  • Habtom Mebrahtu
  • Hassan Shirvani
Full Research Article
  • 10 Downloads

Abstract

This paper deals with the production and experimental investigation of very thin aluminium 1050 grade foil products. Single lap joints and samples for flexural testing were made using composite metal foil manufacturing (CMFM) using a special brazing paste. The effect of test speeds, material thickness and lap lengths on aluminium 1050 single lap joints was analysed. The test results showed that all the samples failed within the parent metal and the bond created during the process remained intact. Two distinct modes of failure were observed for the single lap joints. Microstructural analysis was carried out to analyse the efficacy of the paste in terms of creating a strong bond between the metal foils. Comparative three-point flexural testing was conducted using a part made by conventional machining method and another made by CMFM. The results showed that the part made by CMFM has 7.7% higher load values compared to the part made by the machining method. Both the samples exhibit similar elastic and plastic regions but CMFM part also shows higher strength. The results validate the effectiveness of CMFM and demonstrate its capabilities in terms of repeatability, reproducibility and strength.

Keywords

Brazing Lap-shear test Three-point flexural test Microstructure Metal foils 

Notes

Acknowledgements

The authors would like to thank their affiliation institution for the resources.

Compliance with ethical standards

Conflict of interest

On behalf of all authors, the corresponding author states that there is no conflict of interest.

References

  1. 1.
    Bartolai J, Simpson TW, Xie R (2018) Predicting strength of additively manufactured thermoplastic polymer parts produced using material extrusion. Rapid Prototyp J 24(2):321–332CrossRefGoogle Scholar
  2. 2.
    Atzeni E, Salmi A (2012) Economics of additive manufacturing for end-usable metal parts. Int J Adv Manuf Technol 62(9–12):1147–1155CrossRefGoogle Scholar
  3. 3.
    Chevalier J, Gremillard L (2009) Ceramics for medical applications: a picture for the next 20 years. J Eur Ceram Soc 29(7):1245–1255CrossRefGoogle Scholar
  4. 4.
    Tian L, Anderson I, Riedemann T, Russell A (2014) Modeling the electrical resistivity of deformation processed metal–metal composites. Acta Mater 77:151–161CrossRefGoogle Scholar
  5. 5.
    Butt J, Shirvani H (2018) Experimental analysis of metal/plastic composites made by a new hybrid method. Addit Manuf 22:216–222CrossRefGoogle Scholar
  6. 6.
    Sames WJ, List FA, Pannala S, Dehoff RR, Babu SS (2016) The metallurgy and processing science of metal additive manufacturing. Int Mater Rev 61(5):315–360CrossRefGoogle Scholar
  7. 7.
    Gu DD, Meiners W, Wissenbach K, Poprawe R (2012) Laser additive manufacturing of metallic components: materials, processes and mechanisms. Int Mater Rev 57(3):133–164CrossRefGoogle Scholar
  8. 8.
    Körner C (2016) Additive manufacturing of metallic components by selective electron beam melting—a review. Int Mat Rev 61(5):315–377CrossRefGoogle Scholar
  9. 9.
    Matthews MJ, Guss G, Khairallah SA, Rubenchik AM, Depond PJ, King WE (2016) Denudation of metal powder layers in laser powder bed fusion processes. Acta Mater 114:33–42CrossRefGoogle Scholar
  10. 10.
    Zhao C, Fezzaa K, Cunningham RW, Wen H, Carlo F, Chen L, Rollett AD, Sun T (2017) Real-time monitoring of laser powder bed fusion process using high-speed X-ray imaging and diffraction. Sci Rep 7(1):3602CrossRefGoogle Scholar
  11. 11.
    King WE, Anderson AT, Ferencz RM, Hodge NE, Kamath C, Khairallah SA, Rubenchik AM (2015) Laser powder bed fusion additive manufacturing of metals; physics, computational, and materials challenges. Appl Phys Rev 2(4):041304CrossRefGoogle Scholar
  12. 12.
    Ding D, Pan Z, Cuiuri D, Li H (2015) Wire-feed additive manufacturing of metal components: technologies, developments and future interests. Int J Adv Manuf Technol 81(1–4):465–481CrossRefGoogle Scholar
  13. 13.
    Kelly GS, Just MS, Advani SG, Gillespie JW (2014) Energy and bond strength development during ultrasonic consolidation. J Mater Process Technol 214(8):1665–1672CrossRefGoogle Scholar
  14. 14.
    Butt J, Mebrahtu H, Shirvani H (2014) A novel rapid prototyping process for the production of metal parts. In: Proceedings of the 2nd international conference on advances in civil, structural and mechanical engineering-CSM, Birmingham, pp 26–29Google Scholar
  15. 15.
    He XH, Shi HJ, Zhang YD, Yang ZG, Wilkinson CE, Neal AL, Norfolk M (2015) Mechanical properties and microstructure of Al/Al laminated structure produced via ultrasonic consolidation process. Mater Sci Technol 31(15):1910–1918CrossRefGoogle Scholar
  16. 16.
    Butt J, Mebrahtu H, Shirvani H (2016) Rapid prototyping by heat diffusion of metal foil and related mechanical testing. Int J Adv Manuf Technol 84(9–12):2357–2366CrossRefGoogle Scholar
  17. 17.
    Butt J (2016) A novel additive manufacturing process for the production of metal parts. Doctoral dissertation, Anglia Ruskin UniversityGoogle Scholar
  18. 18.
    Kong CY, Soar RC, Dickens PM (2002) August. An investigation of the control parameters for aluminum 3003 under ultrasonic consolidation. In: Proceeding 13th solid freeform fabrication symposium, pp 199–211Google Scholar
  19. 19.
    British Standards Institution (2009) BS EN 1465: Adhesives—determination of tensile lap-shear strength of bonded assemblies. London, England: BSIGoogle Scholar
  20. 20.
    British Standards Institution (2016) BS EN ISO 7438: Metallic materials—bend Test. London, England: BSIGoogle Scholar
  21. 21.
    British Standards Institution (1995) BS EN ISO 10365: Adhesives—designation of main failure patterns. London, England: BSIGoogle Scholar
  22. 22.
    Da Silva LF, Carbas RJC, Critchlow GW, Figueiredo MAV, Brown K (2009) Effect of material, geometry, surface treatment and environment on the shear strength of single lap joints. Int J Adhes Adhes 29(6):621–632CrossRefGoogle Scholar
  23. 23.
    Butt J, Mebrahtu H, Shirvani H (2015) Peel and tensile test investigation of aluminium 1050 foil parts made with a new additive manufacturing process. Int J Rapid Manuf 5(1):95–115CrossRefGoogle Scholar
  24. 24.
    Butt J, Mebrahtu H, Shirvani H (2016) Strength analysis of aluminium foil parts made by composite metal foil manufacturing. Prog Addit Manuf 1(1–2):93–103CrossRefGoogle Scholar
  25. 25.
    Butt J, Mebrahtu H, Shirvani H (2018) Numerical and experimental analysis of product development by composite metal foil manufacturing. Int J Rapid Manuf 7(1):59–82CrossRefGoogle Scholar
  26. 26.
    Butt J, Mebrahtu H, Shirvani H (2016) Microstructure and mechanical properties of dissimilar pure copper foil/1050 aluminium composites made with composite metal foil manufacturing. J Mater Process Technol 238:96–107CrossRefGoogle Scholar
  27. 27.
    Butt J, Mebrahtu H, Shirvani H (2015) Thermo-mechanical analysis of dissimilar al/cu foil single lap joints made by composite metal foil manufacturing. World Acad Sci Eng Technol Int J Mech Aerosp Ind Mech Manuf Eng 10(1):41–46Google Scholar
  28. 28.
    Nammi SK, Butt J, Mauricette JL, Shirvani H (2017) Numerical analysis of thermal stresses around fasteners in composite metal foils. In: IOP conference series: materials science and engineering, vol 280, no 1. IOP Publishing, Birmingham, UK, p 012016Google Scholar
  29. 29.
    Ruffo M, Tuck C, Hague R (2006) Cost estimation for rapid manufacturing-laser sintering production for low to medium volumes. Proc Inst Mech Eng Part B J Eng Manuf 220(9):1417–1427CrossRefGoogle Scholar

Copyright information

© Springer Nature Switzerland AG 2018

Authors and Affiliations

  1. 1.Engineering and Built EnvironmentAnglia Ruskin UniversityChelmsfordUK

Personalised recommendations