A Study on the Phosphate-Bonded High-Alumina Castable — Effect of MgO Addition

  • R. Sarkar
  • U.K. Behera
Research and Development Alumina Castables
  • 6 Downloads

Abstract

Mono-aluminium phosphate [MAP, Al(H2PO4)3] is a widely used chemical binder in the refractory industries due to its higher water solubility and greater bonding strength at low temperatures as it reacts with both basic and amphoteric oxides and has higher application temperature. In the present work, commercial-grade MAP is used in high-alumina castables, with different particle size distributions, as the sole binder. The effect of addition of 1 mass-% MgO as a setting accelerator to the castable compositions is also studied. Castables are processed as per conventional processing methods and heat treated after drying at 1000 and 1600 °C. Dried and fired compositions were evaluated for density and strength. Also micro-structural study of the 1600 °C sintered samples was carried out. Addition of MgO resulted in a marginal decrease in density values which may be due to a greater amount of hydrated phase formation and their decomposition at higher temperatures; but it significantly increased crushing strength for all the heat treatment temperatures. Greater bonding from faster reaction at low temperature and the formation of a liquid phase at higher temperatures are the reasons for such an enhancement.

Keywords

phosphate bonding alumina castables MAP MgO addition properties microstructure 

Notes

Acknowledgment

The authors thankfully acknowledge the support of Mr. S. Mukherjee and Mr. S. Chatterjee for supplying different grades of alumina and the staff of the Department of Ceramic Engineering, NIT Rourkela for their support and help regarding different experimentation for the work.

References

  1. [1]
    Sarkar, R.: Refractory Technology: Fundamentals and Applications. CRC Press, Florida, US, (2016) 252–254, ISBN 9781498754255CrossRefGoogle Scholar
  2. [2]
    Krietz, L.: Refractory castables. C.A. Schacht (Ed.), Refractories Handbook, CRC Press, Florida, US, (2004) 259–285, ISBN 9780824756543CrossRefGoogle Scholar
  3. [3]
    Ishikawa, M.: Refractory castables. Taikabutsu Overseas 19 (1999) [3] 7–13Google Scholar
  4. [4]
    Zhou, N., Hu, S., Zhang, S.: Advances in modern refractory castables. CN-Refractories 13 (2004) [2] 3–12Google Scholar
  5. [5]
    Zhou, N.: New castables and their role in advancements in monolithic refractories. Interceram 55 (2006) [1] 24–26Google Scholar
  6. [6]
    Lee, W.E., Vieira, W., Zhang, S., Ghanbari Ahari, K., Sarpoolaky, H., Parr, C.: Castable refractory concretes. Int. Mater. Rev. 46 (2001) [3] 145–167CrossRefGoogle Scholar
  7. [7]
    Nouri-Khezrabad, M., Braulio, M.A.L., Pandolfelli, V.C., Golestani-Fard, F., Rezaie, H.R.: Nano-bonded refractory castables. Ceram. Int. 39 (2013) [4] 3479–3497CrossRefGoogle Scholar
  8. [8]
    Parr, C., Auvray, J.M., Pelletier, J., Szepizdyn, M., Wohrmeyer, C., Zetterstrom, C.: A review of refractory bond systems for monolithic castable refractories. In: Proc. of the 5th Ann. Symp. on Refractories, St. Louis, USA, (2014) 18–35Google Scholar
  9. [9]
    Li, Z., Ye, G.: Bonding and recent progress of monolithic refractories. Interceram 41 (1992) [3] 169–172Google Scholar
  10. [10]
    Nishikawa, A.: Technology of monolithic refractories. Plibrico Japan Company Ltd., Japan (1984) 101–114Google Scholar
  11. [11]
    Cassidy, J. E.: Phosphate bonding then and now. Ceram. Bull. 56 (1977) [7] 640–643.Google Scholar
  12. [12]
    Luz, A.P., Gomes, D.T., Pandolfelli V.C.: High-alumina phosphate-bonded refractory castables: Al(OH)3 sources and their effects. Ceram. Int. 41 (2015) 9041–9050CrossRefGoogle Scholar
  13. [13]
    Wagh, A.S.: Chemically bonded phosphate ceramics, twenty-first century materials with diverse applications. Elsevier Ltd., Oxford (2004) 43–62, ISBN 9780080445052CrossRefGoogle Scholar
  14. [14]
    Giskow, R., Lind, J., Schmidt, E.: The variety of phosphates for refractory and technical applications by the example of aluminum phosphates. Cfi/Ber. DKG 81 (2004) E1–E5Google Scholar
  15. [15]
    Gower, G.D., Gower, I.R.: Properties of magnesium-phosphate-bonded refractory castables, Refract. Appl. News 11 (2006) [5] 11–13Google Scholar
  16. [16]
    Finch, T., Sharp, J.H.: Chemical reactions between magnesia and aluminum orthophosphate to form magnesia-phosphate cements. J. Mater. Sci. 24 (1989) 4379–4386CrossRefGoogle Scholar
  17. [17]
    Dinger, D.R., Funk, J.E.: Particle Packing III: Discrete versus continuous particle sizes, Interceram, 41 (1992) [5] 332–334Google Scholar
  18. [18]
    Myhre, B., Hundere, A.: The use of particle size distribution in development of refractory castables. Proc. XXV Alafar Congress, Bariloche, Argentina, (1996) 33–42Google Scholar
  19. [19]
    Sarkar, R., Das, S.K.: Effect of distribution coefficient on gel bonded high alumina castable. IRMA J. 43 (2010) [1] 31–36Google Scholar
  20. [20]
    Sarkar, R.: Particle size distribution for refractory castables: A review. Interceram 65 (2016) [3] 82–86Google Scholar
  21. [21]
    Luz, A.P., Braulio, M.A.L., Pandolfelli, V.C.: Refractory castable engineering, installation techniques: Focusing on shotcreting. Göller Verlag, Baden-Baden, Germany (2015) Chapter 5, 257–309Google Scholar
  22. [22]
    Luz, A.P., Oliveira, G.R., Gomes, D.T., Pandolfelli, V.C.: Mono-aluminum phosphate-bonded refractory castables for petro-chemical application. Ceram. Int. 42 (2016) 8331–8337CrossRefGoogle Scholar
  23. [23]
    Singh A.K., Sarkar, R.: Effect of binders and distribution coefficient on the properties of high alumina castables. J. Austr. Ceram. Soc. 50 (2014) [2] 93–98Google Scholar
  24. [24]
    Sarkar, R., Parija, A.: Effect of alumina fines on high alumina self-flow low cement castables, Refractories World Forum 6 (2014) [1] 73–77Google Scholar
  25. [25]
    Sarkar, R., Parija, A.: Effect of alumina fines on vibratable high alumina low cement castable, Interceram 63 (2014) [3] 113–116Google Scholar

Copyright information

© Springer Fachmedien Wiesbaden GmbH, part of Springer Nature 2018

Authors and Affiliations

  1. 1.Department of Ceramic EngineeringNational Institute of TechnologyRourkela, OdishaIndia

Personalised recommendations