Probabilistic considerations about the strength of laminated annealed float glass

  • Antonio Bonati
  • Gabriele PisanoEmail author
  • Gianni Royer Carfagni
S.I.: Glass Performance Paper
  • 4 Downloads

Abstract

Laminated structures are parallel (or redundant) systems, i.e. failure occurs when all the elements (glass plies) reach, in cascade, the ultimate limit state. Following the failure mode approach, the reliability analysis is consequent to the identification of all possible rupture modes of the glass plies, where each mode is identified by the sequence of collapse, synthetically schematized as an event-tree. The event “structural failure” is the union of all the possible failure modes. The static theorem of limit analysis guarantees that the more the structure is divided into load bearing elements acting in parallel, the safer it is, but this conclusion holds only for ideal ductile systems. For brittle glass it is often assumed that lamination gives a beneficial contribution in all cases, but glass strength is affected by a size effect in terms of area, because surface micro-cracks govern the overall capacity of the material. Taking this into account, we show through the failure mode approach, under some simplifying assumptions, that lamination can decrease the strength of a plate made of annealed glass, since the higher the number of plies is, the larger is the surface area under tensile stress. This finding focalizes the attention on the importance of an accurate characterization of the size effect in glass strength.

Keywords

Laminated glass Structural safety Redundancy Strength Size effect 

Notes

Acknowledgements

GRC acknowledges the support of the Italian Dipartimento della Protezione Civile under project ReLUIS-DPC 2019-2021 and the support of the Italian Ministero dell’Istruzione, dell’Università e della Ricerca under grant MIUR-PRIN voce COAN 5.50.16.01 code 2015JW9NJT.

References

  1. Augusti, G., Baratta, A.: Limit analysis of structures with stochastic strength variations. J. Struct. Mech. 1(1), 43–62 (1972)CrossRefGoogle Scholar
  2. Ballarini, R., Pisano, G., Royer Carfagni, G.: The lower bound for glass strength and its interpretation with generalized Weibull statistics for structural applications. ASCE J. Eng. Mech. 142(12), 04016100 (2016)CrossRefGoogle Scholar
  3. Baraldi, D., Cecchi, A., Foraboschi, P.: Broken tempered laminated glass: Non-linear discrete element modeling. Compos. Struct. 140, 278–295 (2016)CrossRefGoogle Scholar
  4. Behr, R., Minor, J., Norville, H.: Structural behavior of architectural laminated glass. J. Struct. Eng. 119, 202–222 (1993)CrossRefGoogle Scholar
  5. Bennison, S., Jagota, A., Smith, C.: Fracture of glass/poly(vinyl butyral) (butacite) laminates in biaxial flexure. J. Am. Ceram. Soc. 82(7), 1761–1770 (1999)CrossRefGoogle Scholar
  6. Biolzi, L., Orlando, M., Piscitelli, L.R., Spinelli, P.: Static and dynamic response of progressively damaged ionoplast laminated glass beams. Compos. Struct. 157, 337–347 (2016)CrossRefGoogle Scholar
  7. Bonati, A., Pisano, G., Royer Carfagni, G.: Redundancy and robustness of brittle laminated plates: overlooked aspects in structural glass. Compos. Struct. 227, 111288 (2019)CrossRefGoogle Scholar
  8. Calderone, I., Davies, P., Bennison, S., Huang, X., Gang, L.: Effective laminate thickness for the design of laminated glass. In: Proceedings of Glass Performance Days, Tampere, FI (2009)Google Scholar
  9. CEN/TC129/WG8: An overview of prEN-13474 and the work of CEN/TC129/WG8 from which it was developed. Internal Document (2006)Google Scholar
  10. CNR-DT 210: National Research Council of Italy. Guide for the Design, Construction and Control of Buildings with Structural Glass Elements. Technical Recommendations for Construction (2013)Google Scholar
  11. Evans, A.G.: A general approach for the statistical anlysis of multiaxial fracture. J. Am. Ceram. Soc. 61, 302–308 (1978)CrossRefGoogle Scholar
  12. Galuppi, L., Royer Carfagni, G.: Enhanced effective thickness of multi-layered laminated glass. Compos. Part B Eng. 64, 202–2013 (2014)CrossRefGoogle Scholar
  13. Irwin, G.: Analysis of stresses and strains near the end of a crack traversing a plate. J. Appl. Mech. 24, 361–364 (1957)Google Scholar
  14. Melchers, R.E., Beck, A.T.: Structural Reliability Analysis and Prediction, 3rd edn. Wiley, London (2018)Google Scholar
  15. Munz, D., Fett, T.: Ceramics: Mechanical Properties, Failure Behavior, Materials Selection. Springer, Heidelberg (1999)CrossRefGoogle Scholar
  16. Pisano, G., Royer Carfagni, G.: The statistical interpretation of the strength of float glass for structural applications. Constr. Build. Mater. 98, 741–756 (2015)CrossRefGoogle Scholar
  17. Pisano, G., Royer Carfagni, G.: Towards a new standardized configuration for the coaxial double test for float glass. Eng. Struct. 119, 149–163 (2016)CrossRefGoogle Scholar
  18. Pisano, G., Royer Carfagni, G.: A micromechanical derivation of the macroscopic strength statistics for pristine or corroded/abraded float glass. J. Eur. Cerem. Soc. 37, 4197–4206 (2017)CrossRefGoogle Scholar
  19. Seshadri, M., Bennison, S., Jagota, A., Saigal, S.: Mechanical response of cracked laminated plates. Acta Mater. 50, 4477–4490 (2002)CrossRefGoogle Scholar
  20. Simiu, E., Reed, A.D., Yancey, C.W.C., Martin, J.W., Hendrikson, E.M., Gonzalez, A.C. et al.: Ring-on-ring test and load capacity of cladding glass. Technical Report NBS Building Science Series 162, National Bureau of Standards, U.S. Department of Commerce (1984)Google Scholar
  21. Vandebroek, M., Louter, C., Caspeele, R., Ensslen, F., Belis, J.: Size effect model for the edge strength of glass and ground edge finishing. Eng. Struct. 79, 96–105 (2014)CrossRefGoogle Scholar
  22. Weibull, W.: A statistical theory of the strength of materials. Ingenirsvetenskapsakademiens Handlingar 151, 1–45 (1939)Google Scholar
  23. Wiederhorn, S.M., Bolz, L.H.: Stress corrosion and static fatigue of glass. J. Am. Ceram. Soc. 53(10), 543–548 (1970)CrossRefGoogle Scholar
  24. Wiederhorn, S.M.: Strength of glass: a fracture mechanics approach. Technical Report AD-780 704, National Bureau of Standards, Office Naval Research (1974)Google Scholar

Copyright information

© Springer Nature Switzerland AG 2019

Authors and Affiliations

  1. 1.CNR-ITC National Research CouncilInstitute for Construction TechnologiesSan Giuliano MilaneseItaly
  2. 2.Department of Engineering and ArchitectureUniversity of ParmaParmaItaly

Personalised recommendations