Material design and characterization of pervious concrete reactive barrier containing nano-silica and fine pumice aggregate

  • Abolghasem Alighardashi
  • Mohammad Javad Mehrani
  • Niloufar Fakhravar
  • Amir Mohammad Ramezanianpour
Original Paper
  • 12 Downloads

Abstract

In this study, the physical and mechanical properties of pervious concrete (PC) containing nano-silica (NS) was carried out. Mix design based on the Taguchi method in three levels and four factors (water to cement ratio, aggregate to cement ratio, the percentage of nano-silica, and percentage of fine aggregate (FA)) were examined. Concrete properties such as compressive strength, density (D), permeability (P), and porosity were evaluated. Among nine mix designs, the optimum one according to Taguchi optimization results was found from experimental results: (W/C) = 0.26, (A/C) = 5, 6% (NS) and 20% (FA). The corresponding mechanical and physical properties had a compressive strength of 3.6 (MPa), permeability of 1.06 (cm/s), void ratio of 19.7 (%), and density of 879 (kg/m3). Adding NS (up to 6% of cement weight) and FA (up to 20% of aggregates weight) had an important effect on almost all tests especially on CS, and there was no impressive influence related to another factor (W/C, A/C) in all tests. It is noticeable that the influence of adding NS to the mix design on CS was higher than adding FA.

Keywords

Pervious concrete Mix design Taguchi method Nano-silica 

Notation

PC

Pervious concrete

NS

Nano-silica

FA

Fine aggregate

D

Density

P

Permeability

V

Void content

CS

Compressive strength

Notes

Acknowledgements

The authors are thankful to the Shahid Beheshti University for providing a grant.

Compliance with ethical standards

Conflict of interest

On behalf of all authors, the corresponding author states that there is no conflict of interest.

References

  1. ACI 522-R (2013) The American Concrete Institute (Report on pervious concrete). Farmington Hills.Google Scholar
  2. Alighardashi, A., Mehrani, M.J., Ramezanianpour, A.M. (2018). Pervious concrete containing nano silica for nitrate removal from contaminated water. Environmental Science and Pollution Research, 2018.  https://doi.org/10.1007/s11356-018-3008-9.CrossRefGoogle Scholar
  3. ASTM C1754. (2012). Standard test method for density and void content of hardened pervious concrete. West Conshohocken: ASTM International.Google Scholar
  4. ASTM C39. (2017). Standard test method for compressive strength of cylindrical concrete specimens. West Conshohocken: ASTM International.Google Scholar
  5. Ayan, E., Saatçioğlu, Ö., & Turanli, L. (2011). Parameter optimization on compressive strength of steel fiber reinforced high strength concrete. Construction and Building Materials, 25, 2837–2844.CrossRefGoogle Scholar
  6. Bortone, I. (2012). Groundwater protection by pervious adsorption barrier at solid waste landfills. Rome: Nova Science Publishers.Google Scholar
  7. Elizalde-González, M. P., García-Díaz, E., González-Perea, M., & Mattusch, J. (2017). Removal of gadolinium-based contrast agents: adsorption on activated carbon. Environmental Science and Pollution Research, 24, 8164–8175.CrossRefGoogle Scholar
  8. Hashemi, S. H. (2013). Optimal reduction of the concrete mixture design containing nano-silica and micro-silica using Taguchi method. Journal of Concrete Research, 5, 45–53.Google Scholar
  9. Holmes, R. R., Hart, M. L., & Kevern, J. T. (2017). Enhancing the ability of pervious concrete to remove heavy metals from stormwater. Journal of Sustainable Water in the Built Environment, 3, 04017004.CrossRefGoogle Scholar
  10. Jo, B. W., Kim, C. H., & Lim, J. H. (2007). Investigations on the development of powder concrete with nano-SiO2 particles. KSCE Journal of Civil Engineering, 11, 37–42.CrossRefGoogle Scholar
  11. Jo, M., Soto, L., Arocho, M., John, J., & Hwang, S. (2015). Optimum mix design of fly ash geopolymer paste and its use in pervious concrete for removal of fecal coliforms and phosphorus in water. Construction and Building Materials, 93, 1097–1104.CrossRefGoogle Scholar
  12. Joshaghani, A., Ramezanianpour, A. A., Ataei, O., & Golroo, A. (2015). Optimizing pervious concrete pavement mixture design by using the Taguchi method. Construction and Building Materials, 101, 317–325.CrossRefGoogle Scholar
  13. Kong, D., Du, X., Wei, S., Zhang, H., Yang, Y., & Shah, S. P. (2012). Influence of nano-silica agglomeration on microstructure and properties of the hardened cement-based materials. Construction and Building Materials, 37, 707–715.CrossRefGoogle Scholar
  14. Liu, Y., Zhang, Y., Wang, W., & Li, Z. (2015). Mechanical properties of thermal insulation concrete with a high volume of glazed hollow beads. Magazine of Concrete Research, 67, 693–706.CrossRefGoogle Scholar
  15. Mehrani M. J., Alighardashi A., & Ramezanianpour A. M. (2017). An experimental study on the nitrate removal ability of aggregates used in pervious concrete. Desalination and Water Treatment, 86, 124–130.CrossRefGoogle Scholar
  16. Mnif, I., Sahnoun, R., Ellouze-Chaabouni, S., & Ghribi, D. (2014). Evaluation of B. subtilis SPB1 biosurfactants’ potency for diesel-contaminated soil washing: optimization of oil desorption using Taguchi design. Environmental Science and Pollution Research, 21, 851–861.CrossRefGoogle Scholar
  17. Olivia, M., & Nikraz, H. (2012). Properties of fly ash geopolymer concrete designed by Taguchi method. Materials and Design, 1980–2015(36), 191–198.CrossRefGoogle Scholar
  18. Öztürk, N., & Bektaş, T. E. (2004). Nitrate removal from aqueous solution by adsorption onto various materials. Journal of Hazardous Materials, 1, 155–162.CrossRefGoogle Scholar
  19. Rodríguez-Robles, D., Morán-del Pozo, J. M., Garciá-González, J., Guerra-Romero, M. I., & Juan-Valdeś, A. (2015). Effect of mixed recycled aggregates on mechanical properties of recycled concrete. Magazine of Concrete Research, 67, 247–256.CrossRefGoogle Scholar
  20. Roy, R. (2010). A primer on the Taguchi method, Society of Manufacturing Engineers, 2nd edition, USA.Google Scholar
  21. Sadrmomtazi, A., Kohani Khoshkbijari, R., Tahmouresi, B. (2017) Effect of fly ash and silica fume on transition zone, pore structure and permeability of concrete. Magazine of Concrete Research. http://dx.doi.org/10.1680/jmacr.16.00537.
  22. Sanchez, F., & Sobolev, K. (2010). Nanotechnology in concrete—a review. Construction and Building Materials, 24, 2060–2071.CrossRefGoogle Scholar
  23. Shabalala, A. N., Ekolu, S. O., Diop, S., & Solomon, F. (2017). Pervious concrete reactive barrier for removal of heavy metals from acid mine drainage—column study. Journal of Hazardous Materials, 323(Part B), 641–653.CrossRefGoogle Scholar
  24. Singh, L. P., Karade, S. R., Bhattacharyya, S. K., Yousuf, M. M., & Ahalawat, S. (2013). Beneficial role of nano-silica in cement-based materials—a review. Construction and Building Materials, 47, 1069–1077.CrossRefGoogle Scholar
  25. Us, E. P. A. (2002). Field applications of in situ remediation technologies: pervious reactive barriers, office of solid waste and emergency response. Washington: U.S. Environmental Protection Agency.Google Scholar
  26. Vázquez-Rivera, N. I., Soto-Pérez, L., St John, J. N., Molina-Bas, O. I., & Hwang, S. S. (2015). Optimization of pervious concrete containing fly ash and iron oxide nanoparticles and its application for phosphorus removal. Construction and Building Materials, 93, 22–28.CrossRefGoogle Scholar
  27. Wei, M., Yuan, F., Huang, G., Chen, H., & Liu, F. (2016). Long-term effect of nitrate on Cr(VI) removal by Fe0: column studies. Environmental Science and Pollution Research, 23, 8589–8597.CrossRefGoogle Scholar
  28. Zaetang, Y., Wongsa, A., Sata, V., & Chindaprasirt, P. (2013). Use of lightweight aggregates in pervious concrete. Construction and Building Materials, 48, 585–591.  https://doi.org/10.1016/j.conbuildmat.2013.07.077.CrossRefGoogle Scholar
  29. Zahedi, M., Ramezanianpour, A. A., & Ramezanianpour, A. M. (2015). Evaluation of the mechanical properties and durability of cement mortars containing nano-silica and rice husk ash under chloride ion penetration. Construction and Building Materials, 78, 354–361.CrossRefGoogle Scholar
  30. Zhang, M. H., & Islam, J. (2012). Use of nano-silica to reduce the setting time and increase early strength of concretes with high volumes of fly ash or slag. Construction and Building Materials, 29, 573–580.CrossRefGoogle Scholar

Copyright information

© Springer Nature Switzerland AG 2018

Authors and Affiliations

  1. 1.Department of Civil, Water and Environmental EngineeringShahid Beheshti UniversityTehranIran
  2. 2.Department of Civil EngineeringBauhaus Universität WeimarWiemarGermany
  3. 3.Faculty of Civil Engineering, College of EngineeringUniversity of TehranTehranIran

Personalised recommendations