Effect of Different Reinforcing Fillers on Properties, Interfacial Compatibility and Weatherability of Wood-plastic Composites

  • Xiaoqian Wang
  • Zhiming Yu
  • Armando G. McDonaldEmail author
Article

Abstract

Utilization of biochar in plastic based blends offers a sustainable way to renewable materials as well as value-added use of wood waste. To investigate the interfacial compatibility and weatherability properties of biochar composites, four types of Wood-Plastic Composites (WPC) were prepared by an extrusion process. The mechanical properties, water absorptions, thermal and viscoelastic properties, and rheological behavior of the composites were also evaluated. The decolorizing carbon (NA) composite melts showed the higher modulus and viscosity, indicating better melt strength. The NA composites performed the best in tensile properties (strength of 28.6 MPa and modulus of 3.4 GPa) and had strong interfacial interaction between particles and the matrix. The degree of HDPE crystallinity in the biochar and carbon composites decreased relative to Douglas-fir (DF) composites, while the thermal properties of the composites improved compared with DF composites. For the water resistance, the DF composites displayed the highest water absorption (3.7%) and thickness swell (2.9%). During accelerated weathering tests, longer exposure time increased the color change and lightness, especially for DF composite. NA and biochar composites resulted in improved photostability. This study opens up a pathway to utilize effectively the renewable biochar as reinforcing filler in WPC in outdoor applications.

Keywords

biochar interfacial compatibility accelerated weathering wood-plastic composites 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

Notes

Acknowledgement

This work was supported by China Scholarship Council (No. 201706510025). Additionally, the authors acknowledge (1) Dr. Abdulbaset Alayat for his technical help and surface area measurement, (2) Maged Mohamed for technical help with the accelerated weathering tests, and (3) Farid Sotoudehniakarani for his technical help in the extractions. We also acknowledge the M.J. Murdock Charitable Trust for their support in the purchase of the twin screw extruder and USDA-CSREES grant 2007-34158-17640 for support in the purchase of the DSC and DMA instruments.

References

  1. [1]
    Li X, Lei B, Lin Z, Huang L, Tan S, Cai X. The utilization of bamboo charcoal enhances wood plastic composites with excellent mechanical and thermal properties. Materials Design, 2014, 53, 419–424.CrossRefGoogle Scholar
  2. [2]
    Peng Y, Wang W, Cao J. Preparation of lignin-clay complexes and its effects on properties and weatherability of wood flour/polypropylene composites. Industrial & Engineering Chemistry Research, 2016, 55, 9657–9666.CrossRefGoogle Scholar
  3. [3]
    Pickering K L, Aruan Efendy M G, Le T M. A review of recent developments in natural fiber composites and their mechanical performance. Composites Part A: Applied Science and Manufacturing, 2016, 83, 98–112.CrossRefGoogle Scholar
  4. [4]
    Liu R, Peng Y, Cao J. Thermal stability of organo-montmorillonite-modified wood flour/poly(lactic acid) composites. Polymer Composites, 2016, 37, 1971–1977.CrossRefGoogle Scholar
  5. [5]
    Arao Y, Nakamura S, Tomita Y, Takakuwa K, Umemura T, Tanaka T. Improvement on fire retardancy of wood flour/polypropylene composites using various fire retardants. Polymer Degradation and Stability, 2014, 100, 79–85.CrossRefGoogle Scholar
  6. [6]
    Li X, Lei B, Lin Z, Huang L, Tan S, Cai X. The utilization of organic vermiculite to reinforce wood-plastic composites with higher flexural and tensile properties. Industrial Crops and Products, 2013, 51, 310–316.CrossRefGoogle Scholar
  7. [7]
    Wei L, McDonald A G, Freitag C, Morrell J J. Effects of wood fiber esterification on properties, weatherability and biodurability of wood plastic composites. Polymer Degradation and Stability, 2013, 98, 1348–1361.CrossRefGoogle Scholar
  8. [8]
    Deka B K, Maji T K. Effect of silica nanopowder on the properties of wood flour/polymer composite. Polymer Engineering and Science, 2012, 52, 1516–1523.CrossRefGoogle Scholar
  9. [9]
    Devi R R, Maji T K. Preparation and characterization of wood/styrene-acrylonitrile copolymer/MMT nanocomposite. Journal of Applied Polymer Science, 2011, 122, 2099–2109.CrossRefGoogle Scholar
  10. [10]
    Mwaikambo L Y, Ansell M P. The effect of chemical treatment on the properties of hemp, sisal, jute and kapok for composite reinforcement. Die Angewandte Makromolekulare Chemie, 1999, 272, 108–116.CrossRefGoogle Scholar
  11. [11]
    Lee S H, Wang S. Biodegradable polymers/bamboo fiber biocomposite with bio-based coupling agent. Composites Part A: Applied Science and Manufacturing, 2006, 37, 80–91.CrossRefGoogle Scholar
  12. [12]
    Das O, Kim N K, Sarmah A K, Bhattacharyya D. Development of waste based biochar/wool hybrid biocomposites: Flammability characteristics and mechanical properties. Journal of Cleaner Production, 2017, 144, 79–89.CrossRefGoogle Scholar
  13. [13]
    Srinivasan P, Sarmah A K, Smernik R, Das O, Farid M, Gao W. A feasibility study of agricultural and sewage biomass as biochar, bioenergy and biocomposite feedstock: Production, characterization and potential applications. Science of the Total Environment, 2015, 512-513, 495–505.CrossRefGoogle Scholar
  14. [14]
    Kookana R S, Sarmah A K, Van Zwieten L, Krull E, Singh B. Biochar application to soil: Agronomic and environmental benefits and unintended consequences. Advances in Agronomy, 2011, 112, 103–143.CrossRefGoogle Scholar
  15. [15]
    Arni S A. Comparison of slow and fast pyrolysis for converting biomass into fuel. Renewable Energy, 2018, 124, 197–201.CrossRefGoogle Scholar
  16. [16]
    Mohanty P, Nanda S, Pant K K, Naik S, Kozinski J A, Dalai A K. Evaluation of the physiochemical development of biochars obtained from pyrolysis of wheat straw, timothy grass and pinewood: Effects of heating rate. Journal of Analytical and Applied Pyrolysis, 2013, 104, 485–493.CrossRefGoogle Scholar
  17. [17]
    Spiridon I. Natural fiber-polyolefin composites. Cellulose Chemistry and Technology, 2014, 48, 599–612.Google Scholar
  18. [18]
    Belda R M, Lidón A, Fornes F. Biochars and hydrochars as substrate constituents for soilless growth of myrtle and mastic. Industrial Crops and Products, 2016, 94, 132–142.CrossRefGoogle Scholar
  19. [19]
    Oliveira F R, Patel A K, Jaisi D P, Adhikari S, Lu H, Khanal S K. Environmental application of biochar: Current status and perspectives. Bioresource Technology, 2017, 246, 110–122.CrossRefGoogle Scholar
  20. [20]
    Vaughn S F, Kenar J A, Tisserat B, Jackson M A, Joshee N, Vaidya B N, Peterson S C. Chemical and physical properties of Paulownia elongata biochar modified with oxidants for horticultural applications. Industrial Crops and Products, 2017, 97, 260–267.CrossRefGoogle Scholar
  21. [21]
    Margenot A J, Griffin D E, Alves B S Q, Rippner D A, Li C, Parikh S J. Substitution of peat moss with softwood biochar for soil-free marigold growth. Industrial Crops and Products, 2018, 112, 160–169.CrossRefGoogle Scholar
  22. [22]
    Zhang Q, Cai H, Yang K, Yi W. Effect of biochar on mechanical and flame retardant properties of wood - Plastic composites. Results in Physics, 2017, 7, 2391–2395.CrossRefGoogle Scholar
  23. [23]
    Das O, Bhattacharyya D, Hui D, Lau K T. Mechanical and flammability characterisations of biochar/polypropylene biocomposites. Composites Part B: Engineering, 2016, 106, 120–128.CrossRefGoogle Scholar
  24. [24]
    DeVallance D B, Oporto G S, Quigley P. Investigation of hardwood biochar as a replacement for wood flour in wood-polypropylene composites. Journal of Elastomers and Plastics, 2016, 48, 510–522.CrossRefGoogle Scholar
  25. [25]
    Ho M, Lau K, Wang H, Hui D. Improvement on the properties of polylactic acid (PLA) using bamboo charcoal particles. Composites Part B: Engineering, 2015, 81, 14–25.CrossRefGoogle Scholar
  26. [26]
    Ahmetli G, Kocaman S, Ozaytekin I, Bozkurt P. Epoxy composites based on inexpensive char filler obtained from plastic waste and natural resources. Polymer Composites, 2013, 34, 500–509.CrossRefGoogle Scholar
  27. [27]
    Adefisan O O, McDonald A G. Evaluation of wood plastic composition product from mahogany and teak. International Journal of Advanced Engineering Research and Science (IJAERS), 2017, 4, 27–32.CrossRefGoogle Scholar
  28. [28]
    Quirk J T. Cell-wall density of Douglas-fir by two optometric methods. Wood Fiber Science, 1984, 16, 224–236.Google Scholar
  29. [29]
    Brewer C E, Chuang V J, Masiello C A, Gonnermann H, Gao X, Dugan B, Driver L E, Panzacchi P, Zygourakis K, Davies C A. New approaches to measuring biochar density and porosity. Biomass & Bioenergy, 2014, 66, 176–185.CrossRefGoogle Scholar
  30. [30]
    Fabiyi J S, McDonald A G. Effect of wood species on property and weathering performance of wood plastic composites. Composites Part A: Applied Science and Manufacturing, 2010, 41, 1434–1440.CrossRefGoogle Scholar
  31. [31]
    Stark N M, Matuana L M. Surface chemistry changes of weathered HDPE/wood-flour composites studied by XPS and FTIR spectroscopy. Polymer Degradation and Stability, 2004, 86, 1–9.CrossRefGoogle Scholar
  32. [32]
    Nunes C A, Guerreiro M C. Estimation of surface area and pore volume of activated carbons by methylene blue and iodine numbers. Quimica Nova, 2011, 34, 472–476.CrossRefGoogle Scholar
  33. [33]
    Clemons C M, Stark N M. Feasibility of using saltcedar as a filler in injection-molded polyethylene composites. Wood Fiber Science, 2009, 41, 2–12.Google Scholar
  34. [34]
    Gallagher L W, McDonald A G. The effect of micro sized wood fibers in wood plastic composites. Maderas-Ciencia Y Tecnologia, 2013, 15, 357–374.Google Scholar
  35. [35]
    Hristov V, Takács E, Vlachopoulos J. Viscoelastic behavior of highly filled HDPE/wood flour composites. ANTEC, 2005, 1331–1335.Google Scholar
  36. [36]
    Luo S, Cao J, McDonald A G. Interfacial improvements in a green biopolymer alloy of poly(3-hydroxybutyrateco-3-hydroxyvalerate) and lignin via in situ reactive extrusion. ACS Sustainable Chemistry & Engineering, 2016, 4, 3465–3476.CrossRefGoogle Scholar
  37. [37]
    Marcovich N E, Reboredo M M, Kenny J M, Aranguren M. Rheology of particle suspensions in viscoelastic media. Wood flour-polypropylene melt. Rheologica Acta, 2004, 43, 293–303.CrossRefGoogle Scholar
  38. [38]
    Hristov V, Takacs E, Vlachopoulos J. Surface tearing and wall slip phenomena in extrusion of highly filled HDPE/wood flour composites. Polymer Engineering and Science, 2006, 46, 1204–1214.CrossRefGoogle Scholar
  39. [39]
    Ou R, Xie Y, Wolcott M P, Yuan F, Wang Q. Effect of wood cell wall composition on the rheological properties of wood particle/high density polyethylene composites. Composites Science and Technology, 2014, 93, 68–75.CrossRefGoogle Scholar
  40. [40]
    Belaïd S, Boiteux G, Cassagnau P. Rheological and electrical properties of EVA copolymer filled with bamboo charcoal. Rheologica Acta, 2013, 52, 75–84.CrossRefGoogle Scholar
  41. [41]
    Stark N M, Rowlands R E. Effects of wood fiber characteristics on mechanical properties of wood/polypropylene composites. Wood and Fiber Science, 2003, 35, 167–174.Google Scholar
  42. [42]
    Ikram S, Das O, Bhattacharyya D. A parametric study of mechanical and flammability properties of biochar reinforced polypropylene composites. Composites Part A: Applied Science and Manufacturing, 2016, 91, 177–188.CrossRefGoogle Scholar
  43. [43]
    Das O, Sarmah A K, Bhattacharyya D. A novel approach in organic waste utilization through biochar addition in wood/polypropylene composites. Waste Management, 2015, 38, 132–140.CrossRefGoogle Scholar
  44. [44]
    Zhang Q, Yi W, Li Z, Wang L, Cai H. Mechanical properties of rice husk biochar reinforced high density polyethylene composite. Polymers, 2018, 10, 286–295.CrossRefGoogle Scholar
  45. [45]
    Ren W, Zhang D, Wang G, Cheng H. Mechanical and thermal properties of bamboo pulp fiber reinforced polyethylene composites. Bioresources, 2014, 9, 4117–4127.Google Scholar
  46. [46]
    Wang C, Yu X, Smith L M, Wang G, Cheng H, Zhang S. Interfacial properties of bamboo fiber-reinforced high-density polyethylene composites by different methods for adding nano calcium carbonate. Polymers, 2017, 9, 587–600.CrossRefGoogle Scholar
  47. [47]
    Tian S, He H, Yu P, Zhou L, Luo Y, Jia D. Sustainable utilization of waste printed circuit boards powders in HDPE-wood composites: Synergistic effects of multicomponents on structure and properties. Journal of Cleaner Production, 2017, 164, 840–847.CrossRefGoogle Scholar
  48. [48]
    Kubat J, Rigdahl M, Welander M. Characterization of interfacial interactions in high density polyethylene filled with glass spheres using dynamic-mechanical analysis. Journal of Applied Polymer Science, 1990, 39, 1527–1539.CrossRefGoogle Scholar
  49. [49]
    Luo S, Cao J, McDonald A G. Esterfication of industrial lignin and its effect on the resulting poly(3-hydroxybutyrateco-3-hrdroxyvalerate) or polypropylene blends. Industrial Crops and Products, 2017, 97, 281–291.CrossRefGoogle Scholar
  50. [50]
    Debenedetti P G, Stillinger F H. Supercooled liquids and the glass transition. Nature, 2001, 410, 259–267.CrossRefGoogle Scholar
  51. [51]
    Xu X, Liu F, Jiang L, Zhu J Y, Haagenson D, Wiesenborn D P. Cellulose nanocrystals vs. cellulose nanofibrils: A comparative study on their microstructures and effects as polymer reinforcing agents. ACS Applied Materials & Interfaces, 2013, 5, 2999–3009.CrossRefGoogle Scholar
  52. [52]
    Yu H Y, Qin Z Y, Yan C F, Yao J M. Green nanocomposites based on functionalized cellulose nanocrystals: A study on the relationship between interfacial interaction and property enhancement. ACS Sustainable Chemistry & Engineering, 2014, 2, 875–886.CrossRefGoogle Scholar
  53. [53]
    Lu H, Nutt S. Restricted relaxation in polymer nanocomposites near the glass transition. Macromolecules, 2003, 36, 4010–4016.CrossRefGoogle Scholar
  54. [54]
    Sun F, Huang H. Rheology and thermal properties of polypropylene modified by reactive extrusion with dicumyl peroxide and trimethylol propane triacrylate. Advances in Polymer Technology, 2009, 28, 16–25.CrossRefGoogle Scholar
  55. [55]
    Cui Y H, Tao J, Noruziaan B, Cheung M, Lee S. DSC analysis and mechanical properties of wood-plastic composites. Journal of Reinforced Plastics and Composites, 2010, 29, 278–289.CrossRefGoogle Scholar
  56. [56]
    Das O, Sarmah A K, Zujovic Z, Bhattacharyya D. Characterisation of waste derived biochar added biocomposites: Chemical and thermal modifications. Science of The Total Environment, 2016, 550, 133–142.CrossRefGoogle Scholar
  57. [57]
    Ndiaye D, Dipo B, Thiandoume C, Fall P A, Farota A K, Tidjani A. Morphology and thermo mechanical properties of wood/polypropylene composites. In: Dogan F (ed.), Polypropylene, InTech Open Access, London, UK, 2012, 415–428. DOI:  https://doi.org/10.5772/36148 Google Scholar
  58. [58]
    Ouajai S, Shanks R A. Composition, structure and thermal degradation of hemp cellulose after chemical treatments. Polymer Degradation and Stability, 2005, 89, 327–335.CrossRefGoogle Scholar
  59. [59]
    Essabir H, Hilali E, Elgharad A, Minor H E, Imad A, Elamraoui A, Gaoudi O Al. Mechanical and thermal properties of bio-composites based on polypropylene reinforced with nut-shells of argan particles. Materials & Design, 2013, 49, 442–448.CrossRefGoogle Scholar
  60. [60]
    Ahmad E E M, Luyt A S. Effects of organic peroxide and polymer chain structure on morphology and thermal properties of sisal fiber reinforced polyethylene composites. Composites Part A: Applied Science and Manufacturing, 2012, 43, 703–710.CrossRefGoogle Scholar
  61. [61]
    Zhang Y, Ma Z, Zhang Q, Wang J, Ma Q, Yang Y, Luo X, Zhang W. Comparison of the physicochemical characteristics of bio-char pyrolyzed from Moso bamboo and rice husk with different temperatures. Bioresources, 2017, 12, 4652–4669.Google Scholar
  62. [62]
    Meng X, Zhang Y, Lu J, Zhang Z, Liu L, Chu P K. Effects of bamboo charcoal power on the curing characteristics, mechanical properties, and thermal properties of styrene-butadiene rubber with bamboo charcoal power. Journal of Applied Polymer Science, 2013, 130, 4534–4541.CrossRefGoogle Scholar
  63. [63]
    Abdul Khalil H P S, Firoozian P, Bakare I O, Akil H M, Noor A M. Exploring biomass based carbon black as filler in epoxy composites: Flexural and thermal properties. Materials & Design, 2010, 31, 3419–3425.CrossRefGoogle Scholar
  64. [64]
    Li S, Li X, Chen C, Wang H, Deng Q, Gong M, Li D. Development of electrically conductive nano bamboo charcoal/ultra-high molecular weight polyethylene composites with a segregated network. Composites Science and Technology, 2016, 132, 31–37.CrossRefGoogle Scholar
  65. [65]
    Fabiyi J S, McDonld A G, Morrell J J, Freitag C. Effects of wood species on durability and chemical changes of fungal decayed wood plastic composites. Composites Part A: Applied Science and Manufacturing, 2011, 42, 501–510.CrossRefGoogle Scholar
  66. [66]
    Javadi Y, Hosseini M S, Aghjeh M K R. The effect of carbon black and HALS hybrid systems on the UV stability of high-density polyethylene (HDPE). Iranian Polymer Journal, 2014, 23, 793–799.CrossRefGoogle Scholar
  67. [67]
    Liu M, Horrocks A R. Effect of carbon black on UV stability of LLDPE films under artificial weathering conditions. Polymer Degradation and Stability, 2002, 75, 485–499.CrossRefGoogle Scholar
  68. [68]
    Faix O. Fourier transform infrared spectroscopy. in: Lin S Y, Dence C W, eds. Methods in Lignin Chemistry. Springer, Berlin, Germany, 1992, 83–109.CrossRefGoogle Scholar
  69. [69]
    Miller F A. Characteristic frequencies of alkenes (olefins). In: Mayo D W, Miller F A, Hannah R W, eds. Course Notes on the Interpretation of Infrared and Raman Spectra. John Wiley & Sons, New York, USA, 2003, 73–84.Google Scholar
  70. [70]
    Fabiyi J S, McDonald A G, Wolcott M P, Griffiths P R. Wood plastic composites weathering visual appearance and chemical changes. Polymer Degradation and Stability, 2008, 93, 1405–1414.CrossRefGoogle Scholar
  71. [71]
    Lacoste J, Carlsson D J, Falicki S, Wiles D M. Polyethylene hydroperoxide decomposition products. Polymer Degradation and Stability, 1991, 34, 309–323.CrossRefGoogle Scholar
  72. [72]
    Mayo D W. Spectra of carbonyl compounds of all kinds (factors affecting carbonyl group frequencies). In: Mayo D W, Miller F A, Hannah R W, eds. Course Notes on the Interpretation of Infrared and Raman Spectra, John Wiley & Sons, New York, USA, 2003, 179–204.Google Scholar
  73. [73]
    Stark N M, Matuana L M, Clemons C M. Effect of processing method on surface and weathering characteristics of wood-flour/HDPE composites. Journal of Applied Polymer Science, 2004, 93, 1021–1030.CrossRefGoogle Scholar
  74. [74]
    Evans P D, Owen N L, Schmid S, Webster R D. Weathering and photostability of benzoylated wood. Polymer Degradation and Stability, 2002, 76, 291–303.CrossRefGoogle Scholar
  75. [75]
    Peña J M, Allen N S, Edge M, Liauw C M, Valange B. Studies of synergism between carbon black and stabilisers in LDPE photodegradation. Polymer Degradation and Stability, 2001, 72, 259–270.CrossRefGoogle Scholar

Copyright information

© Jilin University 2019

Authors and Affiliations

  • Xiaoqian Wang
    • 1
    • 2
  • Zhiming Yu
    • 1
  • Armando G. McDonald
    • 1
    • 2
    Email author
  1. 1.MOE Key Laboratory of Wooden Material Science and ApplicationBeijing Forestry UniversityBeijingChina
  2. 2.Renewable Materials Program, Department of Forest, Rangeland, and Fire SciencesUniversity of IdahoMoscow, IdahoUSA

Personalised recommendations