Pressure and temperature sensitivity analysis of palm fiber as a biobased reinforcement material in brake pad
- 40 Downloads
The effect of palm fiber on properties of automotive brake composite materials is analyzed. The test procedure followed is JASO C 406, which is for passenger car pads. Tribological properties of three brake pads (6 PF, 8 PF and 10 PF) were tested on full-scale inertia dynamometer for various performance parameters such as pressure–speed sensitivity (effectiveness studies) and Temperature sensitivity (fade and recovery behaviour). A pad undergoes all the testing parameters and maintains its low temperature rise in the disc for three pressure sensitivity and two temperature sensitivity tests. By increasing palm fiber content, hardness, heat swell and specific gravity increases, and also porosity and loss on ignition decreases. Test has been conducted using scanning electron microscope to analyse the all three specimens to evaluate the contact plateaus and wear debris during braking. 8% of palm fiber content in brake pad was found to be superior to 6 PF and 10 PF in most of the important tribological properties.
KeywordsPalm fiber Brake pad Pressure sensitivity Fade and recovery Friction
We thank Central Institute of Plastics and Technology (CIPET), Chennai for helping us doing in SEM analysis and also we thank Sai Friction (Brake Pad manufacturers) Chennai, for supporting to manufacture brake pads.
- 2.Ruzaidi CM, Kamarudin H, Shamsul JB, Mustafa Al Bakri AM, Rafiza AR (2011) Comparative study of thermal, compressive, and wear properties of palm slag brake pad composites with other fillers. Aust J Basic Appl Sci 5:790–796. https://doi.org/10.4028/www.scientific.net/AMR.328-330.1636 Google Scholar
- 12.Thiyagarajan V, Kalaichelvan K, Vijay R, Lenin Singaravelu D (2015) Influence of thermal conductivity and thermal stability on the fade and recovery characteristics of non–asbestos semi–metallic disc brake pad. J Braz Soc Mech Sci Eng 38:1207. https://doi.org/10.1007/s40430-015-0448-8 CrossRefGoogle Scholar
- 25.Avital Gabriel de Almeida Rosa, Jéferson Aparecido Moreto, Marcos Dorigão Manfrinato, Luciana Sgarbi Rossino (2014) Study on friction and wear behavior of SAE 1045 steel, reinforced nylon 6.6 and NBR rubber used in clutch disks. Mater Sci. 17:1397–1403. https://doi.org/10.1590/1516-1439.282714