Slag characterisation of 308L-type stainless steel rutile flux-cored wires
- 16 Downloads
The behaviour of the weld characteristic of flux-cored wires is strongly influenced by the flux. The weld metal and weldability are determined by the flux composition and to a much smaller level by shielding gas used as well. The wide variety of components combined with the complexity of the welding process result in intricate mechanisms occurring in the slag. The slags of the different rutile flux-cored wires, designed for either position or standard downhand welding, were analysed in order to gain knowledge about the complex slag mechanisms and to carry out a metallurgical characterisation. Chemical analysis, differential thermal analysis and microstructural investigations of the slags were conducted to identify and characterise the formed phases. In addition, the viscosities of the slags were measured and correlated with the DTA results.
KeywordsSlag characterisation Flux-cored wires DTA HT-LSCM Viscosity
The authors gratefully acknowledge financial support from the K1-MET GmbH Metallurgical Competence Centre. The research program of the K1-MET Competence Centre is supported by COMET (Competence Centre for Excellent Technologies), the Austrian program for competence centres. COMET is funded by the Federal Ministry for Transport, Innovation, and Technology, the Federal Ministry for Science, Research and Economy, the provinces of Upper Austria, Tyrol, and Styria as well as the Styrian Business Promotion Agency (SFG).
- 1.Strassburg F W, Wehner H, Schweißen nichtrostender Stähle, 4., überarb. u. erw. Aufl., DVS-Vlg, Düsseldorf, 2008Google Scholar
- 2.Mills KC, Yuan L, Jones RT (2011) Estimating the physical properties of slags. J South Afr Inst Min Metall 111(10):649–658Google Scholar
- 3.Verein Deutscher Eisenhüttenleute (VDEh) (1995) Slag atlas, 2nd edn. Verlag Stahleisen, DüsseldorfGoogle Scholar
- 4.Mysen BO (1988) Structure and properties of silicate melts. Elsevier, AmsterdamGoogle Scholar
- 6.ISO 11357-2 (2013) Plastics – differential scanning calorimetry – part 2: determination of glass transition temperature. https://www.iso.org/standard/57966.html
- 7.Verein Deutscher Eisenhüttenleute (VDEh), Ausschuss für Metallurgische Grundlagen (1981) Slag atlas. Verlag Stahleisen, DüsseldorfGoogle Scholar
- 9.Kekkonen M, Oghbasilasie H, Louhenkilpi S (2012) Viscosity models for molten slags, research report, Aalto University. Helsinki, Finland https://aaltodoc.aalto.fi/bitstream/handle/123456789/3640/isbn9789526046037.pdf?sequence=1&isAllowed=y Google Scholar
- 10.Urbain G, Cambier F, Deletter M, Anseau MR (1981) Viscosity of silicate melts. Trans J Br Ceram Soc 80(4):139Google Scholar
- 11.Bauné E, Bonnet C, Liu S (2000) Reconsidering the basicity of a FCAW consumable-part 1: solidified slag composition of a FCAW consumable as a basicity indicator. Weld J 79(3):57s–65sGoogle Scholar
- 12.Mills K (2011) The estimation of slag properties: short course presented as part of Southern African Pyrometallurgy, http://www.pyrometallurgy.co.za/KenMills/index.html, Abgerufen am: 04.08.2016
- 13.Schwemmer DD, Olson DL, Williamson DL (1979) The relationship of weld penetration to the welding flux. Weld J 58(5):153s–160sGoogle Scholar