High Strain Rate Response of Al0.7CoCrFeNi High Entropy Alloy: Dynamic Strength Over 2 GPa from Thermomechanical Processing and Hierarchical Microstructure

  • S. Gangireddy
  • B. Gwalani
  • R. Banerjee
  • R. S. Mishra
Article
  • 25 Downloads

Abstract

Dynamic mechanical behavior of a dual-phase, precipitation-hardenable, near-eutectic, hierarchical high entropy alloy Al0.7CoCrFeNi was investigated using split-Hopkinson pressure bar. Cast alloy was processed via cold rolling to 30% reduction and annealing at two different temperatures, 1100 °C/5 min and 580 °C/24 h. The microstructure consists of a fine FCC + B2 lamellar structure which looked similar for all three conditions under scanning electron microscope but demonstrated very disparate flow stresses. X-ray diffraction measurements were used to analyze stored dislocation density, i.e. micro-strain in the individual phases i.e. FCC and B2, induced by the cold work and the extent of its recovery after each heat treatment. Transmission electron microscopy was used to characterize the naano-scale features in all the three heat treatment conditions. Low temperature annealing at 580 °C/24 h, with limited recovery of cold work coupled with precipitation of L12 in FCC phase and an adjacent B2/BCC lamellar phase, was discovered to result in exceptionally high dynamic strength of 2150 MPa.

Keywords

Dynamic deformation Al0.7CoCrFeNi Thermomechanical processing Ordered intermetallic Cold work 

Notes

Acknowledgements

The work was performed under a cooperative agreement between the Army Research Laboratory and the University of North Texas (W911NF-16-2-0189). We also acknowledge the Materials Research Facility at the University of North Texas for microscopy facilities.

References

  1. 1.
    Yeh JW (2006) Recent progress in high entropy alloys. Ann Chim Sci Mat 31(6):633–648CrossRefGoogle Scholar
  2. 2.
    Yeh JW (2007) Novel alloy concept, challenges and opportunities of high-entropy alloys. In: Raj B (ed) Frontiers design materials. CRC Press, Boca Raton, pp. 31–47Google Scholar
  3. 3.
    Ranganathan S (2003) Alloyed pleasures: multimetallic cocktails. Curr Sci 85(5):1404–1406Google Scholar
  4. 4.
    Zhang Y (2008) Solid-solution phase formation rules for multi-component alloys. Adv Eng Mater 10(6):534–538CrossRefGoogle Scholar
  5. 5.
    Gao MC (2016) High-entropy alloys. Springer, ChamCrossRefGoogle Scholar
  6. 6.
    Tsai M-H (2014) High-entropy alloys: a critical review. Mater Res Lett 2(3):107–123CrossRefGoogle Scholar
  7. 7.
    Liu G, Liu L, Liu X, Wang Z, Han Z, Zhang G, Kostka A (2018) Microstructure and mechanical properties of Al 0.7 CoCrFeNi high-entropy-alloy prepared by directional solidification. Intermetallics 93:93–100CrossRefGoogle Scholar
  8. 8.
    Lu Y, Dong Y, Guo S, Jiang L, Kang H, Wang T, Ruan H (2014) A promising new class of high-temperature alloys: eutectic high-entropy alloys. Sci Rep 4:6200CrossRefGoogle Scholar
  9. 9.
    Liao Y, Baker I (2008) Microstructure and mechanical properties of Fe30Ni20Mn35Al15. Mater Charact 59:1546–1549CrossRefGoogle Scholar
  10. 10.
    Joseph J (2017) Understanding the mechanical behaviour and the large strength/ductility differences between FCC and BCC AlxCoCrFeNi high entropy alloys. J Alloys Compd 726:885–895CrossRefGoogle Scholar
  11. 11.
    Chou HP (2009) Microstructure, thermophysical and electrical properties in AlxCoCrFeNi (0 ≤ x ≤ 2) high-entropy alloys. Mater Sci Eng B 163(3):184–189CrossRefGoogle Scholar
  12. 12.
    Chen WP, Fu ZQ, Fang SC, Xiao HQ, Zhu DZ (2013) Alloying behavior, microstructure and mechanical properties in a FeNiCrCo0.3Al0.7 high entropy alloy. Mater Des 51:854–860CrossRefGoogle Scholar
  13. 13.
    Zheng RX, Chen J, Xiao WL, Ma CL (2016) Microstructure and tensile properties of nanocrystalline (FeNiCoCu)1-xTixAlx high entropy alloys processed by high pressure torsion. Intermetallics 74:38–45CrossRefGoogle Scholar
  14. 14.
    Laplanche G, Kostka A, Horst OM, Eggeler G, George EP (2016) Microstructure evolution and critical stress for twinning in the CrMnFeCoNi high entropy alloy. Acta Mater 118:152–163CrossRefGoogle Scholar
  15. 15.
    Niu S et al (2016) Strengthening of nanoprecipitations in an annealed Al0. 5CoCrFeNi high entropy alloy. Mater Sci Eng A 671:82–86CrossRefGoogle Scholar
  16. 16.
    Wang J et al (2017) The FCC to BCC phase transformation kinetics in an Al0. 5CoCrFeNi high entropy alloy. J Alloys Compd 710:144–150CrossRefGoogle Scholar
  17. 17.
    Guo T et al (2018) Microstructure and properties of bulk Al0. 5CoCrFeNi high-entropy alloy by cold rolling and subsequent annealing. Mater Sci Eng A 729:141–148CrossRefGoogle Scholar
  18. 18.
    Wang L et al (2018) Mechanical response and deformation behavior of Al0. 6CoCrFeNi high-entropy alloys upon dynamic loading. Mater Sci Eng A 727:208–213CrossRefGoogle Scholar
  19. 19.
    Li Z, Zhao S, Diao H, Liaw PK, Meyers MA (2017) High-velocity deformation of Al 0. 3 CoCrFeNi high-entropy alloy: remarkable resistance to shear failure. Sci Rep 7:42742CrossRefGoogle Scholar
  20. 20.
    Gangireddy S, Gwalani B, Soni V, Banerjee R, Mishra RS (2018) Contrasting mechanical behavior in precipitation hardenable AlXCoCrFeNi high entropy alloy microstructures: single phase FCC vs. dual phase FCC-BCC. Mater Sci Eng A 739:158–166Google Scholar
  21. 21.
    Giwa AM (2016) Microstructure and small-scale size effects in plasticity of individual phases of Al 0.7 CoCrFeNi high entropy alloy. Extrem Mech Lett 8:220–228CrossRefGoogle Scholar
  22. 22.
    Chen WW (2010) Split Hopkinson (Kolsky) bar: design, testing and applications. Springer, BostonGoogle Scholar
  23. 23.
    Williamson GK, Hall WH (1953) X-ray line broadening from filed aluminium and wolfram. Acta Metall 1(1):22–31CrossRefGoogle Scholar
  24. 24.
    de Formanoir C (2017) A strategy to improve the work-hardening behavior of Ti–6Al–4V parts produced by additive manufacturing. Mater Res Lett 5(3):201–208Google Scholar
  25. 25.
    Bartholomeusz MF (1995) The enhanced work hardening rates of the constituent TiAl and Ti3Al phases in a lamellar microstructure. Mater Sci Eng A 201(1-2):24–31CrossRefGoogle Scholar
  26. 26.
    Tsai MH (2013) Significant hardening due to the formation of a sigma phase matrix in a high entropy alloy. Intermetallics 33:81–86CrossRefGoogle Scholar
  27. 27.
    Dieter GE, Bacon DJ (1986) Mechanical metallurgy, vol 3. McGraw-hill, New YorkGoogle Scholar

Copyright information

© Society for Experimental Mechanics, Inc 2018

Authors and Affiliations

  1. 1.Advanced Materials and Manufacturing Processes InstituteUniversity of North TexasDentonUSA
  2. 2.Materials Science and EngineeringUniversity of North TexasDentonUSA

Personalised recommendations