Abstract
Nanocarbon-based materials, such as carbon nanotubes (CNTs) and graphene have been attached much attention by scientific and industrial community. As two representative nanocarbon materials, one-dimensional CNTs and two-dimensional graphene both possess remarkable mechanical properties. In the past years, a large amount of work have been done by using CNTs or graphene as building blocks for constructing novel, macroscopic, mechanically strong fibrous materials. In this review, we summarize the assembly approaches of CNT-based fibers and graphene-based fibers in chronological order, respectively. The mechanical performances of these fibrous materials are compared, and the critical influences on the mechanical properties are discussed. Personal perspectives on the fabrication methods of CNT- and graphene-based fibers are further presented.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
1 Introduction
Nanocarbon-based materials, such as carbon nanotubes (CNTs) and graphene, are extensively investigated due to their outstanding properties such as large theoretical specific area, high Young’s modulus (E), unparalleled thermal and electricity conductivity, and ultrahigh electron mobilities [1–4]. It is of practical significance to integrate the superior physical and chemical properties of individual CNTs or graphene to the macroscopic level by assembling them into macroscopic architectures [4]. As a representative of high-performance fibers, carbon fibers featured by their high tensile strength (σ) and E are widely used in aerospace, aviation, automobile, electronic, mechanical, chemical, textile, and other civilian industry. However, the electrical and thermal conductivities of carbon fibers are not satisfied. One-dimensional (1D) macroscopic architecture of CNTs and graphene, namely CNTs fibers (CFs) and graphene fibers (GFs), are analogous to carbon fibers in constitution and structure. Moreover, the combined performances including good flexibility and excellent electrical and thermal conductivities make them potential as structural–functional integrated materials. As more attentions have been attracted to the macroscopic fibers of 1D CNTs and 2D (two-dimensional) graphene, it is the time to give a correlative review about CFs and GFs together. We think that this insightful review can help researchers to have a better systematic understanding of the whole developing journey of macroscopic assembled fibers. In this mini review, we firstly introduce the assembly strategies of CFs and GFs and then compare the mechanical performance of fibers made from different approaches. Finally, we present our perspectives on the future of CFs and GFs.
2 CNTs Fibers: 1D CNTs Macroscopic Architectures
Macroscopic fibers containing only CNTs will yield great advances in high-tech applications (e.g., aerocraft, lightweight cables) if they can attain the extraordinary mechanical and electrical properties of individual CNTs. This requires that the CNTs in the fibers are sufficiently long, highly aligned, and packed in an arrangement, and is nearly free of defects. Until now, the strategies for assembling CNTs to CFs can be classified into liquid- or solid-state spinning approaches. Liquid-state spinning approaches involve the dispersing of CNTs in a suitable solvent and shaping in coagulation bath. Solid-state spinning approach circumvents the dissolution problem either by drawing a fiber from a vertically grown CNT array or by drawing directly from an aerogel in the furnace [5].
2.1 Liquid-State Spinning Approaches
Liquid-state spinning approaches generally include polymer-based coagulation spinning method, liquid crystalline (LC) spinning method, polymer-free spinning method, and dip-coating method. Among them, polymer-based coagulation spinning method is first introduced to achieve CFs.
2.1.1 Polymer-Based Coagulation Spinning Method
The history of CFs fabrication dates back as far as 17 years ago. In 2000, Poulin’s group dispersed single-wall carbon nanotubes (SWNTs) in sodium dodecyl sulfonate (SDS) solutions, recondensed the nanotubes in the flow of poly(vinyl alcohol) (PVA) solution to form a nanotube mesh, and then collated this mesh to a nanotube fiber (Fig. 1a–c). When SWNTs dispersion was slowly injected through a syringe needle or a thin glass capillary, flow-induced alignment of the nanotubes occurred in the direction of the fluid velocity. The flow-induced alignment was maintained by the PVA solution since it allows the SWNTs to be rapidly stuck together. The as-made CNT/PVA fibers possess good mechanical performance with 150 MPa for σ and 15 GPa for E [6]. Replaced SDS surfactant with DNA, the CFs were also mechanically strong and conductive [7]. Scanning electron microscopy (SEM) images reveal that the fiber has a circular cross section with 80 μm in diameter (Fig. 1d) and well-resolved network of DNA-SWNT hybrid (Fig. 1e) [8].
By utilizing SWNTs synthesized from carbon monoxide and lithium dodecyl sulfate as a surfactant, Baughman’s groups first produced mechanically strong gel fibers. After post-treatment with acetone-washing bath, continuous, multifunctional dry CFs were achieved. The resultant CFs showed a dramatically increased σ and toughness (570 J g−1) [9, 10] Besides, hot-drawing technique was utilized to improve the properties of CFs [11]. The resulting 10-m-long fiber collected onto a small winder is shown in Fig. 1f. This treatment induced a crystallinity increase in the PVA and an unprecedented degree of alignment of the CNTs, leading to a markedly improved energy absorption at low strain [11].
2.1.2 LC Spinning Method
The main challenge of producing CFs is to disperse the CNTs at high concentration for efficient alignment. Using surfactant is an effective approach to disperse CNTs into solutions, yet there is a loss in the properties of CFs due to the decreased van der Waals interaction between the neighboring CNTs. So super-acid (100% sulfuric acid) was introduced to increase the dispersity of CNTs. The protonated SWNTs in the super-acid behave as rigid-rod-like liquid crystals (LC) and exhibit an isotropic-to-nematic phase transition with an increased concentration (Fig. 2a, b) [12–14]. Based on this behavior, LC spinning technique was proposed to produce highly orientated CF [15, 16]. Windle’s group spun fibers consisting of multi-wall carbon nanotubes (MWNTs) directly from the lyotropic LC phase. Ethylene glycol was used as the lyotropic solvent, enabling a wider range of CNTs types (SWNTs, DWNTs, MWNTs) to be spun than previously. Fibers spun with CNTs and nitrogen-doped CNTs were also compared [16]. The spun fibers were flexible and can be easily twisted and knotted. The orientation increased with decreasing the diameter of fibers, leading to better thermal and electrical conductivity [17].
Ericson et al. [18] improved this method by dispersing SWNTs in fuming sulfuric acid (102% sulfuric acid), which charges SWNTs by acid anions and orders them into an aligned phase. When the viscosity reached a steady state, the SWNTs dispersion was extruded through a small capillary tube into a coagulation bath and collected onto a Teflon drum after washing (Fig. 2c–e). The resulting CFs possess good mechanical (120 GPa for E and 116 MPa for σ) and electrical (5000 S cm−1) properties.
2.1.3 Polymer-Free Spinning Method
Unlike the LC spinning method, polymer-free spinning process using dilute, low-viscosity CNT dispersions (0.6 wt%) as spinning dope. By adjusting the pH (pH > 13 or pH < 1), polymer-free, surfactant-stabilized CNTs were flocculated/coagulated rapidly and uniformly to afford continuous CNTs gel fibers (Fig. 3a, b) [19]. In addition, hollow fibers, folded ribbon fibers, and solid CFs can also be easily achieved by this method (Fig. 3c–f) [19]. Due to the absence of polymer, the electrical conductivities (15 S cm−1) of these fibers were two orders of magnitude higher than that of fibers made by polymer-based coagulation spinning method (0.2 S cm−1).
2.1.4 Dip-Coating Method
Besides the above three spinning techniques, a quite simple dip-coating method of fabricating CFs without any additive was developed with no additional electrical equipment or complex apparatus. This method utilizes microfluidics, which includes capillary condensation, capillary flow, and surface tension, and results in the self-assembly and self-alignment of SWNT colloids (Fig. 4) [20]. The resulting SWNT fibers with a diameter of 10–20 μm and a length of several tens of centimeters possess good electrical conductivity of 3000 S cm−1.
2.2 Solid-State Spinning Approaches
2.2.1 Spinning 1D CFs from CNT Array
Drawing CNTs out from superaligned CNT array is an efficient way to prepare long CFs. The original work was done by Fan and co-workers. They produced a continuous yarn of pure CNTs (Fig. 5a) by pulling out a bundle of CNTs from a CNTs array several hundred micrometers high and grown on a silicon substrate. Figure 5b shows a 100-μm-high, freestanding CNT array with an indentation region that is being turned into a 30-cm-long and 200-μm-wide yarn. It was estimated that an array area of roughly 1 cm2 can generate about 10 m of yarn. To achieve continuous yarns, the CNTs in the arrays must be superaligned and held together by van der Waals interactions to form bundles (Fig. 5c). The as-spun yarns were composed of parallel threads that have diameters in the range of several hundreds of nanometers (Fig. 5d) [21].
Inspired by this report, Zhu’s group has done a series of work in the fabrication of CFs with high strength [22–26]. They synthesized a series of CNT arrays with lengths up to 4.7 mm by an ion-beam assisted deposition technique. The CNT arrays were spinnable in a wide range of lengths (0.5–1.5 mm), much longer than those reported previously [22]. Such long arrays rendered CFs with superior strength and electrical conductivity, and the highest σ of 3.3 GPa for CFs were spun from the 1-mm array [22]. The properties of CFs can be also improved by decreasing the diameter of the fibers or increasing the packing density of CNTs in the fiber (Fig. 5e, f) [23, 24]. As a result, the CFs can be twisted to hold a 0.1-mm-diameter Ni wire (Fig. 5g, h).
In addition, the effect of chemical post-treatments was also demonstrated. The covalent bonding of gold nanoparticles to the CFs remarkably improves conductivity, whereas annealing CFs in hydrogen-containing atmosphere leads to a dramatic decrease in conductivity [25]. Besides common CNT constitution, well-aligned, pearl-like CNTs were also assembled into macroscopic fibers. Due to the unique morphology, these fibers possess tensile strength of 350 MPa and electrical conductivity of 250 S cm−1 [26].
2.2.2 Direct Spinning Based on Chemical Vapor Deposition (CVD) Technique
CVD technique is a common approach to synthesize CNTs. In 2002, the CVD technique was modified to directly synthesize microscopic 1D CFs. Long CNT strands (20 cm in length, a diameter of 0.3 mm, Fig. 6a, b) consisting of aligned SWNTs (Fig. 6c) were achieved through the catalytic pyrolysis of n-hexane with an enhanced vertical floating technique [27]. The edges of the spun SWNT strands were smooth, with a few individual nanotube bundles protruding out of the edge (Fig. 6b). High-resolution transmission electron microscopy (HRTEM) images (Fig. 6d) show that each bundle is composed of aligned SWNTs.
This method was then carried forward by Windle’s group [28–31]. They drew the CVD-grown CNT aerogel onto a rotating rod, produced continuous fibers with a degree of twist (Fig. 6e–i). This endowed the CNT fibers with excellent flexibility. The fibers can be unwound from the spindle and wound up onto another rod and can hold the twisting state after removal from the rod (Fig. 6j) [28]. Because the structure of the fibers itself consists of a network of smaller filament subunits (nanotubes and bundles), they can bend through very tight radii without apparent permanent damage and showed knot efficiencies of 100% (Fig. 6k, l) [29]. By optimizing the process conditions including using three different hydrocarbons, changing the concentration of iron nanocatalyst, the maximum σ of CFs was reached to 1.46 GPa [30].
Based on these prior works, Li et al. further advanced this approach and fabricated novel continuous CFs with a multilayered structure. The CFs, featured with a length of over several kilometers and a quality close to conventional textile yarns, can be controlled to be either hollow or monolithic with compacted or detached CNT monolayers by controlling the spinning process [32].
2.2.3 Twisting CNT Films
Twisting CNT thin films with mesh-like structure can afford uniform CF (Fig. 7a). Although this method may not be suitable for continuous production of CFs, the control of the diameters and twisting degrees is more convenient [33–35]. Since the twisting process led to the stretch and alignment of nanotubes (Fig. 7b), the interbundle junctions were reinforced and the fibers have higher strengths than the films [33]. Twisting the fibers to a higher degree, a yarn-derived spring-like CNT rope, that consisted of uniform, neat loops with perfect arrangement over long distance, were formed (Fig. 7c, d) [36]. The elongation at break point of these CNT ropes is up to 285% by loop opening and straightening during elongation. Within a moderate strain (20%), the CNT rope behaved like a spring with a stable spring constant when stretched by 1000 times with energy absorption during contraction [36–38]. This twisting–spinning process was further employed to produce a highly twisted yarn-derived double-helix structure. The double-helix configurations were stable and consisted of two single-helical yarn segments, with controlled pitch and much larger strain up to 150% [39].
Besides the spinning of neat CFs, this method can make the powders and nanofibers spinnable. Combined CNT sheets with other functional materials, more than 95 wt% of powders or nanofibers were incorporated into scrolled CNT yarns, while maintaining the guest functionality in the meantime (Fig. 7h–j). The complex structures of scroll sacks were related to twist-dependent extension of Fermat spirals (Fig. 7e), Archimedean spirals (Fig. 7f), or spiral pairs (Fig. 7g) into scrolls. Although a very small amount of CNT host is employed to mechanically confine the unbonded powder guest, biscrolled yarns can still be knotted and sewn (Fig. 7k–m). This technology was used to make yarns of superconductors, lithium-ion battery materials, graphene ribbons, catalytic nanofibers for fuel cells, and titanium dioxide for photocatalysis [40].
2.2.4 Other Methods
Different from the method of direct spinning based on CVD technique, which involves the directly drawing and twisting of the fresh generated CNT hot aerogel, Ci et al. fabricated continuous CFs from the cool DWNT cotton based on surface-tension-driven densification. The starting, cotton-like material must be wet in order to draw a continuous fiber because the wet material is denser and has stronger internanotube interactions [41]. Figure 8a shows a schematic illustration of the spinning process, and an optical image of the as-spun DWNT fibers. Similarly, a 35-mm-long quartz-supported CNT cotton was spun into 10-cm-long fibers with good mechanical strength through simply pulling and rotating [42]. Individual CNTs in the cotton were easily collected and aligned along the pulling direction during fiber spinning (Fig. 8b, c).
Electrophoretic approach is generally used in the field of assembly. The early try of assembling CNTs into fibers was finished by Alldredge and co-workers. A carbon fiber tip was withdrawn slowly from a dispersion of SWNT under an electric field. During this process, CNTs were gathered around and assembled one-by-one at the positively charged carbon fiber tip, yet only 5-cm-long fibers could be achieved [43]. Distinct from the former assembly method, Liu et al. invented a step-by-step way to prepare CNT yarns by drawing the CVD-grown films through a series of diamond wire drawing dies (Fig. 8d). Passing through the series dies with decreased pore diameters, the CNT networks were highly aligned and densified into 1D fibers [44, 45].
No matter what methods applied, the nanotubes in CF must be superaligned and densely packed to achieve high performance. Based on the above, we can draw a conclusion that shear rate within the extrusion orifice, flow-induced alignment in the direction of the fluid velocity and the spontaneous ordering in the liquid crystalline phase are all responsible for the alignment. Polarized Raman spectroscopy and XRD can been used to quantitatively probe the degree of alignment. Meanwhile, high-speed drawing, twisting, and surface-tension-driven densification can increase in interbundle contact and packing density.
We will give an example to show how to improve the degree of alignment and packing density by adjusting process parameters. One typical work by Windle’s group systematically explored the effects of density and orientation on the properties of CNT fibers [31]. The degree of alignment and density can be increased simultaneously by increasing the fiber-winding rate, which is a basic precept for the processing of commercial polymer fiber. Additionally, running the fiber through a vapor stream can also significantly densify the fiber due to the surface tension effect. Another important processing technique to improve the mechanical performance is decreasing the diameters of the fiber, which will effectively reduce the flaws along the fiber samples according to Griffith size-scaling law.
3 Graphene Fibers: 1D Graphene Macroscopic Architectures
Inspired by the assembly strategies for CFs, 1D GFs were also assembled through analogous approaches such as LC spinning, twisting their 2D films, electrophoretic method. Even so, many novel methods were further developed to achieve GFs with high strength and high electrical conductivity.
3.1 Liquid-State Spinning Approaches
Graphene or graphene oxide (GO) can yield LC phase due to its high aspect ratio (or width/thickness ratio) and sufficient dispersibility/solubility with the solution concentration up to 30 mg mL−1 [46–49]. This LC phase is promising for processing of neat graphitic macroscopic articles such as fibers. In 2011, Gao’s group firstly spun continuous GF utilizing the liquid crystal phase behavior of GO sheets in aqueous solution (Fig. 9a) [46]. The gel-state graphene was extruded from glass syringes and injected into the NaOH/methanol solution under 1.5 MPa held by N2 flow. The sheet alignment inherited from the intrinsic lamellar order of LCs provides strong interactions between contacted sheets that were responsible for the strong mechanical strength of GFs. The locally crumbled structures of individual sheets made the GFs flexible (Fig. 9b, c), which can be even woven into a compact knot (Fig. 9d) [46]. The GFs were then functionalized by MnO2 and polyaniline and used as electrodes of yarn supercapacitors [50, 51].
Wallace’s group used a multi-hole spinneret to produced GO yarns (Fig. 9e, f). They revealed the correlation of processability with LC behavior (Fig. 9g), aspect ratio, and the dispersion concentration to provide a viable platform for spinning of LC GO [49]. By adjusting the GO sheet size and polydispersity, the very low concentrations GO dispersions (as low as 0.075 wt%) can be used as spinning dope to prepare the continuous GFs [49]. The morphology of the fiber reveals that GO sheets were stacked in layers with some degree of folding and were orientated along the fiber axis direction (Fig. 9h, i). Neat and macroscopic GFs with mechanical strength of 182 MPa and electrical conductivity of 3500 S m−1 were also be spun by Yu’s group. They injected GO dispersion into CATB solution, and the curliness-fold formation mechanism of GO fibers was proved by SEM observations (Fig. 10) [52]. By introducing shear stress during wet-spinning process, flat and uniform ribbons with high flexibility were also produced [53].
Neat GO aerogel fibers with unique “porous core-dense shell” structure from flowing GO LCs with lamellar ordering were fabricated by the combination of spinning technology and ice-templating strategy (Fig. 11a) [54]. Graphene porous fibers (GPFs) were achieved after chemical or thermal reduction, which were flexible and can be folded (Fig. 11b). The folded GPFs was stretched to its original straight shape without any fracture (Fig. 11c). The SEM observation revealed that graphene sheets interconnect with each other and form axially aligned empty cells (Fig. 11d, e). The GPFs held high σ and high compression strength [54].
Neat, morphology-defined, graphene-based hollow fibers were fabricated via a coaxial two-capillary spinning strategy [55]. The coaxial two-capillary spinneret was fabricated by inserting a stainless steel needle (connected to a syringe-containing coagulation bath) into a branched glass tube (filled with GO suspension) with a capillary tip. Figure 11f shows a schematic illustration of the apparatus for spinning with the coagulation bath of methanol solution containing 3 M KCl. The semitransparent graphene oxide hollow fibers (GO-HFs) (Fig. 11g) were continuously produced, and the hollow structure was reflected by the open tip (Fig. 11g, inset) and SEM observation (Fig. 11h). After being naturally dried, the GO-HFs were converted to black color (Fig. 11i). Replacing the inner fluid of KCl/methanol solution with compressed air, the obtained GO-HFs displayed a necklace-like structure (Fig. 11j).
This coaxial wet-spinning technology is further extended to prepare core-sheath GFs [56]. The spinning process is shown in Fig. 12a. GO dispersion and sodium carboxymethyl cellulose (CMC) aqueous solutions were chosen as inner and outer spinning dopes, respectively. The as-prepared coaxial fibers were featured with GO as core and CMC as sheath (Fig. 12b, c), and the CMC sheath wrapped the core tightly without any gaps and void (Fig. 12h–j). Treated by chemically reduced with hydroiodic acid, the color of the core was changed from brown to dark while the polyelectrolyte sheath retained well (Fig. 12d). A 100-m-long coaxial fiber was achieved by this approach (Fig. 12e). The integration of high flexibility and scalable fabrication made these coaxial fibers promising in co-woven with cotton yarns (Fig. 12f). A cloth supercapacitor was then fabricated by using two individual 40-cm-long coaxial fibers as anode and cathode (Fig. 12g). Besides the cloth supercapacitor, the yarn supercapacitors were also prepared by tightly intertwining two coaxial fibers followed by coating a layer of H3PO4-PVA gel electrolyte as ion source (Fig. 12k–m). The as-prepared yarn supercapacitors were very safe, and short circuit never happened in the assembly and working process of YSCs because of the protection of the CMC sheath.
Chemical functionalization of graphene with polymer can enhance the dispersibility in specific solvents and afford them LC behavior. Polyacrylonitrile (PAN) and poly (glycidyl methacrylate) (PGMA) chains were covalently and uniformly grafted onto GO surfaces via a simple free radical polymerization process [57, 58]. The continuous, conductive, flexible graphene composite fibers were then spun utilizing them as building blocks.
To make the multifunctionalization of graphene-based fibers fast and easy, Gao’s group combined liquid crystal self-templating (LCST) approach and wet-spinning technology to continuously fabricate biomimetic composites fibers (Fig. 13a–g). They introduced hyperbranched molecules (HPG) [59, 60] into the LC-state GO dispersion to achieve nacre-mimic fibers with excellent mechanical performance (σ = 652 MPa, E = 20.9 GPa). A deformation mechanism model was also proposed based on the SEM observation (Fig. 13h–j). Besides HPG, PVA [61] and sodium alginate (SA) [62] acted as guests were also mixed with GO host. The assembled macroscopic GO-SA composite fiber inherited the alignment of the GO sheets from the LC phase (Fig. 13k–m), reached 784.9 MPa and 58 GPa for σ and E, respectively. Apart from the above macromolecules, inorganic components such as Ag nanowires [63], bismuth oxide nanotubes [64] and montmorillonite [65] were also employed as introduced guests to endow graphene-based composite fibers with multiple functions such as high electrical conductivity, improved electrochemical properties and flame retardant.
3.2 One-step Dimensionally Confined Hydrothermal Strategy
Besides the above wet-spinning method, Qu’s group developed a one-step dimensionally confined hydrothermal strategy to prepared GFs [66]. They injected aqueous GO suspension into the glass pipeline with a 0.4-mm-inner diameter by use of a syringe and baked it at 230 °C for 2 h after sealing up the two ends of the pipeline. The wet state GF matching the pipe geometry was produced. It was released from the pipeline by flow of N2 and was hold by glass slides for drying in air [66]. To endow the fiber multifunction, they integrated the GFs with Fe3O4 and TiO2 and obtained functional GFs with magnetic and photoelectric (electrical current induced by light) response [66]. The Fe3O4 functionalized GFs was then acted as both substrate and catalyst for CVD growth of CNTs. The subsequent 1D CNTs and 2D graphene hybrid fibers with a large surface area (ca. 79.5 m2 g−1) and high electrical conductivity (1200 S m−1) were achieved [67]. This strategy is then extended to using PP pipeline instead of glass pipeline and vitamin C, and low temperature chemical reduction replace of hydrothermal reduction [68].
3.3 Electrophoretic Self-Assembly Method
Reduced GO nanoribbon (GONR) fibers were also fabricated by using an electrophoretic self-assembly method without any polymer or surfactant. Specifically, a graphitic tip as a positive electrode was immersed into the chemically reduced GONR colloidal solution in a Teflon vessel containing the counter electrode. The distance between two electrodes is ca. 5 mm, and the fiber is drawn out under a constant voltage ranging from 1 to 2 V. After annealing treatment, the fiber showed superior field emission performance with a low potential for field emission and a giant field emission current density when compared with vertically aligned few-layer graphene and single-layer graphene films prepared by electrophoretic deposition [69].
3.4 Self-Assembly from 2D Graphene Films
Different from the above three methods using GO as precursors, self-assembly method directly utilizes graphene films to fabricate GFs. The 1D fiber-like structures were self-assembled from 2D graphene films in an organic solvent (e.g., ethanol, acetone) and then dried to give the porous and crumpled structure [70, 71]. The morphology and pore structure of the fibers can be adjusted by controlling the evaporation of solvents with suitable surface tension [72–74].
4 Mechanical Properties of CNTs/Graphene Fibers
4.1 Mechanical Properties of CFs
Based on the assembly approaches, the mechanical properties of CFs show a broad range from 109 to 8800 MPa for σ and 1.25 to 397 GPa for E (as shown in Table 1). In general, CFs spun from CNT aerogel/array show higher σ and E than those produced by wet-spinning approach. To further improve the mechanical performance to compete with conventional high-performance fiber materials (e.g., Kevlar and CFs), it is fundamentally important to probe the critical factors affecting the mechanical properties of CFs. The CNT structures (diameter, aspect ratio, defects, morphology, purity, and orientation) [75] and CF geometries (e.g., diameter, twist angle, and volume fraction) are two major factors dominating CFs’ mechanical behavior. In the case of CNT structures, SWNTs or DWNTs are the best candidates to achieve good fiber performances compared with MWNTs. The well-aligned CNT arrays yield fibers with much higher performance, while wavy and entangled arrays give poor properties [76]. The larger the aspect ratio of graphene units and CNTs, the higher the tensile strength of the CF. In the case of fiber geometries, both the σ and E would reduce with increasing twisting MWNT fibers to a larger extent [77].
Owing to the weak van der Waals interaction between the neighboring CNT, the CNT can easily slide on each other, resulting in a low E of CFs. To solve this problem, strong interaction between the tubes must be introduced. Electron beam irradiation is an effective approach to cause stable links between neighboring CNT within bundles. The mechanical properties showed a 30-fold increase in the bending modulus due to the formation of stable crosslinks that effectively eliminate sliding between the nanotubes [78].
Besides the electron-beam-induced crosslinking approach, a method based on filtration-twisting was proposed to fabricate CNT-based composite fibers [35]. The strength values for epoxy- and PVA-infiltrated fibers were increased to 0.9–1.6 and 0.7–1.3 GPa, while modules were improved to 30–50 and 20–35 GPa, respectively. The toughness of PVA-infiltrated fibers reaches 50 J g−1, far superior to commercially used high-strength fibers [35]. Further increased toughness results from combining CNTs and reduced GO flakes in solution-spun polymer fibers. The gravimetric toughness approaches 1000 J g−1, far exceeding spider dragline silk (165 J g−1) and Kevlar (78 J g−1) [79].
Apart from PVA or epoxy, super-strong CFs with tensile strength up to GPa scale were also fabricated inspired by the molecular mechanics of mussel adhesive formation (Fig. 14a, b). The CFs were spun from the CNT forest (Fig. 14c, d). Treated with twisting, infiltrating the adhesive polymer poly(ethylenimine) catechol (PEI-C), and solvent evaporation, the strong and densified fibers (Fig. 14e, f) were prepared. The PEI-C-infiltrated CFs (PEI-C-CNT) exhibited 65% increase in σ from 0.55 to 0.91 GPa compared with the pure fibers. After crosslinking at 120 °C for 2 h, σ and E of the fibers increased to 2.2 GP and 120 GPa, respectively (Fig. 14g). Besides the heat-induced crosslinking, the Fe-catechol coordination and Fe-induced oxidative crosslinking chemistry further enhanced σ to 2.5 GPa and toughness of 32.5 MJ m−3 (Fig. 14h) [80].
4.2 Mechanical Properties of Graphene Fibers
The first GFs show a σ of ca. 140 MPa with breakage elongation of 5.8%, but has good flexibility to make tight knots [46]. Compared to the intrinsic nature of graphene (σ, 130 GPa, E, 1.1 TPa) [81–83], a plenty of work should be done to improve the mechanical performance of GFs. Based on the subsequent study of GFs, the mechanical performance can be enhanced from three aspects: (1) improving the alignment of graphene sheets along the fiber axis; (2) decreasing the structural defects that include sheets boundaries, voids and impurities; and (3) enhancing the interlayer interaction of the constituent graphene sheets by either covalent or noncovalent bonds [84, 85]. The stretching operation leads to a high alignment of GO sheets and benefit for the formation of compact structures [86]. When draw ratios were increased from 1.09 to 1.45, the σ is raised from 124 to 214 MPa and E reaches 47 from 14 GPa. To decreasing the structural defects, large-sized GO were used as building block [49, 55, 86, 87]. As a result, the improved σ ranged from 214 to 501 MPa. To enhance the interlayer interaction, PVA [61], HPG [59], PAN [57], PGMA [58], and SA [62] were introduced into interlayer galleries. The resultant fibers exhibited σ of 199, 652, 452, and 500 MPa, E of 17.1, 20.9, 8.31, and 18.8 GPa, respectively (as shown in Table 1).
High-temperature graphitization process is a more effective method to achieve high-performance GFs since the structural defects were removed or restored. The σ break through 1 GPa for the first time. In 2015, Lian’s group improved the mechanical performance of GFs to 1.15 GPa by combining the large-sized graphene with small-sized graphene, aided by flowing-stretching and high-temperature graphitization treatment [88]. Recently, Xu et al. raised this value to 2.2 GPa through a full-scale synergetic defect engineering method to minimize the possible defects at all levels ranging from atomic to macroscale, the best mechanical performance until now [89–91].
5 Concluding Remarks and Prospects
Many methods are developed to assemble CNTs and graphene into macroscopic fibers. For CNT fibers, on account of the entanglement nature between individual nanotubes, the approach of drawing CNT out from superaligned CNT arrays or aerogels is promising in achieved continuous, high-strength and high-electrical-conductive fibers. For GFs, considering the excellent dispersity of GO in water and organic solvent, liquid-state spinning approaches may be more competitive in the future.
Although great progress has been made to improve the mechanical performance of macroscopic CFs and GFs, a wide gap still exists considering the intrinsic properties of CNT and graphene building blocks. Until now, the σ of CFs and GFs both exceed 1 GPa, comparable to that of the universal carbon fibers. In order to improve the performance of macroscopic CFs and GFs, defects such as voids and disordered orientation should be minimized.
To further upgrade the combined performance of CFs and GFs, especially the mechanical strength and electrical conductivity, much work is waiting to be explored and more sophisticated understandings about the relationship between the structure and performance is of significant important from the viewpoints of both fundamental research and real application. On the one hand, we should establish a real-time system to monitor the structural evolution of the basic CNTs/graphene units during the fiber-forming process, which will contribute to the structure controlling of the fibers. On the other hand, the processing techniques (e.g., stretching, fining, densifying, annealing) used to enhance the performance of polymeric fibers and carbon fibers should be borrowed to optimize the fabrication process throughout.
References
S. Nardecchia, D. Carriazo, M.L. Ferrer, M.C. Gutierrez, F. Del Monte, Three dimensional macroporous architectures and aerogels built of carbon nanotubes and/or graphene: synthesis and applications. Chem. Soc. Rev. 42(2), 794–830 (2013). doi:10.1039/C2CS35353A
Z. Li, Z. Liu, H.Y. Sun, C. Gao, Superstructured assembly of nanocarbons: fullerenes, nanotubes, and graphene. Chem. Rev. 115(15), 7046–7117 (2015). doi:10.1021/acs.chemrev.5b00102
L. Liu, W. Ma, Z. Zhang, Macroscopic carbon nanotube assemblies: preparation, properties, and potential applications. Small 7(11), 1504–1520 (2011). doi:10.1002/smll.201002198
H.-P. Cong, J.-F. Chen, S.-H. Yu, Graphene-based macroscopic assemblies and architectures: an emerging material system. Chem. Soc. Rev. 43(21), 7295–7325 (2014). doi:10.1039/C4CS00181H
N. Behabtu, M.J. Green, M. Pasquali, Carbon nanotube-based neat fibers. Nano Today 3(5–6), 24–34 (2008). doi:10.1016/s1748-0132(08)70062-8
B. Vigolo, A. Penicaud, C. Coulon, C. Sauder, R. Pailler, C. Journet, P. Bernier, P. Poulin, Macroscopic fibers and ribbons of oriented carbon nanotubes. Science 290(5495), 1331–1334 (2000). doi:10.1126/science.290.5495.1331
J.N. Barisci, M. Tahhan, G.G. Wallace, S. Badaire, T. Vaugien, M. Maugey, P. Poulin, Properties of carbon nanotube fibers spun from DNA-stabilized dispersions. Adv. Funct. Mater. 14(2), 133–138 (2004). doi:10.1002/adfm.200304500
S.R. Shin, C.K. Lee, I. So, J.H. Jeon, T.M. Kang et al., DNA-wrapped single-walled carbon nanotube hybrid fibers for supercapacitors and artificial muscles. Adv. Mater. 20(3), 466–470 (2008). doi:10.1002/adma.200701102
A.B. Dalton, S. Collins, E. Munoz, J.M. Razal, V.H. Ebron, J.P. Ferraris, J.N. Coleman, B.G. Kim, R.H. Baughman, Super-tough carbon-nanotube fibres—these extraordinary composite fibres can be woven into electronic textiles. Nature 423(6941), 703 (2003). doi:10.1038/423703a
E. Munoz, A.B. Dalton, S. Collins, M. Kozlov, J. Razal et al., Multifunctional carbon nanotube composite fibers. Adv. Eng. Mater. 6(10), 801–804 (2004). doi:10.1002/adem.200400092
P. Miaudet, S. Badaire, M. Maugey, A. Derre, V. Pichot, P. Launois, P. Poulin, C. Zakri, Hot-drawing of single and multiwall carbon nanotube fibers for high toughness and alignment. Nano Lett. 5(11), 2212–2215 (2005). doi:10.1021/nl051419w
V.A. Davis, L.M. Ericson, A.N.G. Parra-Vasquez, H. Fan, Y. Wang et al., Phase behavior and rheology of SWNTs in superacids. Macromolecules 37(1), 154–160 (2004). doi:10.1021/ma0352328
P.K. Rai, R.A. Pinnick, A.N.G. Parra-Vasquez, V.A. Davis, H.K. Schmidt, R.H. Hauge, R.E. Smalley, M. Pasquali, Isotropic-nematic phase transition of single-walled carbon nanotubes in strong acids. J. Am. Chem. Soc. 128(2), 591–595 (2006). doi:10.1021/ja055847f
S.J. Zhang, I.A. Kinloch, A.H. Windle, Mesogenicity drives fractionation in lyotropic aqueous suspensions of multiwall carbon nanotubes. Nano Lett. 6(3), 568–572 (2006). doi:10.1021/nl0521322
S.J. Zhang, S. Kumar, Carbon nanotubes as liquid crystals. Small 4(9), 1270–1283 (2008). doi:10.1002/smll.200700082
S.J. Zhang, K.K.K. Koziol, I.A. Kinloch, A.H. Windle, Macroscopic fibers of well-aligned carbon nanotubes by wet spinning. Small 4(8), 1217–1222 (2008). doi:10.1002/smll.200700998
W. Zhou, J. Vavro, C. Guthy, K.I. Winey, J.E. Fischer et al., Single wall carbon nanotube fibers extruded from super-acid suspensions: preferred orientation, electrical, and thermal transport. J. Appl. Phys. 95(2), 649–655 (2004). doi:10.1063/1.1627457
L.M. Ericson, H. Fan, H.Q. Peng, V.A. Davis, W. Zhou et al., Macroscopic, neat, single-walled carbon nanotube fibers. Science 305(5689), 1447–1450 (2004). doi:10.1126/science.1101398
M.E. Kozlov, R.C. Capps, W.M. Sampson, V.H. Ebron, J.P. Ferraris, R.H. Baughman, Spinning solid and hollow polymer-free carbon nanotube fibers. Adv. Mater. 17(5), 614–617 (2005). doi:10.1002/adma.200401130
E.Y. Jang, T.J. Kang, H. Im, S.J. Baek, S. Kim, D.H. Jeong, Y.W. Park, Y.H. Kim, Macroscopic single-walled-carbon-nanotube fiber self-assembled by dip-coating method. Adv. Mater. 21(43), 4357–4361 (2009). doi:10.1002/adma.200900480
K. Jiang, Q. Li, S. Fan, Nanotechnology: spinning continuous carbon nanotube yarns. Nature 419(6909), 801 (2002). doi:10.1038/419801a
Q.W. Li, X.F. Zhang, R.F. DePaula, L.X. Zheng, Y.H. Zhao et al., Sustained growth of ultralong carbon nanotube arrays for fiber spinning. Adv. Mater. 18(23), 3160–3163 (2006). doi:10.1002/adma.200601344
X.F. Zhang, Q.W. Li, T.G. Holesinger, P.N. Arendt, J.Y. Huang et al., Ultrastrong, stiff, and lightweight carbon-nanotube fibers. Adv. Mater. 19(23), 4198–4201 (2007). doi:10.1002/adma.200700776
X.F. Zhang, Q.W. Li, Y. Tu, Y.A. Li, J.Y. Coulter et al., Strong carbon-nanotube fibers spun from long carbon-nanotube arrays. Small 3(2), 244–248 (2007). doi:10.1002/smll.200600368
Q.W. Li, Y. Li, X.F. Zhang, S.B. Chikkannanavar, Y.H. Zhao et al., Structure-dependent electrical properties of carbon nanotube fibers. Adv. Mater. 19(20), 3358–3363 (2007). doi:10.1002/adma.200602966
H.S. Peng, M. Jain, Q.W. Li, D.E. Peterson, Y.T. Zhu, Q.X. Jia, Vertically aligned pearl-like carbon nanotube arrays for fiber spinning. J. Am. Chem. Soc. 130(4), 1130–1131 (2008). doi:10.1021/ja077767c
H.W. Zhu, C.L. Xu, D.H. Wu, B.Q. Wei, R. Vajtai, P.M. Ajayan, Direct synthesis of long single-walled carbon nanotube strands. Science 296(5569), 884–886 (2002). doi:10.1126/science.1066996
Y.L. Li, I.A. Kinloch, A.H. Windle, Direct spinning of carbon nanotube fibers from chemical vapor deposition synthesis. Science 304(5668), 276–278 (2004). doi:10.1126/science.1094982
J.J. Vilatela, A.H. Windle, Yarn-like carbon nanotube fibers. Adv. Mater. 22(44), 4959–4963 (2010). doi:10.1002/adma.201002131
M. Motta, Y.L. Li, I. Kinloch, A. Windle, Mechanical properties of continuously spun fibers of carbon nanotubes. Nano Lett. 5(8), 1529–1533 (2005). doi:10.1021/nl050634+
K. Koziol, J. Vilatela, A. Moisala, M. Motta, P. Cunniff, M. Sennett, A. Windle, High-performance carbon nanotube fiber. Science 318(5858), 1892–1895 (2007). doi:10.1126/science.1147635
X.H. Zhong, Y.L. Li, Y.K. Liu, X.H. Qiao, Y. Feng et al., Continuous multilayered carbon nanotube yarns. Adv. Mater. 22(6), 692–696 (2010). doi:10.1002/adma.200902943
W.J. Ma, L.Q. Liu, R. Yang, T.H. Zhang, Z. Zhang et al., Monitoring a micromechanical process in macroscale carbon nanotube films and fibers. Adv. Mater. 21(5), 603–608 (2009). doi:10.1002/adma.200801335
J.M. Feng, R. Wang, Y.L. Li, X.H. Zhong, L. Cui, Q.J. Guo, F. Hou, One-step fabrication of high quality double-walled carbon nanotube thin films by a chemical vapor deposition process. Carbon 48(13), 3817–3824 (2010). doi:10.1016/j.carbon.2010.06.046
W.J. Ma, L.Q. Liu, Z. Zhang, R. Yang, G. Liu et al., High-strength composite fibers: realizing true potential of carbon nanotubes in polymer matrix through continuous reticulate architecture and molecular level couplings. Nano Lett. 9(8), 2855–2861 (2009). doi:10.1021/nl901035v
Y. Shang, X. He, Y. Li, L. Zhang, Z. Li et al., Super-stretchable spring-like carbon nanotube ropes. Adv. Mater. 24(21), 2896–2900 (2012). doi:10.1002/adma.201200576
Y.Y. Shang, Y.B. Li, X.D. He, L.H. Zhang, Z. Li, P.X. Li, E.Z. Shi, S.T. Wu, A.Y. Cao, Elastic carbon nanotube straight yarns embedded with helical loops. Nanoscale 5(6), 2403–2410 (2013). doi:10.1039/c3nr33633f
Y.B. Li, Y.Y. Shang, X.D. He, Q.Y. Peng, S.Y. Du et al., Overtwisted, resolvable carbon nanotube yarn entanglement as strain sensors and rotational actuators. ACS Nano 7(9), 8128–8135 (2013). doi:10.1021/nn403400c
Y.Y. Shang, Y.B. Li, X.D. He, S.Y. Du, L.H. Zhang et al., Highly twisted double-helix carbon nanotube yarns. ACS Nano 7(2), 1446–1453 (2013). doi:10.1021/nn305209h
M.D. Lima, S.L. Fang, X. Lepro, C. Lewis, R. Ovalle-Robles et al., Biscrolling nanotube sheets and functional guests into yarns. Science 331(6013), 51–55 (2011). doi:10.1126/science.1195912
L. Ci, N. Punbusayakul, J.Q. Wei, R. Vajtai, S. Talapatra, P.M. Ajayan, Multifunctional macroarchitectures of double-walled carbon nanotube fibers. Adv. Mater. 19(13), 1719–1723 (2007). doi:10.1002/adma.200602520
L.X. Zheng, X.F. Zhang, Q.W. Li, S.B. Chikkannanavar, Y. Li et al., Carbon-nanotube cotton for large-scale fibers. Adv. Mater. 19(18), 2567–2570 (2007). doi:10.1002/adma.200602648
H.H. Gommans, J.W. Alldredge, H. Tashiro, J. Park, J. Magnuson, A.G. Rinzler, Fibers of aligned single-walled carbon nanotubes: polarized Raman spectroscopy. J. Appl. Phys. 88(5), 2509–2514 (2000). doi:10.1063/1.1287128
G.T. Liu, Y.C. Zhao, K. Deng, Z. Liu, W.G. Chu et al., Highly dense and perfectly aligned single-walled carbon nanotubes fabricated by diamond wire drawing dies. Nano Lett. 8(4), 1071–1075 (2008). doi:10.1021/nl073007o
Z. Liu, K.H. Zheng, L.J. Hu, J. Liu, C.Y. Qiu et al., Surface-energy generator of single-walled carbon nanotubes and usage in a self-powered system. Adv. Mater. 22(9), 999–1003 (2010). doi:10.1002/adma.200902153
Z. Xu, C. Gao, Graphene chiral liquid crystals and macroscopic assembled fibres. Nat. Commun. 2, 571 (2011). doi:10.1038/ncomms1583
Z. Xu, C. Gao, Aqueous liquid crystals of graphene oxide. ACS Nano 5(4), 2908–2915 (2011). doi:10.1021/nn200069w
N. Behabtu, J.R. Lomeda, M.J. Green, A.L. Higginbotham, A. Sinitskii et al., Spontaneous high-concentration dispersions and liquid crystals of graphene. Nat. Nanotechnol. 5(6), 406–411 (2010). doi:10.1038/nnano.2010.86
R. Jalili, S.H. Aboutalebi, D. Esrafilzadeh, R.L. Shepherd, J. Chen et al., Scalable one-step wet-spinning of graphene fibers and yarns from liquid crystalline dispersions of graphene oxide: towards multifunctional textiles. Adv. Funct. Mater. 23(43), 5345–5354 (2013). doi:10.1002/adfm.201300765
B. Zheng, T. Huang, L. Kou, X. Zhao, K. Gopalsamy, C. Gao, Graphene fiber-based asymmetric micro-supercapacitors. J. Mater. Chem. A 2(25), 9736–9743 (2014). doi:10.1039/C4TA01868K
T.Q. Huang, B.N. Zheng, L. Kou, K. Gopalsamy, Z. Xu, C. Gao, Y.N. Meng, Z.X. Wei, Flexible high performance wet-spun graphene fiber supercapacitors. RSC Adv. 3(46), 23957–23962 (2013). doi:10.1039/c3ra44935a
H.P. Cong, X.C. Ren, P. Wang, S.H. Yu, Wet-spinning assembly of continuous, neat, and macroscopic graphene fibers. Sci. Rep. 2, 613 (2012). doi:10.1038/srep00613
J. Sun, Y. Li, Q. Peng, S. Hou, D. Zou et al., Macroscopic, flexible, high-performance graphene ribbons. ACS Nano 7(11), 10225–10232 (2013). doi:10.1021/nn404533r
Z. Xu, Y. Zhang, P. Li, C. Gao, Strong, conductive, lightweight, neat graphene aerogel fibers with aligned pores. ACS Nano 6(8), 7103–7113 (2012). doi:10.1021/nn3021772
Y. Zhao, C.C. Jiang, C.G. Hu, Z.L. Dong, J.L. Xue, Y.N. Meng, N. Zheng, P.W. Chen, L.T. Qu, Large-scale spinning assembly of neat, morphology-defined, graphene-based hollow fibers. ACS Nano 7(3), 2406–2412 (2013). doi:10.1021/nn305674a
L. Kou, T. Huang, B. Zheng, Y. Han, X. Zhao, K. Gopalsamy, H. Sun, C. Gao, Coaxial wet-spun yarn supercapacitors for high-energy density and safe wearable electronics. Nat. Commun. 5, 3754 (2014). doi:10.1038/ncomms4754
Z. Liu, Z. Xu, X.Z. Hu, C. Gao, Lyotropic liquid crystal of polyacrylonitrile-grafted graphene oxide and its assembled continuous strong nacre-mimetic fibers. Macromolecules 46(17), 6931–6941 (2013). doi:10.1021/ma400681v
X.L. Zhao, Z. Xu, B.N. Zheng, C. Gao, Macroscopic assembled, ultrastrong and H2SO4-resistant fibres of polymer-grafted graphene oxide. Sci. Rep. 3, 3164 (2013). doi:10.1038/srep03164
X.Z. Hu, Z. Xu, C. Gao, Multifunctional, supramolecular, continuous artificial nacre fibres. Sci. Rep. 2, 767 (2012). doi:10.1038/srep00767
X.Z. Hu, Z. Xu, Z. Liu, C. Gao, Liquid crystal self-templating approach to ultrastrong and tough biomimic composites. Sci. Rep. 3, 2374 (2013). doi:10.1038/srep02374
L. Kou, C. Gao, Bioinspired design and macroscopic assembly of poly(vinyl alcohol)-coated graphene into kilometers-long fibers. Nanoscale 5(10), 4370–4378 (2013). doi:10.1039/c3nr00455d
X. Hu, S. Rajendran, Y. Yao, Z. Liu, K. Gopalsamy, L. Peng, C. Gao, A novel wet-spinning method of manufacturing continuous bio-inspired composites based on graphene oxide and sodium alginate. Nano Res. 9(3), 735–744 (2016). doi:10.1007/s12274-015-0952-2
Z. Xu, Z. Liu, H.Y. Sun, C. Gao, Highly electrically conductive Ag-doped graphene fibers as stretchable conductors. Adv. Mater. 25(23), 3249–3253 (2013). doi:10.1002/adma.201300774
K. Gopalsamy, Z. Xu, B. Zheng, T. Huang, L. Kou, X. Zhao, C. Gao, Bismuth oxide nanotubes-graphene fiber-based flexible supercapacitors. Nanoscale 6(15), 8595–8600 (2014). doi:10.1039/C4NR02615B
B. Fang, L. Peng, Z. Xu, C. Gao, Wet-spinning of continuous montmorillonite-graphene fibers for fire-resistant lightweight conductors. ACS Nano 9(5), 5214–5222 (2015). doi:10.1021/acsnano.5b00616
Z.L. Dong, C.C. Jiang, H.H. Cheng, Y. Zhao, G.Q. Shi, L. Jiang, L.T. Qu, Facile fabrication of light, flexible and multifunctional graphene fibers. Adv. Mater. 24(14), 1856–1861 (2012). doi:10.1002/adma.201200170
H.H. Cheng, Z.L. Dong, C.G. Hu, Y. Zhao, Y. Hu, L.T. Qu, N. Chena, L.M. Dai, Textile electrodes woven by carbon nanotube-graphene hybrid fibers for flexible electrochemical capacitors. Nanoscale 5(8), 3428–3434 (2013). doi:10.1039/c3nr00320e
J. Li, J. Li, L. Li, M. Yu, H. Ma, B. Zhang, Flexible graphene fibers prepared by chemical reduction-induced self-assembly. J. Mater. Chem. A 2(18), 6359–6362 (2014). doi:10.1039/C4TA00431K
E.Y. Jang, J. Carretero-Gonzalez, A. Choi, W.J. Kim, M.E. Kozlov et al., Fibers of reduced graphene oxide nanoribbons. Nanotechnology 23(23), 235601–235608 (2012). doi:10.1088/0957-4484/23/23/235601
X.M. Li, T.S. Zhao, K.L. Wang, Y. Yang, J.Q. Wei, F.Y. Kang, D.H. Wu, H.W. Zhu, Directly drawing self-assembled, porous, and monolithic graphene fiber from chemical vapor deposition grown graphene film and its electrochemical properties. Langmuir 27(19), 12164–12171 (2011). doi:10.1021/la202380g
X.M. Li, T.S. Zhao, Q. Chen, P.X. Li, K.L. Wang et al., Flexible all solid-state supercapacitors based on chemical vapor deposition derived graphene fibers. Phys. Chem. Chem. Phys. 15(41), 17752–17757 (2013). doi:10.1039/c3cp52908h
D.D. Nguyen, S. Suzuki, S. Kato, B.D. To, C.C. Hsu, H. Murata, E. Rokuta, N.-H. Tai, M. Yoshimura, Macroscopic, freestanding, and tubular graphene architectures fabricated via thermal annealing. ACS Nano 9(3), 3206–3214 (2015). doi:10.1021/acsnano.5b00292
M. Xiao, T. Kong, W. Wang, Q. Song, D. Zhang, Q. Ma, G. Cheng, Interconnected graphene networks with uniform geometry for flexible conductors. Adv. Funct. Mater. 25(39), 6165–6172 (2015). doi:10.1002/adfm.201502966
X. Shao, A. Srinivasan, Y. Zhao, A. Khursheed, A few-layer graphene ring-cathode field emitter for focused electron/ion beam applications. Carbon 110, 378–383 (2016). doi:10.1016/j.carbon.2016.09.048
M. Naraghi, T. Filleter, A. Moravsky, M. Locascio, R.O. Loutfy, H.D. Espinosa, A multiscale study of high performance double-walled nanotube-polymer fibers. ACS Nano 4(11), 6463–6476 (2010). doi:10.1021/nn101404u
L.X. Zheng, G.Z. Sun, Z.Y. Zhan, Tuning array morphology for high-strength carbon-nanotube fibers. Small 6(1), 132–137 (2010). doi:10.1002/smll.200900954
L. Kai, S. Yinghui, Z. Ruifeng, Z. Hanyu, W. Jiaping, L. Liang, F. Shoushan, J. Kaili, Carbon nanotube yarns with high tensile strength made by a twisting and shrinking method. Nanotechnology 21(4), 045708 (2010). doi:10.1088/0957-4484/21/4/045708
A. Kis, G. Csanyi, J.P. Salvetat, T.-N. Lee, E. Couteau, A.J. Kulik, W. Benoit, J. Brugger, L. Forro, Reinforcement of single-walled carbon nanotube bundles by intertube bridging. Nat. Mater. 3(3), 153–157 (2004). doi:10.1038/nmat1076
M.K. Shin, B. Lee, S.H. Kim, J.A. Lee, G.M. Spinks et al., Synergistic toughening of composite fibres by self-alignment of reduced graphene oxide and carbon nanotubes. Nat. Commun. 3, 650 (2012). doi:10.1038/ncomms1661
S. Ryu, Y. Lee, J.W. Hwang, S. Hong, C. Kim, T.G. Park, H. Lee, S.H. Hong, High-strength carbon nanotube fibers fabricated by infiltration and curing of mussel-inspired catecholamine polymer. Adv. Mater. 23(17), 1971–1975 (2011). doi:10.1002/adma.201004228
K.S. Novoselov, A.K. Geim, S.V. Morozov, D. Jiang, Y. Zhang, S.V. Dubonos, I.V. Grigorieva, A.A. Firsov, Electric field effect in atomically thin carbon films. Science 306(5696), 666–669 (2004). doi:10.1126/science.1102896
A.K. Geim, Graphene: status and prospects. Science 324(5934), 1530–1534 (2009). doi:10.1126/science.1158877
M.J. Allen, V.C. Tung, R.B. Kaner, Honeycomb carbon: a review of graphene. Chem. Rev. 110(1), 132–145 (2010). doi:10.1021/cr900070d
Z. Xu, C. Gao, Graphene fiber: a new trend in carbon fibers. Mater. Today 18(9), 480–492 (2015). doi:10.1016/j.mattod.2015.06.009
L. Chen, Y. He, S. Chai, H. Qiang, F. Chen, Q. Fu, Toward high performance graphene fibers. Nanoscale 5(13), 5809–5815 (2013). doi:10.1039/C3NR01083J
C. Xiang, C.C. Young, X. Wang, Z. Yan, C.-C. Hwang et al., Large flake graphene oxide fibers with unconventional 100% knot efficiency and highly aligned small flake graphene oxide fibers. Adv. Mater. 25(33), 4592–4597 (2013). doi:10.1002/adma.201301065
Z. Xu, H. Sun, X. Zhao, C. Gao, Ultrastrong fibers assembled from giant graphene oxide sheets. Adv. Mater. 25(2), 188–193 (2013). doi:10.1002/adma.201203448
G. Xin, T. Yao, H. Sun, S.M. Scott, D. Shao, G. Wang, J. Lian, Highly thermally conductive and mechanically strong graphene fibers. Science 349(6252), 1083–1087 (2015). doi:10.1126/science.aaa6502
Z. Xu, Y. Liu, X. Zhao, L. Peng, H. Sun et al., Ultrastiff and strong graphene fibers via full-scale synergetic defect engineering. Adv. Mater. 28(30), 6449–6456 (2016). doi:10.1002/adma.201506426
Y. Liu, Z. Xu, J. Zhan, P. Li, C. Gao, Superb electrically conductive graphene fibers via doping strategy. Adv. Mater. 28(36), 7941–7947 (2016). doi:10.1002/adma.201602444
Y. Liu, Z. Xu, W. Gao, Z. Cheng, C. Gao, Graphene and other 2D colloids: liquid crystals and macroscopic fibers. Adv. Mater. 29(14), 1606794 (2017). doi:10.1002/adma.201606794
B. Vigolo, P. Poulin, M. Lucas, P. Launois, P. Bernier, Improved structure and properties of single-wall carbon nanotube spun fibers. Appl. Phys. Lett. 81(7), 1210–1212 (2002). doi:10.1063/1.1497706
W. Neri, M. Maugey, P. Miaudet, A. Derre, C. Zakri, P. Poulin, Surfactant-free spinning of composite carbon nanotube fibers. Macromol. Rapid Commun. 27(13), 1035–1038 (2006). doi:10.1002/marc.200600150
N. Behabtu, C.C. Young, D.E. Tsentalovich, O. Kleinerman, X. Wang et al., Strong, light, multifunctional fibers of carbon nanotubes with ultrahigh conductivity. Science 339(6116), 182–186 (2013). doi:10.1126/science.1228061
J.N. Wang, X.G. Luo, T. Wu, Y. Chen, High-strength carbon nanotube fibre-like ribbon with high ductility and high electrical conductivity. Nat. Commun. 5, 3848 (2014). doi:10.1038/ncomms4848
B. Alemán, V. Reguero, B. Mas, J.J. Vilatela, Strong carbon nanotube fibers by drawing inspiration from polymer fiber spinning. ACS Nano 9(7), 7392–7398 (2015). doi:10.1021/acsnano.5b02408
J. Di, S. Fang, F.A. Moura, D.S. Galvão, J. Bykova et al., Strong, twist-stable carbon nanotube yarns and muscles by tension annealing at extreme temperatures. Adv. Mater. 28(31), 6598–6605 (2016). doi:10.1002/adma.201600628
Y. Shang, Y. Wang, S. Li, C. Hua, M. Zou, A. Cao, High-strength carbon nanotube fibers by twist-induced self-strengthening. Carbon 119, 47–55 (2017). doi:10.1016/j.carbon.2017.03.101
Acknowledgements
This work is supported by the National Natural Science Foundation of China (Nos. 21325417, 51533008), the MOST National Key Research and Development Plan (2016YFA0200200), the National Postdoctoral Program for Innovative Talents (No. BX201700209), and the State Key Laboratory for Modification of Chemical Fibers and Polymer Materials, Donghua University (No. LK1403).
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Kou, L., Liu, Y., Zhang, C. et al. A Mini Review on Nanocarbon-Based 1D Macroscopic Fibers: Assembly Strategies and Mechanical Properties. Nano-Micro Lett. 9, 51 (2017). https://doi.org/10.1007/s40820-017-0151-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s40820-017-0151-7