Ignition-proof performance and mechanism of AZ91D-3Nd-xDy magnesium alloys at high temperatures

  • Yong-yan Li
  • Wei-min Zhao
  • Jian Ding
  • Hai-tao Xue
Research & Development
  • 16 Downloads

Abstract

This study focused on the synergistic effect of alloying elements neodymium (Nd) and dysprosium (Dy) on the ignition-proof performance of AZ91D alloy. The ignition-proof mechanism of AZ91D-3Nd-xDy (x = 0.5, 1.0, 1.5, 2.0 and 2.5wt.%) alloy was discussed in depth through ignition-proof testing and microstructure observation. The results showed that the AZ91 D-3Nd-2Dy alloy exhibited the highest ignition-point of 893 K, increased by 69 K as compared to the AZ91D alloy. The ignition-proof mechanism of Nd and Dy additions lay in three aspects: (1) the formation of denser oxide film consisting of Dy2o3 and MgO improves the oxidation resistance of the alloy, (2) the great reduction of the low melting-point phase β-Mg17Al12, which leads to the decrease in the oxygen diffusion channels, and (3) the newly formed high melting-point phases (Al2Nd and Al2Dy), which block the oxygen diffusion channels and prevent the chemical reaction of Mg and oxygen.

Keywords

AZ91D Nd Dy ignition-proof high temperature 

Document Code

References

  1. [1]
    Gwynne B A. Magnesium alloys in aerospace applicationsflammability testing. TMS 2010 139th Annual Meeting & Exhibition. Washington, USA 2010.Google Scholar
  2. [2]
    Jeon J, Lee S, Kim B, et al. Effect of Sb and Sr addition on corrosion properties of Mg-5AI-2Si alloy. J. Korean Inst. Met. Mater, 2008,46 (5): 304–309.Google Scholar
  3. [3]
    Zhou Na, Zhang Zhenyan, Dong Jie, et al. Selective oxidation behavior of an ignition-proof Mg-Y-Ca-Ce alloy. J. Rare Earths, 2013, 31 (10): 1003–1008.CrossRefGoogle Scholar
  4. [4]
    Shih Tengshih, Liu Jyunbo, Wei Paisheng. Oxide films on magnesium and magnesium alloys. Mater. Chem. Phys, 2007, 104 (2-3): 497–504.CrossRefGoogle Scholar
  5. [5]
    Zeng Xiaoqin, Wang Qudong, Lü Yizhen, et al. Study on ignition proof magnesium alloy with beryllium and rare earth additions. Scr. Mater, 2000,43 (5): 403–409.CrossRefGoogle Scholar
  6. [6]
    Fan J F, Yang Ch L, Han G, et al. Oxidation behavior of ignitionproof magnesium alloys with rare earth addition. J. Alloy. Compd, 2011,509 (5): 2137–2142.CrossRefGoogle Scholar
  7. [7]
    Kim Y M, Yim C D, Kim H S, et al. Key factor influencing the ignition resistance of magnesium alloys at elevated temperatures. Scripta Mater., 2011,65 (11): 958–961.CrossRefGoogle Scholar
  8. [8]
    Ha S H, Lee J K, Jo H H, et al. Behavior of CaO and Calcium in pure Magnesium. Rare Met., 2006,25 (Z2): 150–154.CrossRefGoogle Scholar
  9. [9]
    Lin Pengyu, Zhou Hong, Li Wei, et al. Interactive effect of cerium and aluminum on the ignition point and the oxidation resistance of magnesium alloy. Corros Sci., 2008,50 (9): 2669–2675.CrossRefGoogle Scholar
  10. [10]
    Zhang Guoying, Luo Zhicheng, Zhang Hui, et al. Igniton-proof mechanism of magnesium ally added with rare earth La from first-principle study. J. Rare Earths, 2012,30 (6): 573–578.CrossRefGoogle Scholar
  11. [11]
    Fan Jianfeng, Chen Zhiyuan, Yang Weidong, et al. Effect of yttrium, calcium and zirconium on ignition-proof principle and mechanical properties of magnesium alloys. J. Rare Earths, 2012,30(1): 74–78.CrossRefGoogle Scholar
  12. [12]
    Zhao Hongjin, Zhang Yinghui, Kang Yonglin. Effect of cerium on ignition point of AZ91D magnesium ally. China Foundry, 2008, 5 (1): 32–35.Google Scholar
  13. [13]
    Wang Xuemin, Zeng Xiaoqin, Wu Guosong, et al. The effect of alloy elements on the oxidation of Magnesium alloys. Materials Review, 2006,20 (11): 69–72.Google Scholar
  14. [14]
    Wang Jun, Wang Limin, An Jian, etal. Microstructure and Elevated Temperature Properties of Die-cast AZ91-xNd Magnesium Alloys. J. Mater. Eng. Perform, 2008,17 (5): 725–729.CrossRefGoogle Scholar
  15. [15]
    Jin Liling, Y B Kang, Chartrand P, et al. Thermodynamic evaluation and optimization of Al-Gd, Al-Tb, Al-Dy, Al-Ho and Al-Er systems using a Modified Auasichemical Model for the liquid. Calphad, 2010,34 (4): 456–466.CrossRefGoogle Scholar
  16. [16]
    Pilling N B, Bed worth R E. The oxidation of metals at high temperatures. J. Inst. Met., 1923,29:529–582.Google Scholar

Copyright information

© Foundry Journal Agency and Springer Nature Singapore Pte Ltd. 2018

Authors and Affiliations

  • Yong-yan Li
    • 1
  • Wei-min Zhao
    • 1
  • Jian Ding
    • 1
  • Hai-tao Xue
    • 1
  1. 1.School of Materials Science & EngineeringHebei University of TechnologyTianjinChina

Personalised recommendations