Experimental investigations on the creep behaviour of PVB under different temperatures and humidity conditions

  • M. BotzEmail author
  • K. Wilhelm
  • G. Siebert
Research paper

Abstract

The use of structural glass applications with requirements on post-fracture performance has so far only been possible under consideration of large-scale tests. The development of a design concept for fractured laminated glass is the subject of current research in structural glass engineering. This requires material models for the respected components (glass and polymer interlayer). Since moisture can reach the polymer interlayer in the fractured state via the cracks in the glass, investigations on the mechanical behaviour of the interlayer at different air humidity levels are necessary. In order to obtain the first systematically recorded parameters for the material behaviour of the most common polymeric interlayer used in laminated glass, standard Polyvinylbutyral (PVB), a test set up was developed for carrying out creep tests at different levels of load, humidity and temperatures. Subsequently, tests were conducted which were evaluated with the help of Digital Image Correlation. The results show that the stiffness of the interlayer decreases significantly with increasing relative humidity and temperature. Based on the data obtained, material models can be developed which take into account the influence of the interlayer moisture on the post fracture performance of laminated glass. Analogously to the time temperature superposition principle it can be shown, that the application of a time humidity superposition principle is possible and standard PVB is approximately a moisture rheological simple material.

Keywords

Laminated glass PVB Creep-test Humidity 

Notes

Acknowledgements

The authors thank kuraray, Devision Trosifol for providing and preparing the tested interlayer and the TechnicalUniversity Darmstadt, Institute of Structural Mechanics and Design (Miriam Schuster) for the support in the sample preparation.

Compliance with ethical standards

Conflict of interest

On behalf of all authors, the corresponding author states that there is no conflict of interest.

References

  1. Becker, F.: Entwicklung einer Beschreibungsmethodik für das mechanische Verhalten unverstärkter Thermoplaste bei hohen Deformationsgeschwindigkeiten. Dissertation, Martin-Luther-Universtiät Halle-Wittenberg (2009)Google Scholar
  2. Blumrich, F.: Optische korrelationsbasierte Messtechnik mittels zufälliger Punktemuster. Dissertation. Universität Stuttgart (2009)Google Scholar
  3. Botz, M., Kraus, M.A., Siebert, G.: Der Ansatz des Schubverbundes bei der Bemessung von Verbundgläsern, Teil 2—Grundlagen und Anwendungsbeispiele. Konstr. Ing. 01(2018), 43–52 (2018)Google Scholar
  4. Botz, M., Kraus, M.A., Siebert, G.: Untersuchungen zur thermomechanischen Modellierung der Resttragfähigkeit von Verbundglas. Glasbau, Frankfurt (2019)CrossRefGoogle Scholar
  5. DIN 18008-1: Glas im Bauwesen – Bemessungs- und Konstruktionsregeln – Teil 1: Begriffe und Grundlagen (2018)Google Scholar
  6. DIN 53441: Prüfung von Kunstoffen, Spannungsrelaxationsversuch (1984) (Withdrawn)Google Scholar
  7. DIN 53444: Prüfung von Kunststoffen, Zeitstand-Zugversuch (1990) (Withdrawn)Google Scholar
  8. EN ISO 12543-4: Glass in Building—Laminated Glass and Laminated Safety Glass—Part 4: Test Methods for Durability (2011)Google Scholar
  9. EN ISO 291: Plastics—Standard Atmospheres for Conditioning and Testing (2008)Google Scholar
  10. Ensslen, F.: Zum Tragverhalten von Verbund-Sicherheitsglas unter Berücksichtigung der Alterung der Polyvinylbutyral-Folie. Dissertation, Ruhr-Universität Bochum, Bochum (2005)Google Scholar
  11. Galuppi, L., Royer-Cafagni, G.: The post-breakage response of laminated heat-treated glass under in plane and out of plane loading. Compos Part B 147, 227–239 (2018)CrossRefGoogle Scholar
  12. Gottfried, W.E.: Polymer-Werkstoffe, Struktur-Eigenschaften-Anwendung. Carl Hanser Verlag, Munich (2011)Google Scholar
  13. Grellmann, W.: Kunststoffprüfung. Carl Hanser Verlag, Munich (2015)Google Scholar
  14. Jenckel, E.: Zur Verwendung von Modellen für das plastisch-elastische Verhalten. Kolloid Zeitschrift, 134(47) (1953).  https://doi.org/10.1007/BF01513742
  15. Kothe, M.: Alterungsverhalten von polymeren Zwischenschichtmaterialien im Bauwesen. Dissertation, Technische Universität Dresden, Dresden (2013)Google Scholar
  16. Kraus, M.A.: Machine Learning Techniques for the Material Parameter Identification of Laminated Glass in the Intact and Post-Fracture State. Dissertation, Universität der Bundeswehr München, Neubiberg (2019)Google Scholar
  17. Kraus, M.A., Niederwald, M.: Generalized collocation method using Stiffness matrices in the context of the Theory of Linear viscoelasticity (GUSTL). Tech. Mech. 37(1), 82–106 (2017b)Google Scholar
  18. Kraus, M.A., Botz, M., Siebert, G.: Der Ansatz des Schubverbundes bei der Bemessung von Verbundgläsern, Teil 1 - Grundlagen und Anwendungsbeispiele. Konstr. Ing. 06(2017), 43–51 (2017a)Google Scholar
  19. Kuntsche, J.: Mechanisches Verhalten von Verbundglas unter zeitabhängiger Belastung und Explosionsbeanspruchung. Dissertation, Technische Universität Darmstadt, Darmstadt (2015)CrossRefGoogle Scholar
  20. Kuntsche, J., Schuster, M., Schneider, J.: Bemessung von Verbundsicherheitsglas unter Berücksichtigung des Schubverbunds. Der Bauing. 93, 28–36 (2018)Google Scholar
  21. Kuraray Europe GmbH, Division TROSIFOL: TROSIFOL Manual - The Processing of TROSIFOL PVB Film (2014)Google Scholar
  22. NEN_2608: Glass in building – Requirements and determination method (2014)Google Scholar
  23. ÖNORM B 3716 – 1: Glas im Bauwesen – Konstruktiver Glasbau – Teil 1: Grundlagen (Anforderungen an die Sicherheit, Festigkeitswerte, Einwirkungen, Bemessungen) (2016)Google Scholar
  24. PRCEN/TS XXXX-1:2018: Structural Glass—Design and Construction Rules—Part 1: Basis of Design and Materials (2018)Google Scholar
  25. Rühl, A.: On the Time and Temperature Dependent Behaviour of Laminated Amorphous Polymers Subjected to Low-Velocity Impact. Technische Universität Darmstadt, Darmstadt (2017)CrossRefGoogle Scholar
  26. Sackmann, V.: Untersuchungen zur Dauherhaftigkeit des Schubverbundes in Verbundsicherheitsglas mit unterschiedlichen Folien aus Polyinylbutyral. Dissertation, Technische Universität München, Munich (2007)Google Scholar
  27. Schuler, C.: Einfluss des Materialverhaltens von Polyvinylbutyral auf das Tragverhalten von verbundsicherheitsglas in Abhängigkeit von Temperatur und Belastung. Dissertation, Technische Universität München, Munich (2003)Google Scholar
  28. Schwarzl, P.D.F.R.: Polymermechanik. Springer, Berlin, Heidelberg, New York (1990)CrossRefGoogle Scholar
  29. Williams, M.L., Landel, R.F., Ferry, H.D.: The temperature dependence of relaxation mechanisms in amorphous polymers and other glass-forming liquids. J. Am. Chem. Soc. 77(14) (1955).  https://doi.org/10.1021/ja01619a008 CrossRefGoogle Scholar
  30. Ylinen, A.: Über die Bestimmung der zeitbedingten elastischen und Festigkeitseigenschaften des Holzes mit Hilfe eines allgemeinen nichtlinear viskoelastischen rheologischen Modelles. Holz Roh Werkst. 23(5), 193–196 (1965).  https://doi.org/10.1007/BF02612966 CrossRefGoogle Scholar
  31. Z-70.3-230: Allgemeine bauaufsichtliche Zulassung Z-70.3-230: Verbundglas aus der Produktfamilie SAFLEX DG mit Schubverbund. In: Prüfamt, D.I.f.B.-Z.f.B.u.B.-B. (ed.). (2016)Google Scholar
  32. Z-70.3-236: Allgemeine bauaufsichtliche Zulassung Z-70.3-236 Verbund-Sicherheitsglas mit der PVB-Folie TROSIFOL ES mit Schubverbund. In: Prüfamt, D.I.f.B.-Z.f.B.u.B.-B. (ed.). (2016)Google Scholar

Copyright information

© Springer Nature Switzerland AG 2019

Authors and Affiliations

  1. 1.Institute and Laboratory for Structural EngineeringBundeswehr University MunichNeubibergGermany

Personalised recommendations