Machinability study of manganese alloyed austempered ductile iron

  • Ananda Hegde
  • Sathyashankara Sharma
Technical Paper
  • 68 Downloads

Abstract

Austempered ductile iron (ADI) is a heat-treated ductile cast iron with ausferrite microstructure. ADI has high strength and hardness with good ductility and toughness. However, because of the high strength and hardness of ADI, there is a concern regarding its machinability. In the present study, machinability of ADI is assessed using tool life and the surface roughness. Machining tests are conducted using Taguchi experimental design. The effects of machining parameters, heat treatment parameters, on manganese alloyed ADI in the dry turning operation are studied and it was found that austempering temperature and cutting speed have the major contributions on tool life, whereas feed rate has the major contribution on surface roughness of the material within the range of values under study. Metallographic study has revealed coarser structure at higher austempering temperature of 420° which resulted in better tool life. 0.64 wt% of manganese in the ADI has resulted in lower surface roughness value.

Keywords

Machinability Manganese ADI Austenitization Austempering 

References

  1. 1.
    Keough JR, Hayrynen KL (2003) World ADI conference on austempered ductile iron. The State of the Industry, LouisvilleGoogle Scholar
  2. 2.
    Parez MJ, Cisneros MM, Lopez HF (2006) Wear resistance of Cu–Ni–Mo austempered ductile iron. Wear 260:879–885CrossRefGoogle Scholar
  3. 3.
    Lerner YS, Kingsbury GR (1997) Wear resistance properties of austempered ductile iron. J Mater Eng Perform 7:48–52CrossRefGoogle Scholar
  4. 4.
    Olawale JO, Oluwasegun KM (2016) Austempered ductile iron (ADI): a review. Mater Perform Charact 5:289–311Google Scholar
  5. 5.
    Narasimha Murthy K, Sampathkumaran P, Seetharamu S (2009) Abrasion and erosion behaviour of manganese alloyed permanent moulded austempered ductile iron. Wear 267:1393–1398CrossRefGoogle Scholar
  6. 6.
    Barbosa PA, Costa ÉS, Guesser WL et al (2015) Comparative study of the machinability of austempered and pearlitic ductile irons in drilling process. J Braz Soc Mech Sci Eng 37:115–122CrossRefGoogle Scholar
  7. 7.
    Cemal Cakir M, Isik Yahya (2008) Investigating the machinability of austempered ductile irons having different austempering temperatures and times. Mater Des 29(5):937–939CrossRefGoogle Scholar
  8. 8.
    Ulvi Seker and Hasan Hasirci (2006) Evaluation of machinability of austempered ductile irons in terms of cutting forces and surface quality. J Mater Process Technol 173:260–268CrossRefGoogle Scholar
  9. 9.
    Klocke F, Arft M, Lung D (2010) Material-related aspects of the machinability of austempered ductile iron. Prod Eng Res Devel 4:433–441CrossRefGoogle Scholar
  10. 10.
    de Carvalho MV, Montenegro DM, de Oliveira Gomes J (2013) An analysis of the machinability of ASTM grades 2 and 3 austempered ductile iron. J Mater Process Technol 213:560–573CrossRefGoogle Scholar
  11. 11.
    Seah KHW, Sharma SC (1995) Machinability of alloyed austempered ductile iron. Int J Mach Tools Manuf 35:1475–1479CrossRefGoogle Scholar
  12. 12.
    Arft M, Klocke F (2013) 14th CIRP conference on modeling of machining operations (CIRP CMMO), vol 8, pp 129–134Google Scholar
  13. 13.
    Bayati H, Elliot R (1995) Influence of austenitising temperature on mechanical properties of high manganese alloyed ductile iron. Mater Sci Technol 11:908–913CrossRefGoogle Scholar
  14. 14.
    ASTM A897/A897M-15 (2015) Standard specification for austempered ductile iron castings. In: Annual book of ASTM standards, vol 01.02. ASTM International, West ConshohockenGoogle Scholar
  15. 15.
    ISO 3685: 1993 (E) (1993) Tool-life testing with single point toolsGoogle Scholar
  16. 16.
    Manivel D, Gandhinathan R (2016) Optimization of surface roughness and tool wear in hard turning of austempered ductile iron (grade 3) using Taguchi method. Measurement 93:108–116CrossRefGoogle Scholar
  17. 17.
    ISO 4287: 1997 Geometrical product specifications (GPS)—surface texture: profile method—terms, definitions and surface texture parametersGoogle Scholar
  18. 18.
    Junjun Cui and Liqing Chen (2015) Microstructures and mechanical properties of a wear-resistant alloyed ductile iron austempered at various temperatures. Metall Mater Trans A 46:3627–3634CrossRefGoogle Scholar
  19. 19.
    Chawla V, Batra U, Puri D, Chawla A (2008) To study the effect of austempering temperature on fracture behaviour of Ni–Mo austempered ductile iron (ADI). J Miner Mater Charact Eng 7:307–316Google Scholar
  20. 20.
    Astakhov VP (2010) Surface integrity in machining. Springer, LondonGoogle Scholar
  21. 21.
    Çelik YH, Kilickap E, Güney M (2017) Investigation of cutting parameters affecting on tool wear and surface roughness in dry turning of Ti-6Al-4 V using CVD and PVD coated tools. J Braz Soc Mech Sci Eng 39:2085–2093CrossRefGoogle Scholar

Copyright information

© The Brazilian Society of Mechanical Sciences and Engineering 2018

Authors and Affiliations

  1. 1.Department of Mechanical and Manufacturing Engineering, Manipal Institute of TechnologyManipal Academy of Higher EducationManipalIndia

Personalised recommendations