Acoustic emission characterization of sliding wear under condition of direct and inverse transformations in low-temperature degradation aged Y-TZP and Y-TZP-AL2O3

  • Nikolai L. Savchenko
  • Andrey V. Filippov
  • Sergei Yu. Tarasov
  • Andrey I. Dmitriev
  • Evgeny V. Shilko
  • Aleksandr S. Grigoriev
Open Access
Research Article
  • 17 Downloads

Abstract

In this research, results of the investigation of the sliding friction and wear of yttria-stabilized tetragonal zirconia polycrystalline (Y-TZP) and Y-TZP-Al2O3 samples preliminarily subjected to low-temperature degradation are reported. The investigation was carried out using a pin-on-disk tribometer with simultaneous recording of acoustic emission (AE) and vibration acceleration. The sliding wear process was found to be determined by dynamic direct and inverse Y-TZP transformations detected by monoclinic and tetragonal X-ray diffraction peak ratios. The AE signals generated under direct and inverse transformations can be used to characterize wear and friction mechanisms as well as direct and inversed sliding-induced phase transformations. The AE signal energy grows with the friction coefficient and the inverse transformation degree. Reduction of the AE signal energy indicates establishing the mild wear stage caused by effective stress-induced direct martensitic transformation. The AE signal median frequency increases in the case of lower friction. Numerical studies of wear subsurface fracture under conditions of stress-induced martensitic transformation were used to elucidate the role played by the phase transformation in Y-TZP and Y-TZP-Al2O3. Martensitic transformation in Y-TZP was described with use of the non-associated dilatant plasticity model. Simulation results particularly show that increase in the value of dilatancy coefficient from 0 to 0.2 is accompanied by 25%−30% reduce in characteristic length and penetration depth of sliding-induced subsurface cracks. As shown the AE may be an effective tool for in-situ monitoring the subsurface wear of materials experiencing both direct and inverse transformations.

Keywords

zirconia transformation toughening low-temperature degradation friction acoustic emission numerical modeling movable cellular automata method 

Notes

Acknowledgments

The work was financially supported by the Russian Federation via the Ministry of Education and Science of the Russian Federation (Agreement No. 14.607.21.0186, project identifier RFMEFI60717X0186).

References

  1. [1]
    Turon-Vinas M, Anglada M. Strength and fracture toughness of zirconia dental ceramics. Dental Mater 34(3): 365–375 (2018)CrossRefGoogle Scholar
  2. [2]
    Deville S, Gremillard L, Chevalier J, Fantozzi G. A critical comparison of methods for the determination of the aging sensitivity in biomedical grade yttria-stabilized zirconia. J Biomed Mater Res Part B Appl Biomater 72B(2): 239–245 (2005)CrossRefGoogle Scholar
  3. [3]
    Reveron H, Fornabaio M, Palmero P, Fürderer T, Adolfsson E, Lughi V, Bonifacio A, Sergo V, Montanaro L, Chevalier J. Towards long lasting zirconia-based composites for dental implants: Transformation induced plasticity and its consequence on ceramic reliability. Acta Biomater 48: 423–432 (2017)CrossRefGoogle Scholar
  4. [4]
    Fischer E, Anderson M P, Jahanmir S. Influence of fracture toughness on the wear resistance of yttria-doped zirconium oxide. J Am Ceram Soc 72(2): 252–257 (1989)CrossRefGoogle Scholar
  5. [5]
    Lee W, Hsu S M, Shen M C. Ceramic wear maps: Zirconia. J Am Ceram Soc 76(8): 1937–1947 (1993)CrossRefGoogle Scholar
  6. [6]
    Swain V, Hannink R H J. Metastability of the martensitic transformation in a 12 mol% ceria-zirconia alloy: II, grinding studies. J Am Ceram Soc 72(8): 1358–1364 (1989)CrossRefGoogle Scholar
  7. [7]
    Korolev V, Savchenko N L, Kul’kov S N. Texture formation on the friction surface in transformation-toughened ceramics. Tech Phys Lett 30(1): 12–14 (2004)CrossRefGoogle Scholar
  8. [8]
    Becker C, Libsch T A, Rhee S K. Wear mechanisms of toughened zirconias. In Proceedings of the 9th Annual Conference on Composites and Advanced Ceramic Materials. The American Ceramic Society, 1985: 1040–1058Google Scholar
  9. [9]
    Savchenko L, Kul’kov S N. Friction and wear of Y-TZP and Y-TZP–Al2O3 ceramics in high-speed sliding on steel. J Frict Wear 30(6): 444–448 (2009)CrossRefGoogle Scholar
  10. [10]
    Wu G, Choe C Y, Lee S M, Yoo J A, Hyun C Y, Hong D P, Byeon J W. Real-time monitoring of degradation of zirconia ceramic by acoustic emission. Appl Mech Mater 433–435: 816–820 (2013)CrossRefGoogle Scholar
  11. [11]
    Hua K, Fan Y W, Jin Z M. A biotribo-acoustic testing method for ceramic orthopaedic biomaterials. Tribol Int 71: 1–6 (2014)CrossRefGoogle Scholar
  12. [12]
    Taylor S, Manley T, Sutton K. The role of stripe wear in causing acoustic emissions from alumina ceramic-on-ceramic bearings. J Arthroplasty 22(S7): 47–51 (2007)CrossRefGoogle Scholar
  13. [13]
    Wang L, Wood R J K. Acoustic emissions from lubricated hybrid contacts. Tribol Int 42(11-12): 1629–1637 (2009)CrossRefGoogle Scholar
  14. [14]
    Filippov V, Rubtsov V E, Tarasov S Y. Acoustic emission study of surface deterioration in tribocontacting. Appl Acoust 117: 106–112 (2017)CrossRefGoogle Scholar
  15. [15]
    Filippov V, Nikonov A Y, Rubtsov V E, Dmitriev A I, Tarasov S Y. Vibration and acoustic emission monitoring the stability of peakless tool turning: Experiment and modeling. J Mater Process Technol 246: 224–234 (2017).CrossRefGoogle Scholar
  16. [16]
    Filippov V, Tarasov S Y, Fortuna S V, Podgornykh O A, Shamarin N N, Rubtsov V E. Microstructural, mechanical and acoustic emission-assisted wear characterization of equal channel angular pressed (ECAP) low stacking fault energy brass. Tribol Int 123: 273–285 (2018)CrossRefGoogle Scholar
  17. [17]
    Rubtsov E, Kolubaev E A, Kolubaev A V, Popov V L. Using acoustic emission for the analysis of wear processes during sliding friction. Tech Phys Lett 39(2): 223–225 (2013)CrossRefGoogle Scholar
  18. [18]
    McBride L, Boness R J, Sobczyk M, Viner M R. Acoustics emission from lubricated and rubbing surfaces. J Acoust Emiss 8(1-2): 192–196 (1989)Google Scholar
  19. [19]
    Clarke D R, Arora A. Acoustic emission characterization of the tetragonal-monoclinic phase transformation in zirconia. In Advances in Ceramics, Vol. 12, Science and Technology of Zirconia II. Claussen N, Heuer A H, Ruhle M, Eds. Columbus, OH: American Ceramic Society, 1984.Google Scholar
  20. [20]
    Lankford J. Plastic deformation of partially stabilized zirconia. J Am Ceram Soc 66(11): c212–c213 (1983)CrossRefGoogle Scholar
  21. [21]
    Drozdov V, Galenko V O, Gogotsi G A, Swain M V. Acoustic emission during micro-and macrocrack growth in Mg-PSZ. J Am Ceram Soc 74(8): 1922–1927 (1991)CrossRefGoogle Scholar
  22. [22]
    Chu L, Ren H, Ning J. Damage and Toughening Analysis of Ceramics by AE Location Method//G. Shen et al. (eds.), Advances in Acoustic Emission Technology: Proceedings of the World Conference on Acoustic Emission-2013, Springer Proceedings in Physics 158: 313–321Google Scholar
  23. [23]
    Jacobus K, Sehitoglu H, Balzer M. Effect of stress state on the stress-induced martensitic transformation in polycrystalline Ni-Ti Alloy. Metall Mater Trans A 27(10): 3066–3073 (1996)CrossRefGoogle Scholar
  24. [24]
    Stam G T M, Van Der Giessen E, Meijers P. Effect of transformation-induced shear strains on crack growth in zirconia-containing ceramics. Int J Solids Struct 31(14): 1923–1948 (1994)CrossRefMATHGoogle Scholar
  25. [25]
    Sun P, Hwang K C. Micromechanics modelling for the constitutive behavior of polycrystalline shape memory alloys–I. Derivation of general relations. J Mech Phys Solids 41(1): 1–17 (1993)MathSciNetCrossRefMATHGoogle Scholar
  26. [26]
    Patoor E, Lagoudas C, Entchev P B, Brinson L C, Gao X J. Shape memory alloys, Part I: General properties and modeling of single crystals. Mech Mater 38(5-6): 391–429 (2006)CrossRefGoogle Scholar
  27. [27]
    Lagoudas C, Entchev P B, Popov P, Patoor E, Brinson L C, Gao X J. Shape memory alloys, Part II: Modeling of polycrystals. Mech Mater 38(5-6): 430–462 (2006)CrossRefGoogle Scholar
  28. [28]
    Lankford J, Page A, Rabenberg L. Deformation mechanisms in yttria-stabilized zirconia. J Mater Sci 23(11): 4144–4156 (1988)CrossRefGoogle Scholar
  29. [29]
    Nikolaevsky V N. Geomechanics and Fluidodynamics: with Applications to Reservoir Engineering. Dordrecht, Boston: Kluwer Academic, 1996CrossRefGoogle Scholar
  30. [30]
    Stefanov P, Chertov M A, Aidagulov G R, Myasnikov A V. Dynamics of inelastic deformation of porous rocks and formation of localized compaction zones studied by numerical modeling. J Mech Phys Solids 59(11): 2323–2340 (2011)MathSciNetCrossRefMATHGoogle Scholar
  31. [31]
    Eremin O. Numerical simulation of fracture of ZrO2-Al2O3 ceramic composites. Phys Mesomech 19(4): 452–458 (2016)CrossRefGoogle Scholar
  32. [32]
    Psakhie S, Shilko V, Smolin A, Astafurov S, Ovcharenko V E. Development of a formalism of movable cellular automaton method for numerical modeling of fracture of heterogeneous elastic-plastic materials. Fract Struct Integr 7(24): 26–59 (2013)Google Scholar
  33. [33]
    Shilko V, Psakhie S G, Schmauder S, Popov V L, Astafurov S V, Smolin A Y. Overcoming the limitations of distinct element method for multiscale modeling of materials with multimodal internal structure. Comput Mater Sci 102: 267–285 (2015)CrossRefGoogle Scholar
  34. [34]
    Psakhie G, Shilko E V, Grigoriev A S, Astafurov S V, Dimaki A V, Smolin A Y. A mathematical model of particle–particle interaction for discrete element based modeling of deformation and fracture of heterogeneous elastic–plastic materials. Eng Fract Mech 130: 96–115 (2014)CrossRefGoogle Scholar
  35. [35]
    Dmitriev I, Österle W, Wetzel B, Zhang G. Mesoscale modeling of the mechanical and tribological behavior of a polymer matrix composite based on epoxy and 6 vol.% silica nanoparticles. Comput Mater Sci 110: 204–214 (2015)CrossRefGoogle Scholar
  36. [36]
    Alejano R, Bobet A. Drucker-prager criterion. Rock Mech Rock Eng 45(6): 995–999 (2012)CrossRefGoogle Scholar
  37. [37]
    Dimaki A, Shilko V, Psakhie S, Popov V L. Simulation of fracture using a mesh-dependent fracture criterion in the discrete element method. Facta Univ Ser Mech Eng 16(1): 41–50 (2018)CrossRefGoogle Scholar
  38. [38]
    Pohrt R, Popov L. Adhesive contact simulation of elastic solids using local mesh-dependent detachment criterion in Boundary Elements Method. Facta Univ Ser Mech Eng 13(1): 3–10 (2015)Google Scholar
  39. [39]
    Popov L, Pohrt R, Li Q. Strength of adhesive contacts: Influence of contact geometry and material gradients. Friction 5(3): 308–325 (2017)CrossRefGoogle Scholar
  40. [40]
    Kelly R, Denry I. Stabilized zirconia as a structural ceramic: An overview. Dent Mater 24(3): 289–298 (2008)CrossRefGoogle Scholar

Copyright information

© The author(s) 2018

Open Access: The articles published in this journal are distributed under the terms of the Creative Commons Attribution 4.0 International License (https://doi.org/creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.

Authors and Affiliations

  • Nikolai L. Savchenko
    • 1
  • Andrey V. Filippov
    • 1
    • 2
  • Sergei Yu. Tarasov
    • 1
    • 2
  • Andrey I. Dmitriev
    • 1
    • 3
  • Evgeny V. Shilko
    • 1
    • 3
  • Aleksandr S. Grigoriev
    • 1
  1. 1.Institute of Strength Physics and Materials Science SB RASTomskRussian Federation
  2. 2.National Research Tomsk Polytechnic UniversityTomskRussian Federation
  3. 3.National Research Tomsk State UniversityTomskRussian Federation

Personalised recommendations