In Vitro Corrosion Behaviour of Ti–6Al–4V and 316L Stainless Steel Alloys for Biomedical Implant Applications
- 131 Downloads
Pulsed laser deposition technique is one of the methods to coat the hydroxyapatite on 316L stainless steel and Ti–6Al–4V implants, which is used in orthopaedics and dentistry applications. In this study, hydroxyapatite (HAP) ceramics in the form of calcium phosphate were deposited on Ti–6Al–4V and 316L stainless steel by the pulsed laser deposition method. The coated thin film was characterised by X-ray diffraction (XRD), scanning electron microscopy with energy-dispersive spectroscopy (EDS) and atomic microscopy. The corrosion studies were carried out on coated and uncoated samples using potentiodynamic polarisation studies in simulated body fluid (Hanks’ solution). The bioactivity of the Hap-coated samples on Ti–6Al–4V and 316L stainless steel was evaluated by immersing them in simulated body fluid for 9 days. XRD and EDS analyses confirmed the presence of HAP. The corrosion studies showed that the treated samples have better corrosion resistance compared to Ti–6Al–4V and 316L stainless-steel substrates. The formation of apatite on treated samples revealed the bioactivity of the HAP-coated substrates. HAP-coated Ti–6Al–4V provides higher corrosion protection than the HAP-coated 316L stainless-steel substrates.
KeywordsHydroxyapatite Pulsed laser deposition Corrosion Ti–6Al–4V 316L stainless steel
The author acknowledges the Centre for Nanoscience and Nanotechnology, SRM University for using the laboratory facilities. Author would like to thank Mr. Murali, NRC, SRM University for FESEM studies, and Mr. Bijo Joseph, Department of Physics and Nanotechnology, SRM University for XRD analysis.
- 8.Nelea V, Mihailescu IN, Jelinec M (2007) Biomaterials: new issues and breakthroughs for biomedical applications. In: Eason R (ed) Pulsed laser deposition of thin films. Wiley, New JerseyGoogle Scholar
- 25.Anandan C, Mohan L (2013) In vitro corrosion behavior and apatite growth of oxygen plasma ion implanted titanium alloy β-21S. JMEPEG. https://doi.org/10.1007/s11665-013-0628-6