, Volume 62, Issue 12, pp 1934–1935 | Cite as

Homogeneous core-shell structure stabilizes Mn4+-doped fluoride red phosphors for high-performance warm-white LEDs

  • Xiaoyong HuangEmail author
Highlight
  • 102 Downloads

References

  1. 1.
    Huang X. New red phosphors enable white LEDs to show both high luminous efficacy and color rendering index. Sci Bull, 2019, 64: 879–880CrossRefGoogle Scholar
  2. 2.
    Huang X. Red phosphor converts white LEDs. Nat Photon, 2014, 8: 748–749CrossRefGoogle Scholar
  3. 3.
    Zhu H, Lin CC, Luo W, et al. Highly efficient non-rare-earth red emitting phosphor for warm white light-emitting diodes. Nat Commun, 2014, 5: 4312CrossRefGoogle Scholar
  4. 4.
    Lin H, Hu T, Huang Q, et al. Non-rare-earth K2XF7:Mn4+ (X = Ta, Nb): a highly-efficient narrow-band red phosphor enabling the application in wide-color-gamut LCD. Laser Photonics Rev, 2017, 11: 1700148CrossRefGoogle Scholar
  5. 5.
    Huang L, Liu Y, Yu J, et al. Highly stable K2SiF6:Mn4+@K2SiF6 composite phosphor with narrow red emission for white LEDs. ACS Appl Mater Interfaces, 2018, 10: 18082–18092CrossRefGoogle Scholar
  6. 6.
    Arunkumar P, Kim YH, Kim HJ, et al. Hydrophobic organic skin as a protective shield for moisture-sensitive phosphor-based optoelectronic devices. ACS Appl Mater Interfaces, 2017, 9: 7232–7240CrossRefGoogle Scholar
  7. 7.
    Nguyen HD, Lin CC, Liu RS. Waterproof alkyl phosphate coated fluoride phosphors for optoelectronic materials. Angew Chem Int Ed, 2015, 54: 10862–10866CrossRefGoogle Scholar
  8. 8.
    Fang MH, Hsu CS, Su C, et al. Integrated surface modification to enhance the luminescence properties of K2TiF6:Mn4+ phosphor and its application in white-light-emitting diodes. ACS Appl Mater Interfaces, 2018, 10: 29233–29237CrossRefGoogle Scholar
  9. 9.
    Huang D, Zhu H, Deng Z, et al. Moisture-resistant Mn4+-doped core-shell-structured fluoride red phosphor exhibiting high luminous efficacy for warm white light-emitting diodes. Angew Chem Int Ed, 2019, 58: 3843–3847CrossRefGoogle Scholar

Copyright information

© Science China Press and Springer-Verlag GmbH Germany, part of Springer Nature 2019

Authors and Affiliations

  1. 1.Institute for Advanced StudyShenzhen UniversityShenzhenChina
  2. 2.College of Physics and OptoelectronicsTaiyuan University of TechnologyTaiyuanChina

Personalised recommendations