pH 6 using 20 mL of 20 mg L−1 U(VI) solution at 25 °C for 120 min. The results given in Fig. 7, demonstrate that the sorption efficiency of uranium ions increases rapidly with increasing sorbent mass from 1 mg to 5 mg. This is due to large number of active centers on the surface [49].
Fig. 7

Effect of adsorbent amount on U(VI) uptake by CTF nanoparticles (pH 6.00; amount of adsorbent dose 0.001–0.1 g; [U(VI)]initial 20 mg L−1; shaking time 120 min)

3.3.3 Effect of contact time and adsorption dynamics

The contact time effect on U(VI) uptake capacity of CTF nanocomposite was studied using different U(VI) initial concentration (20, 50 and 70 mg L−1). The obtained results in Fig. 8, showed that the maximum amount of U(VI) was adsorbed at 120 min for the three tested concentrations. The maximum adsorption capacity (qe) was 79, 178 and 245 mg g−1, corresponding to U(VI) initial concentration of 20, 50 and 70 mg L−1, respectively. There is almost no further increase of adsorption beyond 120 min and the initial concentration did not show any significant effect on the time to reach equilibrium. It proves that the U(VI) adsorption capacity increases with its initial concentration increasing. It provides higher driving force that facilitates diffusion of ions from the bulk solution to active sites assembly. Thus the initial U(VI) concentration plays an important role in determining the maximum uptake capacity of the CTF for U(VI) [50].
Fig. 8

Effect of contact time on uranium(VI) adsorption using different initial uranium concentration (pH 6.0; temperature 25 °C; amount of CTF NPs 0.005 g)

Adsorption kinetics is one of the most attractive characteristics to be responsible for the efficiency of adsorption. It is useful for adsorption studies to predict the rate of adsorption and provide valuable data for understanding the mechanism of sorption and the reaction pathways. Actually, most adsorption reactions take place through external film diffusion, intra-particle diffusion and interaction between adsorbate and active sites. Sorption of uranium by the CTF NPs as a function of time was illustrated in Fig. 8. It showed clearly a fast increase in uptake of uranium ions by CTF NPs in the first 2 h of the adsorption then remains constant The obtained data were modeled using pseudo-first-order, pseudo-second-order and intra-particle diffusion.

The pseudo-first- order was calculated according to equation (S1) in Supporting Information (SI). The obtained results of pseudo-first-order adsorption featured in Fig. 9a, indicate that the data did not fit well. The values of K1 along with the corresponding correlation coefficient at different concentrations are presented in Table 2. As shown, the calculated values of qe does not agree with the experimental ones besides its low related coefficients R2. These results indicate that the adsorption mechanism of uranium ions on CTF does not follow a pseudo-first-order kinetic model well.
Fig. 9

Adsorption kinetics models for U(VI) adsorption onto CTF nanocomposite, a Pseudo-first-order model plot. b Pseudo-second-order model plot. c Intra-particle diffusion model plot. Conditions (pH 6.0; temperature 25 °C; amount of CTF NPs 0.005 g)

Table 2

Parameters of various kinetics models fitted to experimental data

C0 (mg L−1)

Pseudo first order

Pseudo second order

Intraparticle diffusion

qe (mg g−1)

K1 (min−1)


qe (mg g−1)

K2 (g mg−1 min−1)


C (mg g−1)

































In order to study pseudo-second-order adsorption (see equation S2) a plot of t/qt versus t is plotted in Fig. 9b. The obtained straight line and the perfect regression analysis R2 = 0.999 prove that the pseudo-second-order kinetic model can be applied to predict the adsorption kinetic, and the process of uranium sorption on CTF NPs is well described by pseudo second order kinetic model, Table 2. It implies that the dominant mechanism for U(VI) adsorption on CTF NPs is chemisorption or strong surface complexation rather than mass transport [51].

To identify the mechanism involved in the adsorption by the intra-particle diffusion technique (see equation S3) a plot of t1/2 versus qt was represented in Fig. 9c. The values of Ki (the intra-particle diffusion rate constant mg g−1 min−1/2) and C adsorption constant (thickness of the boundary layer) are calculated from intercept and slope regression analysis [52, 53, 54, 55, 56]. The results in Table 2 show that the experimental data does not follow the intra-particle diffusion model, i.e. the intra-particle diffusion is not rate limiting step.

3.3.4 Adsorption isotherm

In this study, several isotherm models were selected to fit the obtained experimental data regarding to the adsorption of uranium onto CTF NPs. They are namely Langmuir, Freundlich, Temkin, Dubinin Radushkevich (D–R) and Halsey models.

Langmuir isotherm model was described by equation S4. The plot of Ce/qe versus Ce at different temperatures was shown in Fig. 10a. The values of Qm and KL can be estimated from the slopes and intercepts of the straight lines, Table 3. Adsorption of U/CTF NPs exhibited maximum sorption capacity of 476.2 mg of U(VI)/g of sorbent at pH 6 from aqueous solutions. The sorption capacity of CTF nanoparticles was found greater than that obtained by TiO2–CeO2–Fe2O3 nanoparticles previously reported by us [32]. Table 4 showed comparison of CTF nanoparticles sorption capacity with other reported ones. It indicated that CTF nanoparticles are an excellent adsorbent for uranium ions.
Fig. 10

Adsorption isotherms for U(VI) adsorption onto CTF nanocomposite, a Langmuir isotherm plot, b Freundlich isotherm plot, c Halsey isotherm plot, d Temkin isotherm plot, e D–R isotherm plot. Conditions (pH 6.00; temperature 25–55 °C; amount of CTF NPs 0.005 g)

Table 3

Parameters of various isothermal models fitted to experimental data

Isotherm models


25 °C

35 °C

45 °C

55 °C



































3 × 10−5

4 × 10−5

5 × 10−5

7 × 10−5











































Table 4

Comparison of CTF nanoadsorbent capacity towards U(VI) with the other reported ones

Adsorbent material

Initial pH

Contact time (min)

Temperature (°C)

Adsorption capacity(mg/g)





















Iron oxyhydroxide









Cerium vanadate




















This work

The essential features of the Langmuir isotherm model expressed in terms of a dimensionless constant separation factor or equilibrium parameter RL [57], which is defined by equation S5. In this study, the values of RL lie between 0.041 and 0.446 for all concentration and temperature ranges. This indicates the suitability of the CTF as an adsorbent for adsorption of uranium ions from aqueous solution under the conditions used in this study.

The Freundlich model is expressed by equation S6. The linear plot of lnqe versus lnCe is presented in Fig. 10B.

It was reported that the freundlich isotherm constant can be used to explore the favorability of adsorption process. When value of n within 1 < n < 10, it gives an indication of the favorability of adsorption. In our work it was found that the values of n are situated in this range Table 3, implies stronger interaction between sorbent and uranium ions demonstrating that the adsorption process is favorable.

The Halsey adsorption isotherm was given by equation S7 and the isotherm parameters were obtained from the plot of ln qe versus ln (1/Ce), Table 3. Definitely, the fitting of the experimental data to this equation attest to the heteroporous nature of the adsorbent, Fig. 10c.

The Temkin isotherm was expressed by equation S8. The calculated isotherm parameters are listed in Table 3 and illustrated in Fig. 10d. The linear plot of qe versus lnCe, Fig. 10d, yields the constant bT from 0.023 to 0.029 suggesting chemisorption and physisorption involved in the adsorption of the U(VI) ions. On the other hand, the greater values of AT indicate greater affinity toward the adsorbate [58].

The simple linear form of D–R isotherm is represented in equation S9. The plot between ln qe and ε2 (Fig. 10e) yields the constant K which is used to calculate the mean free energy E of sorption per molecule of the sorbate when it is transferred to the surface of the solid from infinity in the solution (see equations S10 and S11) [59].

The estimated values of E lie between 7.2 and 7.6 kJ mol−1 indicating the physisorption mechanisms. Based on the data given in Table 3, the Freundlich and Halsey models appear to be the best fitting models for uranium adsorption depending on correlation coefficient R2 where it is very high than Langmuir, Temkin and D–R models.

3.3.5 Effect of temperature and adsorption thermodynamics

The adsorption experiments at different temperatures were performed to evaluate the influence of temperature (25–55 °C), Fig. 11. The results showed that the adsorption of uranium ions is favored by an increase in temperature. The temperature dependence of the adsorption process is associated with changes in several thermodynamic parameters such as enthalpy (ΔH) and entropy (ΔS) of adsorption, which are calculated from the slope and intercept of the linear variation of lnKd versus 1/T, Fig. 12, using the following equation:
$$\ln \,{\text{K}}_{\text{d}} = - \frac{{\Delta {\text{H}}^{ \circ } }}{\text{RT}} + \frac{{\Delta {\text{S}}^{ \circ } }}{\text{R}}$$
where Kd is the distribution coefficient (mL/g), T is absolute temperature (K), and R is the ideal gas constant (8.314 kJ mol−1 K−1). The standard free energy values (ΔG) are calculated from:
$$\Delta G^{\circ } =\Delta H^{\circ } {-}T\Delta S^{\circ }$$
Fig. 11

Adsorption isotherm of U(VI)/CTF NPs at different temperatures (pH 6.0; temperature 25–55 °C; amount of CTF NPs 0.005 g)

Fig. 12

Relationship curve between lnKd and 1/T

The obtained thermodynamic parameters from Eqs. (3) and (4) are presented in Table 5. The positive value of ΔH° confirms the endothermic nature of adsorption.
Table 5

Thermodynamic parameters for U(VI) adsorption onto CTF nanoadsorbent

ΔH° (KJ mol−1)

ΔS° (J mol−1 K−1)

ΔG° (KJ mol−1)

298 K

308 K

318 K

328 K



− 27.630

− 28.557

− 29.485

− 30.412

The positive value of ΔS° shows the increase of randomness at the solid–liquid interface during the adsorption of U(VI) onto CTF NPs. The positive entropy (ΔS°) favors complexation and stability of sorption [60]. Positive change in entropy favors a slower sorption of U(VI) onto active sites of the adsorbent. This result is in agreement with the fact that uranium sorption attains an equilibrium within 120 min. Also, it is compatible with the results of the kinetic studies. Where the adsorption process was described by pseudo second order kinetic model which implies that the dominate mechanism is surface complexation or chemisorption.

According to Table 5, all values of ΔG° are negative, which indicate the feasibility of the adsorption process and the spontaneous nature of adsorption. With an increase of temperature, the values of ΔG° are more negative, which suggests that the equilibrium capacity increases. From the above results, the performance of U(VI) sorption on the as-prepared adsorbent is more favorable at higher temperatures.

3.3.6 Desorption and regeneration

Regeneration of CTF NPs was investigated to evaluate its potential application in the removal and recovery of uranium species. The data illustrated in Fig. 13, implies that the adsorbed ions can be desorbed from spent adsorbent in an acid medium. Hence, desorption study was conducted using HNO3 solution having concentration range between 0.01 and 1 M. The desorption efficiency of HNO3 concentrations of 0.01, 0.05, 0.1, 0.5 and 1 M was found 92.18%, 93.54%, 98.96%, 98.92%, 98.64%, respectively. Therefore, 0.1 M HNO3 was determined as optimum desorptive concentration. To assess the reusability of the adsorbent, the adsorption–desorption experiments with 0.1 M HNO3 was repeated six cycles. The adsorption efficiency of the CTF NPs decreased from 98.96% in the first cycle to 89.8% in the six cycles (Fig. 14). These entire make the CTF NPs to be used as a good and efficient adsorbent in waste management of radioactive species.
Fig. 13

Recycled efficiency of CTF nanoadsorbent in removal of U(VI)

Fig. 14

CTF nanocomposite adsorption capacity towards U(VI) of waste solutions sample with different concentrations of U(VI) (2.5, 16, 23, 37 mg L−1)

3.3.7 Application

The fabricated nanocomposite was used for removal of U(VI) from waste solutions derived from routine operations of uranium concentrate purification at Nuclear Material Authority (NMA), Anshas, Egypt. Figure 14 indicated the successful removing of uranium species from derived wastes of different concentration.

4 Conclusion

A synthesized magnetic CTF nanocomposite was successfully applied as a novel and effective sorbent for the removal of U(VI) from aqueous solutions either at low or high levels of uranium concentrations. The sorption ability of U(VI) on fabricated NPs was strongly dependent on pH values. The sorption process was fast and 120 min was enough to achieve the sorption equilibration. The sorption isotherms of U(VI) on the prepared nanocomposite were described well by Frendlich and Halsey models and kinetically fitted with a pseudo-second-order model. The calculated thermodynamic parameters demonstrated that the endothermic heat of adsorption, and it was spontaneous. Easily desorbing of the adsorbed U(VI) from the synthesized nanocomposite several times makes the magnetic CTF nanocomposite act as a perfect adsorbent to remove uranium ions from solution at low and high concentrations.


Compliance with ethical standards

Conflict of interest

The authors declare that they have no conflict of interest.

Supplementary material

42452_2019_176_MOESM1_ESM.docx (74 kb)
Supplementary material 1 (DOCX 73 kb)


  1. 1.
    El-Ansary AL, Abd El-Wahab G, Bayoumi EE, Nouh ESA (2018) Purification of Abu-Zenima wet crude yellow cake using alkaline leaching of U (VI). Egypt J Pet 27:523–530CrossRefGoogle Scholar
  2. 2.
    Nouh ESA, Amin MI, Gouda MM, Abd Almagid A (2015) Extraction of uranium (VI) from sulfate leach liquor after iron removal using manganese oxide coated zeolite. J Environ Chem Eng 3:523–528CrossRefGoogle Scholar
  3. 3.
    Klimova S, Oernik M, Lacinova L, Filip J, Janick D, Zboril R (2011) Zero-valent iron nanoparticles in treatment of acid mine water from in situ uranium leaching. Chemosphere 82:1178–1184CrossRefGoogle Scholar
  4. 4.
    International Atomic Energy Agency (2001) Handling and processing of radioactive waste from nuclear applications; TRS No. 402. IAEA, ViennaGoogle Scholar
  5. 5.
    Bhalara PD, Punetha D, Balasubramanian K (2014) A review of potential remediation techniques for uranium (VI) ion retrieval from contaminated aqueous environment. J Environ Chem Eng 2:1621–1634CrossRefGoogle Scholar
  6. 6.
    Gu B, Liang L, Dickey MJ, Yin X, Dai S (1998) Reductive precipitation of uranium(VI) by zero-valent iron. Environ Sci Technol 32:3366–3373CrossRefGoogle Scholar
  7. 7.
    Banning A, Benfer M (2017) Drinking water uranium and potential health effects in the German Federal State of Bavaria. Int J Environ Res Public Health 14:927CrossRefGoogle Scholar
  8. 8.
    Collman GW, Loomis DP, Sandler DP (1991) Childhood cancer mortality and radon concentration in drinking water in North Carolina. Br J Cancer 63:626–629CrossRefGoogle Scholar
  9. 9.
    Comarmond MJ, Payne TE, Collins RN, Palmer G, Lumpkin GR, Angove MJ (2012) Inhibition of uranium(VI) sorption on titanium dioxide by surface iron(III) species in ferric oxide/titanium dioxide systems. Environ Sci Technol 46:11128–11134CrossRefGoogle Scholar
  10. 10.
    Amaral JCBS, Morais CA (2010) Thorium and uranium extraction from rare earth elements in monazite sulfuric acid liquor through solvent extraction. Miner Eng 23:498–503CrossRefGoogle Scholar
  11. 11.
    Thakur P, Chakravortty P, Dash KC, Ramamohan TR, Reddy MLP (1998) Synergistic extraction of uranium (VI) by mixtures of β-diketones and structurally related crown ethers. Radiochim Acta 80:155–161CrossRefGoogle Scholar
  12. 12.
    John AMS, Cattrall RW, Kolev SD (2010) Extraction of uranium(VI) from sulfate solutions using a polymer inclusion membrane containing di-(2-ethylhexyl) phosphoric acid. J Membr Sci 364:354–361CrossRefGoogle Scholar
  13. 13.
    Ali AH, Nouh ESA (2018) Rhodamine-B modified silica for uranium(VI) extraction from aqueous waste samples. Sep Sci Technol. CrossRefGoogle Scholar
  14. 14.
    Shaabana AF, Khalila AA, Lasheenb TA, Nouh ESA, Ammar H (2018) Polyamidoamine dendrimers modified silica gel for uranium(VI) removal from aqueous solution using batch and fixed-bed column methods. Desalin Water Treat 102:197–210CrossRefGoogle Scholar
  15. 15.
    Nouh ESA, Roy M, Sarkar S (2012) Glucose stabilized magnetic palladium nanoparticles exhibiting enhanced magnetic properties under exposure to hydrogen. Mater Express 2:275–284CrossRefGoogle Scholar
  16. 16.
    Veiseh O, Gunn JW, Zhang M (2010) Design and fabrication of magnetic nanoparticles for targeted drug delivery and imaging. Adv Drug Deliv Rev 62:284–304CrossRefGoogle Scholar
  17. 17.
    Lu AH, Salabas EL, Schuth F (2007) Magnetic nanoparticles: synthesis, protection, functionalization, and application. Angew Chem Int Ed 46:1222–1244CrossRefGoogle Scholar
  18. 18.
    Leal R, Yamaura M (2011) Equilibrium adsorption isotherm of U(VI) at pH 4 and pH 5 onto synthetic magnetite nanoparticles. Int J Nucl Energy Sci Technol 6:1–7CrossRefGoogle Scholar
  19. 19.
    Wei J, Zhang X, Liu Q, Li Z, Liu L, Wang J (2014) Magnetic separation of uranium by CoFe2O4 hollow spheres. Chem Eng J 241:228–234CrossRefGoogle Scholar
  20. 20.
    Tan L, Wang J, Liu Q, Sun Y, Jing X, Liu L, Liua J, Song D (2015) The synthesis of a manganese dioxide–iron oxide–graphene magnetic nanocomposite for enhanced uranium(VI) removal. New J Chem 39:868–876CrossRefGoogle Scholar
  21. 21.
    Dutta P, Ray A, Sharma V, Millero J (2004) Adsorption of arsenate and arsenite on titanium dioxide suspensions. J Colloid Interface Sci 278:270–275CrossRefGoogle Scholar
  22. 22.
    Engates KE, Shipley HJ (2011) Adsorption of Pb, Cd, Cu, Zn, and Ni to titanium dioxide nanoparticles: effect of particle size, solid concentration, and exhaustion. Environ Sci Pollut Res 18:386–395CrossRefGoogle Scholar
  23. 23.
    Laurent S, Forge D, Port M, Roch A, Robic C, Elst LV, Muller RN (2008) Magnetic iron oxide nanoparticles: synthesis, stabilization, vectorization, physicochemical characterizations, and biological applications. Chem Rev 108:2064–2100CrossRefGoogle Scholar
  24. 24.
    Spaldin N (2003) Magnetic materials: fundamentals and device applications. Cambridge University Press, CambridgeGoogle Scholar
  25. 25.
    Tan L, Liua Q, Jinga X, Liua J, Songa D, Hua S, Liub L, Wang J (2015) Removal of uranium(VI) ions from aqueous solution by magnetic cobalt ferrite/multiwalled carbon nanotubes composites. Chem Eng J 273:307–315CrossRefGoogle Scholar
  26. 26.
    Zhang X, Wang J, Li R, Dai Q, Gao R, Liu Q, Zhang M (2013) Preparation of Fe3O4@C@layered double hydroxide composite for magnetic separation of uranium. Ind Eng Chem Res 52:10152–10159CrossRefGoogle Scholar
  27. 27.
    Fan FL, Qin Z, Bai J, Rong WD, Fan FY, Tian W, Wu XL, Wang Y, Zhao L (2012) Rapid removal of uranium from aqueous solutions using magnetic Fe3O4@SiO2 composite particles. J Environ Radioact 106:40–46CrossRefGoogle Scholar
  28. 28.
    Zong P, Gou J (2014) Rapid and economical synthesis of magnetic multiwalled carbon nanotube/iron oxide composite and its application in preconcentration of U(VI). J Mol Liq 195:92–98CrossRefGoogle Scholar
  29. 29.
    Tan L, Zhang X, Liu Q, Jing X, Liu J, Song D, Hu S, Liu L, Wang J (2015) Synthesis of Fe3O4@TiO2 core–shell magnetic composites for highly efficient sorption of uranium(VI). Colloids Surf A Physicochem Eng Asp 469:279–286CrossRefGoogle Scholar
  30. 30.
    Mirzabe G, Keshtkar A (2015) Selective sorption of U(VI) from aqueous solutions using a novel aminated Fe3O4@SiO2/PVA nanofiber adsorbent prepared by electrospinning method. J Radioanal Nucl Chem 303:561–576CrossRefGoogle Scholar
  31. 31.
    Wazne M, Korfiatis GP, Meng X (2003) Carbonate effects on hexavalent uranium adsorption by iron oxyhydroxide. Environ Sci Technol 37:3619–3624CrossRefGoogle Scholar
  32. 32.
    El-sherif RM, Lasheen TA, Jebril EA (2017) Fabrication and characterization of CeO2–TiO2–Fe2O3 magnetic nanoparticles for rapid removal of uranium ions from industrial waste solutions. J Mol Liq 241:260–269CrossRefGoogle Scholar
  33. 33.
    Marczenko Z (1986) Separation and spectrophotometric determination of elements. Ellis Harwood, ChichesterGoogle Scholar
  34. 34.
    Maity D, Chandrasekharan P, Si-Shen F, Xue JM, Ding J (2010) Polyol-based synthesis of hydrophilic magnetite nanoparticles. J Appl Phys 107(09B310):1–3Google Scholar
  35. 35.
    Dyer JR (1965) Application of organic compound, 6th edn. Prentice-Hall, Englewood CliffsGoogle Scholar
  36. 36.
    Kumar S, Kumar P, Singh V, Mandal UK, Konala RK (2015) Synthesis, characterization and magnetic properties of monodisperse Ni, Zn-ferrite nanocrystals. J Magn Magn Mater 379:50–57CrossRefGoogle Scholar
  37. 37.
    Manos MJ, Kanatzidis MG (2012) Layered metal sulfides capture uranium from seawater. J Am Chem Soc 134:16441–16446CrossRefGoogle Scholar
  38. 38.
    Zhu L, Yuan L-Y, Xia L-S, Wang L (2016) Incorporation of magnetism into the dihydroimidazole functionalized mesoporous silica for convenient U(VI) capture. J Radioanal Nucl Chem 308:447–458CrossRefGoogle Scholar
  39. 39.
    Wang F, Li H, Liu Q, Li Z, Li R, Zhang H, Liu L, Emelchenko GA, Wang J (2016) A graphene oxide/amidoxime hydrogel for enhanced uranium capture. Sci Rep 6:1–8CrossRefGoogle Scholar
  40. 40.
    Khanna L, Verma NK (2014) Synthesis, characterization and biocompatibility of potassium ferrite nanoparticles. J Mater Sci Technol 30(1):30–36CrossRefGoogle Scholar
  41. 41.
    Laokul P, Amornkitbamrung V, Seraphin S, Maensiri S (2011) Characterization and magnetic properties of nanocrystalline CuFe 2O4, NiFe2O4, ZnFe2O4 powders prepared by the Aloe vera extract solution. Curr Appl Phys 11:101–108CrossRefGoogle Scholar
  42. 42.
    Sheng GD, Yang ST, Sheng J, Zhao DD, Wang XK (2011) Influence of solution chemistry on the removal of Ni(II) from aqueous solution to titanate nanotubes. Chem Eng J 168:178–182CrossRefGoogle Scholar
  43. 43.
    Moulin C, Laszak I, Moulin V, Tondre C (1998) Time-resolved laser-induced fluorescence as a unique tool for low-level uranium speciation. Appl Spectrosc 52:528–535CrossRefGoogle Scholar
  44. 44.
    Guerra DL, Viana RR, Airoldi CJ (2009) Adsorption of thorium cation on modified clays MTTZ derivative. J Hazard Mater 168:1504–1511CrossRefGoogle Scholar
  45. 45.
    Abbasi WA, Streat M (1994) Adsorption of uranium from aqueous solutions using activated carbon. Sep Sci Technol 27:1217–1230CrossRefGoogle Scholar
  46. 46.
    Yuan L-Y, Liu Y-L, Shi W-Q, Lv Y-L, Lan J-H, Zhao Y-L, Chai Z-F (2011) High performance of phosphonate-functionalized mesoporous silica for U(VI) sorption from aqueous solution. Dalton Trans 40:7446–7453CrossRefGoogle Scholar
  47. 47.
    Bonato M, Ragnarsdottir KV, Allen GC (2012) Removal of uranium(VI), lead(II) at the surface of TiO2 nanotubes studied by X-ray photoelectron spectroscopy. Water Air Soil Pollut 223:3845–3857CrossRefGoogle Scholar
  48. 48.
    Watanabe T, Ikeda Y (2013) A study on identification of uranyl complexes in aqueous solutions containing carbonate ion and hydrogen peroxide. Energy Proc 39:81–95CrossRefGoogle Scholar
  49. 49.
    Nilchi A, Dehaghan TS, Garmarodi SR (2013) Kinetics, isotherm and thermodynamics for uranium and thorium ions adsorption from aqueous solutions by crystalline tin oxide nanoparticles. Desalination 321:67–71CrossRefGoogle Scholar
  50. 50.
    Anirudhan TS, Sreekumari SS (2010) Synthesis and characterization of a functionalized graft copolymer of densified cellulose for the extraction of uranium(VI) from aqueous solutions. Colloids Surf A Physicochem Eng Asp 361:180–186CrossRefGoogle Scholar
  51. 51.
    Kamari A, Ngah WSW, Chong MY, Cheah ML (2009) Sorption of acid dyes onto GLA and H2SO4 cross-linked chitosan beads. Desalination 249:1180–1189CrossRefGoogle Scholar
  52. 52.
    Sabarudin A, Oshima M, Takayanagi T, Hakim L, Oshita K, Gao YH, Motomizu Sh (2007) Functionalization of chitosan with 3,4-dihydroxybenzoic acid for the adsorption/collection of uranium in water samples and its determination by inductively coupled plasma-mass spectrometry. Anal Chim Acta 581:214–220CrossRefGoogle Scholar
  53. 53.
    Sheng G, Li Y, Dong H, Shao D (2012) Environmental condition effects on radionuclide 64Cu(II) sequestration to a novel composite: polyaniline grafted multiwalled carbon nanotubes. J Radioanal Nucl Chem 293:797–806CrossRefGoogle Scholar
  54. 54.
    Yang S, Guo Z, Sheng G, Wang X (2012) Investigation of the sequestration mechanisms of Cd(II) and 1-naphthol on discharged multi-walled carbon nanotubes in aqueous environment. Sci Total Environ 420:214–221CrossRefGoogle Scholar
  55. 55.
    Sun Y, Yang Sh, Sheng G, Guo Z, Wang X (2012) The removal of U(VI) from aqueous solution by oxidized multiwalled carbon nanotubes. J Environ Radioact 105:40–47CrossRefGoogle Scholar
  56. 56.
    Sheng G, Dong H, Shen R, Li Y (2013) Microscopic insights into the temperature-dependent adsorption of Eu(III) onto titanate nanotubes studied by FTIR, XPS, XAFS and batch technique. Chem Eng J 217:486–494CrossRefGoogle Scholar
  57. 57.
    Bhatnagar A, Jain AK (2005) A comparative adsorption study with different industrial wastes as adsorbents for the removal of cationic dyes from water. J Colloid Interface Sci 28:49–55CrossRefGoogle Scholar
  58. 58.
    Hu X, Wang J, Liu Y, Li X, Zeng G, Bao Z, Zeng X, Chen A, Long F (2011) Adsorption of chromium (VI) by ethylenediamine-modified cross-linked magnetic chitosan resin: isotherms, kinetics and thermodynamics. J Hazard Mater 185:306–314CrossRefGoogle Scholar
  59. 59.
    Hameed BH (2009) Removal of cationic dye from aqueous solution using jackfruit peel as non-conventional low-cost adsorbent. J Hazard Mater 162:344–350CrossRefGoogle Scholar
  60. 60.
    Kilincarslan A, Akyil S (2005) Uranium adsorption characteristic and thermodynamic behavior of clinoptilolite zeolite. J Radioanal Nucl Chem 264:541–548CrossRefGoogle Scholar
  61. 61.
    Zong PF, Wang SF, Zhao YL, Wang H, Pan H, He CH (2013) Synthesis and application of magnetic graphene/iron oxides composite for the removal of U(VI) from aqueous solutions. Chem Eng J 220:45–52CrossRefGoogle Scholar
  62. 62.
    Zhao YG, Li JX, Zhao LP, Zhang SW, Huang YS, Wu XL, Wang XK (2014) Synthesis of amidoxime-functionalized Fe3O4@SiO2 core–shell magnetic microspheres for highly efficient sorption of U(VI). Chem Eng J 235:275–283CrossRefGoogle Scholar
  63. 63.
    Banerjee C, Dudwadkar N, Tripathi SC, Gandhi PM, Grover V, Kaushik CP, Tyagi AK (2014) Nano-cerium vanadate: a novel inorganic ion exchanger for removal of americium and uranium from simulated aqueous nuclear waste. J Hazard Mater 280:63–70CrossRefGoogle Scholar

Copyright information

© Springer Nature Switzerland AG 2019

Authors and Affiliations

  • El Said A. Nouh
    • 1
  • T. A. Lasheen
    • 1
  • Rabab M. El-sherif
    • 2
  • N. A. Abdel Ghany
    • 3
  • E. A. Jebril
    • 1
  1. 1.Nuclear Materials AuthorityCairoEgypt
  2. 2.Department of Chemistry, Faculty of ScienceCairo UniversityCairoEgypt
  3. 3.Material Science DepartmentNational Research CentreCairoEgypt

Personalised recommendations