# Dynamic simulation of the effect of time-dependent variation of pH on response variable of the tailing thickener of coal washing plant

- 63 Downloads

## Abstract

Dynamic simulation approach can be used for understanding the nonlinear behavior in mineral processing circuits. In this study, the gel point, the main parameters of batch flux density function and the main parameters of effective solid stress were determined at different conditions (pH, flocculant dosage and particle size). Therefore, the main parameters of phenomenological model of sedimentation and thickening were determined as a function of particle size, pH and flocculant dosages using the result of experimental tests and Curve expert professional software. Then, the dynamic simulation was carried out for the industrial thickener of coal washing plant and the time-dependent variation of response variables was investigated by time-dependent variation of pH of input feed to thickener using the obtained equations. It was observed that it is possible to predict the thickener behavior as a function of time for time dependent variation of pH of input feed to the thickener of coal washing plant using obtained equations that it was not possible using phenomenological model of thickener alone.

## Keywords

Dynamic simulation Dewatering Ideal continuous thickener Thickener behavior Time-dependent variation of pH## 1 Introduction

In the mineral processing industries, the tailing material should be dewatered. During thickener operation, it is often desired to achieve certain amount of solid percent at the thickener underflow.

Sedimentation and thickening of flocculated suspension has attracted the attention of many researchers (Burger and Concha 1998). Many models have been developed by many researchers to simulate industrial thickeners.

Buscall and White (1987) presented the equation of effective solid stress as a function of solid volume fraction. The effective solid stress (\(\sigma_{e} (\phi )\)) represents the stress in the compression zone. The equation of effective solid stress as a function of solid volume fraction and measurement of its parameters will be presented in the next section.

Landman et al. (1988) and Landman and White (1994) developed consolidation equations in the thickener with considering equation of effective solid stress as a function of solid volume fraction, critical solid volume fraction or gel point and hindered settling. These equations can be only used for prediction of thickener behavior in the steady state condition. They concluded that the required bed height to achieve the certain amount of solid percent at the thickener underflow is a function of effective solid stress, flux density function and cross section area of the thickener.

Burger and Concha (1998), Burger et al. (1999) and Garrido et al. (2004) proposed the phenomenological model for the sedimentation and thickening process by considering several constitutive assumptions. This theory allows the incorporation of compression/consolidation effects to the thickener modeling which was unavailable previously due to the non-existence/insignificance of bed/sediment inside conventional thickeners. These researchers considered the effect of effective solid stress, solid volume fraction at the beginning of compressive zone and hindered settling for design and simulation of a continuous thickener. The previous models that were proposed by the other investigators, could consider only steady state condition but the proposed model by these researchers is a dynamic model that can simulate the thickener performance at all times.

In the recent work, Barth et al. (2016) investigated the effect of uncertainty quantification for nonlinear hyperbolic problems with several random perturbations. In this research, feed concentration exhibits stochastic variability and feed flow rate is random perturbation.

Usher and Scales (2005) developed an algorithm to predict the bed height and solid volume fraction of discharge at steady state condition from fundamental material properties include the compressive yield stress (*P*_{y}(*φ*)) and the hindered settling function (*R*(*φ*)). Required input parameters of model are *P*_{y}(*φ*), *R*(*φ*) and thickener diameter as a function of thickener height, solid density, liquid density and solid volume fraction of feed.

Usher et al. (2009) developed the suspension dewatering equations based on aggregate densification. They presented the model for measurement of size distribution of aggregates. In this model, the shape of the aggregates is spherical and medium diameter is d. Settling rates were determined for different medium diameters of aggregates. They concluded that when the aggregates decrease in size, the tortuosities around the aggregates will decrease that lead to significant net decrease in the resistance to fluid flow. Therefore, they concluded that the settling rate will increase with decrease in aggregate size and increase in the density of these aggregates.

The presented model by Usher et al. (2009), assumed the aggregates had evolved to a final densified steady state before entering the consolidation zone of the thickener. However, densification and the associated evolution of the aggregate diameter which both depend on the solids residence time can occur throughout the consolidating bed in industrial thickeners. As densification occurs throughout the consolidation zone, both the solids volume fraction within the aggregates, *φ*_{agg} and the suspension gel point, *φ*_{g}, which can affect the sludge rheological properties, increase with the decrease of the aggregate diameter. The effects of densification as it occurs throughout the consolidating bed upon the sludge rheological properties must therefore be simulated and explored (Zhang et al. 2013).

Gladman et al. (2010) investigated the validation of the presented model by Usher. They validated the model by operating a pilot column continuously and measuring the underflow solids. They confirmed that this model was the most accurate at the shortest residence times and lowest bed heights, but less accurate for longer residence times and higher beds. This was due to the changes in the dewatering properties of flocculated aggregates over time, which had not been adequately considered in the model.

Van Deventer et al. (2011) used the aggregate densification theory to predict the final equilibrium bed height by densification rate and bed compression. They also presented an equation between reduction of aggregate diameter and the thickening time. These researchers presented an equation for the densification rate, which provides the evolution of the aggregate diameters. An important parameter used in this equation is the aggregate densification rate parameter (*A*), which determines the required time to reach the final aggregate diameter in the steady state conditions. The aggregate densification rate parameter (*A*) also affects the rate of change of gel point (The solid volume fraction at the beginning of compressive zone) and the rate of change of solid volume fraction in aggregates. Therefore, in order to simulate and calculate the rheological parameters in the presence of densification, the aggregate densification rate parameter (*A*) should be considered that this parameter was not considered by Usher et al. (2009).

Zhou et al. (2014) used the residence-time distribution (RTD) and the compartment model to determine the flow regions in red mud separation thickener’s feedwells. Their results showed that the inlet feed rate and the aspect ratio of feedwells are the most important parameters that affect the residence time distribution (RTD( of feedwell. Their results also showed that the volume fraction of dead zone can reduce by 10.8% and mixing flow volume fraction can increase 6.5% under the optimal operation conditions.

Rahimi et al. (2015) investigated the effect of pH, flocculant dosage and particle size on gel point and effective solid stress parameters of coal flotation tailing. In that research, the gel point and effective solid stress was measured using different batch settling and batch centrifuge tests, respectively. The results showed that in the case of nonflocculated suspension, the gel point increased with decreasing of pH, however, in the case of flocculated suspension the gel point decreased with decreasing of pH. The gel point also increased with increasing flocculant dosage in certain pH values for the two flocculated and nonflocculated fractions. In the case of nonflocculated suspension, the gel points for two different particle sizes were equal at a certain pH value but in the case of the flocculated suspension the gel point was higher for larger particle size. Likewise, the results showed that effective solid stress decreased with increasing gel point and settling rate.

Rahimi et al. (2017) numerically simulated the pilot thickener operation of copper mine using the phenomenological model and also validated the results for continuous and discontinuous tests. The continuous tests were performed in the plexiglass pilot thickener at different feed flow rates and discharge rates and the solid volume fraction of discharge, the bed height and the time were recorded for each condition. These tests were also simulated and it was observed that there is a good agreement between the results of continuous tests and the results of dynamic simulation. Secondly, the discontinuous tests were performed in the mentioned thickener at different feed flow rates with a discharge rate of zero. The bed formation rate was determined for each condition. These tests were also simulated and it was observed that there is a good agreement between the results of discontinuous tests and the results of simulation.

It was observed that many works have been done in the field of sedimentation and thickening process and many models have been presented for prediction of thickener behavior. Many of presented models can be used for prediction of thickener behavior at the steady state conditions (Landman et al. 1988; Usher and Scales 2005). The presented model by Burger et al. (1999) is a powerful model that can be used for dynamic simulation of thickeners at all time but it is not possible to simulate the time dependent variation of input pulp properties such as pH and flocculant dosage, time dependent variation of ore properties such as particle size of input feed to thickener using this model. In this paper, main parameters of proposed model by Burger et al. (such as gel point, batch flux density function and effective solid stress) are determined as a function of pH, flocculant dosage and particle size of input feed to thickener. Therefore, it is possible to simulate the behavior of industrial thickener for time-dependent variation of pH, flocculant dosage and particle size of input to thickener using obtained equations. The purpose of this research is dynamic simulation of the effect of time-dependent variation of pH on response variable (solid volume fraction of discharge and bed height) of the tailing thickener of coal washing plant that has not been investigated by the other investigators.

## 2 Phenomenological model of thickening and discretization

### 2.1 Phenomenological model of sedimentation and thickening

*φ*) in the thickener as a function of height 0 ≤

*z*≤

*L*and time 0 ≤

*t*≤

*T*:

*φ*is the solid volume fraction, z is the thickener height, ∆

*ρ*is the solid–fluid density difference and g is acceleration of gravity. In the Eq. (1), we have:

*Q*

_{D}is the volumetric discharge rate and

*S*is the cross-sectional area of the thickener.

*f*

_{bk}(

*φ*) is the batch flux density function. (

*f*

_{bk}(

*φ*) < 0). It is usually assumed that

*f*

_{bk}(

*φ*) = 0 for

*φ*= 0 and

*φ*= 1 and

*f*

_{bk}(

*φ*) < 0 for 0 <

*φ*< 1. A typical semi-empirical constitutive equation is given by the Richardson and Zaki (1954):

*a*and

*b*are the constant parameters that are obtained using experimental tests and

*u*

_{∞}represents the settling velocity of a single particle in unbounded fluid. For a particle of small diameter d, the velocity

*u*

_{∞}is usually assumed to be given by the Stokes formula.

*ρ*is the solid–fluid density difference,

*g*is acceleration of gravity and

*µ*

_{f}is the dynamic viscosity of the pure fluid.

*σ*

_{e}(

*φ*) is the effective solid stress and

*φ*

_{c}is the critical solid volume fraction or gel point. The critical solid volume fraction (

*φ*

_{c}) or gel point is the solid volume fraction at the beginning of the compression zone and is the lowest volume fraction that flocs begin to touch each other. By increasing the pressure, the solid volume fraction increases. The effective solid stress (

*σ*

_{e}(

*φ*)) which represents the stress in the compression zone is the stress which must be exceeded by an applied stress before the consolidation will occur. Buscall and White (1987) suggested that the effective solid stress,

*σ*

_{e}(

*φ*), is a function of the solid volume fraction,

*φ*, and can be obtained through using Eq. (5):

*σ*

_{0}and n are the constant parameters that are obtained using experimental tests and

*φ*

_{c}is the critical solid volume fraction or gel point. Equation (1) is a second order quasilinear parabolic partial differential equation degenerating into first order hyperbolic type for the interval of solution values [0,

*φ*

_{c}]. Equation (1) does not have an analytical solution, but can be solved numerically using a finite difference method. The following initial conditions for solving degenerate parabolic partial differential equation (PDE) should be determined:

*z*= 0 and

*z*=

*L*for solving the degenerate parabolic partial differential equation (PDE) are as follows:

*Q*

_{F}is the feed flow rate,

*φ*

_{F}is the solid volume fraction of the thickener feed and

*Q*

_{D}is the volumetric discharge rate

### 2.2 Discretization

*x*=

*L*/

*J*and ∆

*t*=

*T*/

*N*, where

*J*and

*N*are integers representing the number of cells and number of time-steps respectively. Let \(\varphi_{j}^{n}\) denote the approximate value of

*φ*at (

*x*

_{j},

*t*

_{n}) where

*x*

_{j}=

*j*∆

*x*,

*t*

_{n}=

*n*∆

*t*. With assuming initial conditions \(\varphi_{j}^{0}\) for

*j*= 0,1,2,…,

*J*, the discretized Eq. (1) is as follows:

*j*= 0) and feed (

*j*=

*J*) are given as follows:

## 3 Materials and methods

### 3.1 Material

The representative sample was obtained from the thickener feed (flotation tailing) of Tabas coal washing plant in south Khorasan province of Iran. Chemical and mineralogical analyses were performed by X-ray fluorescence (XRF) spectrometry and X-ray diffraction (XRD). According to these results, the main minerals of the sample are: Kaolinite, Quartz, Illite and Montmorillonite.

### 3.2 Determination of gel point, effective solid stress and batch flux density function as a function of pH, flocculant dosage and particle size

As mentioned in the Sect. 2, the effective solid stress,\(\sigma_{e} (\phi )\), is a function of the solid volume fraction, φ, and can be obtained through using Eq. (5).

Experimental methods for measurement of the parameters *σ*_{0} and n and also critical solid volume fraction (gel point) have been explained by Rahimi et al. (2015) and these parameters were determined at different conditions (pH, flocculant dosage and particle size).

*σ*

_{0}, n and critical solid volume fraction (

*φ*

_{c}) were determined as a function of pH, flocculant dosage and particle size that are as follows:

As mentioned in the Sect. 2, the batch flux density function, *f*_{bk}(*φ*), is a function of the solid volume fraction, *φ*, and can be obtained through using Eq. (2). Experimental methods for measurement of the parameters *a* and *b* have been explained by Rahimi et al. (2016a, b) and these parameters were determined at different conditions (pH, flocculant dosage and particle size).

*a*,

*b*were determined as a function of pH, flocculant dosage and particle size that are as follows:

*a*,

*b*,

*n*,

*φ*

_{c}and

*σ*

_{0}that have been measured using experimental tests and have been predicted using model for input feed to tailing thickener of coal washing plant. It can be seen that there is a good agreement between the obtained results by experimental tests and the predicted results using model. Therefore, it is possible to predict amount of parameters

*a*,

*b*,

*n*,

*φ*

_{c}and

*σ*

_{0}using Eqs. (18) to (22) for tailing of coal washing plant.

Compare of parameters, *a*, *b*, *n* and *φ*_{c} that have been measured using experimental tests and have been predicted using model for input feed to tailing thickener of coal washing plant

No. | Particle size (d | Flocculant dosage ( | pH | Parameter | Parameter | Parameter | Parameter | ||||
---|---|---|---|---|---|---|---|---|---|---|---|

Proposed by model | Actual | Proposed by model | Actual | Proposed by model | Actual | Proposed by model | Actual | ||||

1 | 0.275 | 40 | 9 | 0.299 | 0.298 | 5.77 | 5.78 | 1.075 | 1.16 | 16.78 | 18.89 |

2 | 0.275 | 40 | 6 | 0.274 | 0.273 | 5.34 | 5.51 | 1.22 | 1.18 | 20.17 | 19.87 |

3 | 0.275 | 40 | 2 | 0.24 | 0.241 | 4.76 | 4.01 | 1.43 | 1.46 | 25.09 | 24.2 |

4 | 0.275 | 20 | 9 | 0.223 | 0.231 | 3.8 | 3.78 | 1.27 | 1.2 | 25.96 | 23.55 |

5 | 0.275 | 20 | 6 | 0.2135 | 0.215 | 3.62 | 3.4 | 1.34 | 1.29 | 27.1 | 29 |

6 | 0.275 | 20 | 2 | 0.198 | 0.192 | 3.38 | 2.8 | 1.43 | 1.44 | 28.9 | 29 |

7 | 0.275 | 0 | 9 | 0.131 | 0.128 | 1.84 | 1.81 | 1.57 | 1.6 | 59.21 | 61 |

8 | 0.275 | 0 | 6 | 0.137 | 0.137 | 1.91 | 2.12 | 1.55 | 1.6 | 57.98 | 56 |

9 | 0.275 | 0 | 2 | 0.142 | 0.145 | 2 | 2.23 | 1.51 | 1.5 | 56.59 | 54.5 |

10 | 0.125 | 40 | 9 | 0.231 | 0.224 | 3.43 | 3.23 | 1.01 | 1 | 23.34 | 22 |

11 | 0.125 | 40 | 6 | 0.208 | 0.207 | 3.1 | 3.1 | 1.05 | 1 | 24.2 | 24 |

12 | 0.125 | 40 | 2 | 0.176 | 0.187 | 2.73 | 2.76 | 1.095 | 1.1 | 25.73 | 25.8 |

13 | 0.125 | 20 | 9 | 0.19 | 0.207 | 2.72 | 3.086 | 0.98 | 1 | 28.72 | 24.2 |

14 | 0.125 | 20 | 6 | 0.18 | 0.175 | 2.61 | 2.73 | 0.995 | 1.12 | 28.9 | 27 |

15 | 0.125 | 20 | 2 | 0.165 | 0.159 | 2.45 | 2.36 | 1 | 1 | 29 | 34 |

16 | 0.125 | 0 | 9 | 0.131 | 0.123 | 2 | 1.77 | 1.03 | 1 | 58.37 | 61.9 |

17 | 0.125 | 0 | 6 | 0.136 | 0.136 | 2.1 | 2.11 | 1.02 | 1 | 57.1 | 58.21 |

18 | 0.125 | 0 | 2 | 0.14 | 0.142 | 2.17 | 2.17 | 1.01 | 1 | 55.5 | 52 |

## 4 Results and discussion

In this section, dynamic simulation of time dependent variation of pH for input feed to the thickener of coal washing plant is investigated. As mentioned before, Mathematical model of sedimentation and thickening [Eq. (1)] is complicated and does not have an analytical solution, but can be solved numerically using the finite difference method.

### 4.1 Constant particle size: d_{80} = 275 µm, constant flocculant dosage: F = 40 g/t, First pH 9 and then pH 2

Properties proposed to solve the model

Parameters | Conditions | Amount |
---|---|---|

Solid volume fraction of the thickener feed (φ | All conditions | 0.027 |

Feed flow rate (m | All conditions | 0.4651 |

Flow rate of thickener underflow (m | All conditions | 0.0358 |

Solid–fluid density difference (∆ρ) (kg/m | All conditions | 650 |

Acceleration of gravity (g) (m/s | All conditions | 9.81 |

_{80}= 275 µm,

*F*= 40 g/t). The time-dependent variation of pH of input feed to thickener is as follows:

As shown in the Figs. 1a and 2, with starting the thickening process, the pH value is 9 and solid volume fraction of thickener underflow and bed height increase with time. At *t* = 3600 s, the solid volume fraction of discharge and bed height are 0.263 and 1 m respectively and at *t* = 30000 s, the solid volume fraction of discharge and bed height are 0.3175 and 1.7 m respectively. At *t* = 30000 s, amount of pH decreases from 9 to 2. With decreasing of pH value from 9 to 2, from *t* = 30000 s until *t* = 32660 s, the bed height is constant and solid volume fraction of discharge decreases from 0.3175 to 0.255.

From *t* = 32660 s, the bed height begin to increase slightly and solid volume fraction of discharge still decreases. It can be seen from Figs. 1b and 2 that with decreasing of pH from pH 9 to 2 and after 35760 s, solid volume fraction of discharge decreases from 0.3175 to 0.23 and bed height increases from 1.7 to 1.8. The time from *t* = 30000 s until *t* = 35760 s is transition period that pulp with the pH 9 and pulp with the pH 2 are in the thickener. After *t* = 35760 s, only the pulp with the pH 2 is in the thickener.

The reasons that the solid volume fraction of discharge decreases from 0.3175 at *t* = 30000 s to 0.236 at *t* = 35760 s by decreasing of pH from 9 to 2, are as follows.

In our previous paper, it was concluded that in a certain amount of solid volume fraction, the effective solid stress increases with decreasing the pH in the case of flocculated suspension of the thickener of coal washing plant or in the certain amount of effective solid stress (certain amount of bed height), the solid volume fraction of discharge decreases with decreasing the pH (Rahimi et al. (2015)).

Therefore, in the certain amount of effective solid stress (certain amount of bed height), the solid volume fraction of discharge at pH 9 is higher than that at pH 2. In this research, after *t* = 30000 s at pH 9, bed height is 1.7 m and solid volume fraction of discharge is 0.3175. At *t* = 30000 s, pH of flocculated suspension decreases from 9 to 2. In this bed height (1.7 m), the flocculated suspension has the solid volume fraction less than 0.3175 at pH 2. Therefore, at *t* = 30000 s and after decreasing amount of pH form 9 to 2, the solid volume fraction of discharge decreases and the bed height, first is constant and then increases slightly with increasing the time.

_{80}= 275 µm,

*F*= 40 g/t and constant pH 2 for all times. Other parameters are as the same as the parameters of Table 2.

It can be seen from Fig. 3 that when the amount of pH is constant and is equal 2, at *t* = 13000 s, the solid volume fraction of discharge and bed height are 0.236 and 1.8 m, respectively. Therefore, it can be seen from the Figs. 1b and 2 that bed height increases slightly from 1.7 to 1.8 m and the solid volume fraction of discharge decreases with increasing the time to reach the solid volume fraction equivalent of bed height 1.8 m and at *t* = 35760 s, the solid volume fraction of discharge is 0.236 that is solid volume fraction equivalent of bed height 1.8 m.

It can be seen form Figs. 1c and 2 that after *t* = 35760 s, the solid volume fraction of discharge and bed height increase with increasing the time and at *t* = 158000 s, the solid volume fraction of discharge and bed height are 0.3 and 3.4 m, respectively. With comparing the Figs. 1c and 3, it can be concluded that when the amount of pH is 2 and is constant for all time, the solid volume fraction of discharge and bed height are 0.3 and 3.4 m respectively, at *t* = 135000 s. When the amount of pH is 9 and then decrease to 2, the solid volume fraction of discharge and bed height are 0.3 and 3.4 m respectively, at *t* = 158000 s. Therefore, when the amount of pH is 2 and is constant for all time, the time to reach the mentioned conditions is less than when the amount of pH is 9 and then decrease to 2.

### 4.2 Constant particle size: d_{80} = 275 µm, Constant flocculant dosage: *F* = 40 g/t, First pH 2 and then pH 9

The parameters which were used for simulation, have been shown in Table 2.

As shown in the Figs. 4 and 5, with starting the thickening process, the pH value is 2 and solid volume fraction of thickener underflow and bed height increase with time. At *t* = 7200 s, the solid volume fraction of discharge and bed height are 0.215 and 1.4 m respectively and at *t* = 27000 s, the solid volume fraction of discharge and bed height are 0.256 and 2.2 m respectively. At *t* = 27000 s, amount of pH increases from 2 to 9. With increasing of pH value from 2 to 9, the bed height does not change and is constant but solid volume fraction of discharge will increase from 0.256 at high speed and pulp will reach to steady state condition at *t* = 43000 s. The solid volume fraction of discharge is 0.35 at this time.

It was mentioned in the previous section that in a certain amount of solid volume fraction, the effective solid stress increases with decreasing the pH in the case of flocculated suspension of the thickener of coal washing plant or in the certain amount of effective solid stress (certain amount of bed height), the solid volume fraction of discharge decreases with decreasing the pH (Rahimi et al. (2015)).

Therefore, in the certain amount of effective solid stress or bed height, the solid volume fraction of discharge at pH 9 is higher than that at pH 2. In this research, after *t* = 27000 s at pH 2, the bed height is 2.2 m and solid volume fraction of discharge is 0.256. At *t* = 27000 s the pH of flocculated suspension increases from 2 to 9. In this bed height (2.2 m), the flocculated suspension has the solid volume fraction more than 0.256 at pH 9. Therefore, at *t* = 27000 s and after increasing the amount of pH form 2 to 9, the bed height is constant and solid volume fraction of discharge will increase at high speed with increasing the time to reach the solid volume fraction equivalent of bed height 2.2 m at pH 9.

_{80}= 275 µm,

*F*= 40 g/t and constant amount of pH 9 for all times. Other parameters are as the same as the parameters of Table 2.

It can be seen from Fig. 6 that when the amount of pH is constant and is equal 9, at *t* = 135000 s, the pulp will reach to steady state condition and the solid volume fraction of discharge and the bed height are 0.35 and 2.2 m, respectively, at this time. After *t* = 135000 s, the solid volume fraction of discharge and the bed height are constant and do not change.

With comparing the Figs. 4 and 6, it can be concluded that when the amount of pH is 9 and it is constant for all time, the solid volume fraction of discharge and bed height are 0.35 and 2.2 m respectively, at *t* = 135000 s. When the amount of pH is 2 and then increase to 9, the solid volume fraction of discharge and bed height are 0.35 and 2.2 m respectively, at *t* = 43000 s. Therefore, when the amount of pH is 9 and is constant for all time, the time to reach the mentioned conditions is higher than when the amount of pH is 2 and then increase to 9.

## 5 Conclusion

- (1)
The main parameters of phenomenological model of thickener (gel point, effective solid stress, batch flux density function) were determined as a function of particle size, pH and flocculant dosage of input feed to the thickener of coal washing plant using the results of experimental tests and Curve expert professional software. There is a good agreement between the obtained results by experimental tests and the predicted results using model. Therefore, it is possible to predict gel point, effective solid stress and batch flux density function using Eqs. (18–22) for tailing of coal washing plant.

- (2)
It is possible to predict the thickener behavior as a function of time for time dependent variation of pH, flocculant dosage and particle size of input feed to the thickener of coal washing plant using obtained equations that it was not possible using phenomenological model of thickener alone.

- (3)
The dynamic simulation was carried out for the industrial thickener of coal washing plant and the time-dependent variation of response variables (solid volume fraction of discharge and bed height) was investigated by time-dependent variation of pH of input feed to thickener using the obtained equations.

## References

- Barth A, Burger R, Kroker I, Rohde C (2016) Computational uncertainty quantification for a clarifier-thickener model with several random perturbations: a hybrid stochastic Galerkin approach. Comput Chem Eng 89:11–26CrossRefGoogle Scholar
- Burger R, Concha F (1998) Mathematical model and numerical simulation of the settling of flocculated suspensions. Int J Multiphase Flow 24:1005–1023CrossRefGoogle Scholar
- Burger R, Bustos MC, Concha F (1999) Settling velocities of particulate systems: 9. Phenomenological theory of sedimentation processes: numerical simulation of the transient behavior of flocculated suspensions in an ideal batch or continuous thickener. Int J Miner Process 55:267–282CrossRefGoogle Scholar
- Buscall R, White LR (1987) The consolidation of concentrated suspensions part 1. The theory of sedimentation. J Chem SOC Faraday Trans I 83:873–891CrossRefGoogle Scholar
- Garrido P, Burgos R, Concha F, Burger R (2004) Settling velocities of particulate systems: 13. A simulator for batch and continuous sedimentation of flocculated suspensions. Int J Miner Process 73:131–144CrossRefGoogle Scholar
- Gladman BR, Rudman M, Scales PJ (2010) Experimental validation of a 1-D continuous thickening model using a pilot column. Chem Eng Sci 65:3937–3946CrossRefGoogle Scholar
- Landman KA, White LR (1994) Solid/liquid separation of flocculated suspensions. Adv Colloid Interface Sci 51:175–246CrossRefGoogle Scholar
- Landman KA, White LR, Buscall R (1988) The continuous-flow gravity thickener: steady state behavior. AIChE J 34:239–252CrossRefGoogle Scholar
- Rahimi M, Abdollahzadeh A, Rezai B (2015) The effect of particle size, pH and flocculant dosage on the gel point, effective solid stress and thickener performance of coal washing plant. Int J Coal Prep Util 35:125–142CrossRefGoogle Scholar
- Rahimi M, Abdollahzadeh A, Rezai B (2016a) Dynamic simulation of the effect of discharge rate variations on tailing thickener behavior of the coal-washing plant. Int J Coal Prep Util 36:91–108CrossRefGoogle Scholar
- Rahimi M, Abdollahzadeh A, Rezai B (2016b) Dynamic simulation of tailing thickener at the Tabas coal washing plant using the phenomenological model. Int J Miner Process 154:35–40CrossRefGoogle Scholar
- Rahimi M, Unesi M, Rezai B, Abdollahzadeh A (2017) Dynamic simulation of pilot thickener operation using phenomenological model with results validation for continuous and discontinuous tests. J Cent South Univ 24:1207–1216CrossRefGoogle Scholar
- Richardson JF, Zaki WN (1954) The sedimentation of a suspension of uniform spheres under conditions of viscous flow. Chem Eng Sci 3(2):65–73CrossRefGoogle Scholar
- Usher SP, Scales PJ (2005) Steady state thickener modeling from the compressive yield stress and hindered settling function. Chem Eng J 111:253–261CrossRefGoogle Scholar
- Usher SP, Spehar R, Scales PJ (2009) Theoretical analysis of aggregate densification: impact on thickener performance. Chem Eng J 151:202–208CrossRefGoogle Scholar
- Van Deventer BBG, Usher SP, Kumar A, Rudman M, Scales PJ (2011) Aggregate densification and batch settling. Chem Eng J 171:141–151CrossRefGoogle Scholar
- Zhang Y, Martin A, Grassia P (2013) Mathematical modeling of time-dependent densified thickeners. Chem Eng Sci 2013(99):103–111CrossRefGoogle Scholar
- Zhou T, Mao Li M, Li QL, Lei B, Chenn QZ, Zhou JM (2014) Numerical simulation of flow regions in red mud separation thickener’s feedwell by analysis of residence-time distribution. Trans Nonferrous Met Soc China 24:1117–1124CrossRefGoogle Scholar

## Copyright information

**Open Access**This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.