Effect of cooling time t8/5 on microstructure and toughness of Nb–Ti–Mo microalloyed C–Mn steel
- 18 Downloads
In order to further optimize welding process of Nb–Ti–Mo microalloyed steel, welding thermal cycles on coarse-grained heat-affected zone (CGHAZ) of welded joints were simulated using Gleeble 1500. The microstructure and low-temperature impact fracture were investigated using a scanning electron microscope and a pendulum impact machine, respectively. Moreover, the relationship between cooling time t8/5 and the microstructure of CGHAZ was discussed, and the effect of microstructure on impact toughness was also studied. As cooling time increased, martensite fraction decreased from 97.8% (3 s) to 3.0% (60 s). The fraction of martensite/austenite (M/A) constituent increased from 2.2% (3 s) to 39.0% (60 s), its shape changed from granular to strip, and the maximum length increased from 2.4 μm (3 s) to 7.0 μm (60 s). As cooling time increased, the prior austenite grain size increased from 34.0 μm (3 s) to 49.0 μm (60 s), the impact absorption energy reduced from 101.8 J (5 s) to 7.2 J (60 s), and the fracture mechanism changed from quasi-cleavage fracture to cleavage fracture. The decreased toughness of CGHAZ was due to the reduction of lath martensite-content, coarsening of original austenite grain, and increase and coarsening of M/A constituent. The heat input was controlled under 7 kJ cm−1 during actual welding for these steels.
KeywordsMicroalloyed C–Mn steel Cooling time Impact absorption energy M/A constituent Coarse-grained heat-affected zone Heat input
This work was financially supported by the National Natural Science Foundation of China (No. 51775102), Open Research Fund from the State Key Laboratory of Rolling and Automation, Northeastern University (No. 2016005) and Project Funded by China Postdoctoral Science Foundation (No. 2016M601877).
- Z.Y. Du, Welding science foundation-material welding science foundation, Machinery Industry Press, Beijing, 2012.Google Scholar
- F. Matsuda, K. Ikeuchi, H. Okada, I. Hrivnak, H.S. Park, Trans. JWRI 23 (1994) 231–238.Google Scholar
- D.L. Shu, Metal mechanical property, Mechanical Industry Press, Beijing, 1987.Google Scholar