Numerical study on a thermal process in friction spot welding of Al-Zn-Mg-Cu alloy

  • Yunqiang Zhao
  • Chungui Wang
  • Chunlin Dong
  • Jun Deng
  • Jinhong Tan
Research Paper
  • 99 Downloads

Abstract

A three-dimensional coupled thermo-mechanical model under consideration of local melting was developed to study the temperature distribution and thermal cycles during friction spot welding of Al-Zn-Mg-Cu alloy. The results indicate that the high-temperature region during welding was located in the sleeve cavity and the temperature gradient was higher in the thickness direction in the stir zone (SZ). At relatively high plunging depth and rotation speed, the peak temperature in the SZ was higher than the solidus temperature of Al-Zn-Mg-Cu alloy (532 °C). The peak temperature in thermal mechanically affected zone (TMAZ) was higher than the solution temperature (300 °C) but lower than the solidus temperature. The peak temperature in the heat-affected zone (HAZ) was higher than the aging temperature (170 °C). With the increase of the sleeve plunging depth, the peak temperatures in all the zones constantly increased. With the increase of the tool rotation speed, the peak temperature in the SZ and TMAZ first increased and then decreased, while the peak temperature in the HAZ constantly increased.

Keywords

Friction spot welding Temperature field Welding thermal cycle 

Notes

Funding information

The authors are grateful to be supported by the Science and Technology Plan Project of Guangzhou City (201807010068 and 201704030056), the Science and Technology Plan Project of Guangdong Province (2015B090922011), and the Implmenting Innovation-Driven Development Capacity Building Special Funds project of Guangdong Academy of Sciences (2018GDASCX-0113).

References

  1. 1.
    Zhao YQ, Liu HJ, Chen SX, Lin Z, Hou JC (2014) Effects of sleeve plunge depth on microstructures and mechanical properties of friction spot welded alclad 7B04-T74 aluminum alloy. Mater Des 62:40–46CrossRefGoogle Scholar
  2. 2.
    Rosendo T, Parra B, Tier MAD, da Silva AAM, dos Santos JF, Strohaecker TR, Alcântara NG (2011) Mechanical and microstructural investigation of friction spot welded AA6181-T4 aluminium alloy. Mater Des 32:1094–1100CrossRefGoogle Scholar
  3. 3.
    Campanelli LC, Suhuddin UFH, Antonialli AIS, dos Santos JF, de Alcantara NG, Bolfarini C (2013) Metallurgy and mechanical performance of AZ31 magnesium alloy friction spot welds. J Mater Process Technol 213:515–521CrossRefGoogle Scholar
  4. 4.
    Gao C, Gao R, Ma Y (2015) Microstructure and mechanical properties of friction spot welding aluminium–lithium 2A97 alloy. Mater Des 83:719–727CrossRefGoogle Scholar
  5. 5.
    Suhuddin U, Fischer V, Kroeff F, dos Santos JF (2014) Microstructure and mechanical properties of friction spot welds of dissimilar AA5754 Al and AZ31 Mg alloys. Mater Sci Eng A 590:384–389CrossRefGoogle Scholar
  6. 6.
    D'Urso G (2015) Thermo-mechanical characterization of friction stir spot welded AA6060 sheets: experimental and FEM analysis. J Manuf Process 17:108–119CrossRefGoogle Scholar
  7. 7.
    Cox CD, Gibson BT, Strauss AM, Cook GE (2014) Energy input during friction stir spot welding. J Manuf Process 16:479–484CrossRefGoogle Scholar
  8. 8.
    Gao C, Ma Y, Tang L-Z, Wang P, Zhang X (2017) Microstructural evolution and mechanical behavior of friction spot welded 2198-T8 Al-Li alloy during aging treatment. Mater Des 115:224–230CrossRefGoogle Scholar
  9. 9.
    Bhat NN, Kumari K, Dutta S, Pal SK, Pal S (2015) Friction stir weld classification by applying wavelet analysis and support vector machine on weld surface images. J Manuf Process 20:274–281CrossRefGoogle Scholar
  10. 10.
    Hamdollahzadeh A, Bahrami M, Nikoo MF, Yusefi A, Givi MKB, Parvin N (2015) Microstructure evolutions and mechanical properties of nano-SiC-fortified AA7075 friction stir weldment: the role of second pass processing. J Manuf Process 20:367–373CrossRefGoogle Scholar
  11. 11.
    Xiao R, Zhang X (2014) Problems and issues in laser beam welding of aluminum-lithium alloys. J Manuf Process 16:166–175CrossRefGoogle Scholar
  12. 12.
    Pieta G, dos Santos J, Strohaecker TR, Clarke T (2014) Optimization of friction spot welding process parameters for AA2198-T8 sheets. Mater Manuf Process 29:934–940CrossRefGoogle Scholar
  13. 13.
    Zhao YQ, Liu HJ, Lin Z, Chen SX, Hou JC (2014) Microstructures and mechanical properties of friction spot welded Alclad 7B04-T74 aluminium alloy. Sci Technol Weld Join 19:617–622CrossRefGoogle Scholar
  14. 14.
    Suhuddin UFH, Fischer V, dos Santos JF (2013) The thermal cycle during the dissimilar friction spot welding of aluminum and magnesium alloy. Scripta Mater 68:87–90CrossRefGoogle Scholar
  15. 15.
    He XC, Gu FS, Ball A (2014) A review of numerical analysis of friction stir welding. Prog Mater Sci 65:1–66CrossRefGoogle Scholar
  16. 16.
    Hilgert J, Schmidt HNB, dos Santos JF, Huber N (2011) Thermal models for bobbin tool friction stir welding. J Mater Process Technol 211:197–204CrossRefGoogle Scholar
  17. 17.
    Shi L, Wu CS, Liu HJ (2015) The effect of the welding parameters and tool size on the thermal process and tool torque in reverse dual-rotation friction stir welding. Int J Mach Tools Manuf 91:1–11CrossRefGoogle Scholar
  18. 18.
    H-j Z, H-j L, Yu L (2013) Thermal modeling of underwater friction stir welding of high strength aluminum alloy. Trans Nonferrous Metal Soc China 23:1114–1122CrossRefGoogle Scholar
  19. 19.
    Khandkar MZH, Khan JA, Reynolds AP (2003) Prediction of temperature distribution and thermal history during friction stir welding: input torque based model. Sci Technol Weld Join 8:165–174CrossRefGoogle Scholar
  20. 20.
    Zhang Z, Wu Q (2015) Numerical studies of tool diameter on strain rates, temperature rises and grain sizes in friction stir welding. J Mech Sci Technol 29:4121–4128CrossRefGoogle Scholar
  21. 21.
    Buffa G, Pellegrino S, Fratini L (2014) Analytical bonding criteria for joint integrity prediction in friction stir welding of aluminum alloys. J Mater Process Technol 214:2102–2111CrossRefGoogle Scholar
  22. 22.
    Shi L, Wu CS, Liu HJ (2014) Numerical analysis of heat generation and temperature field in reverse dual-rotation friction stir welding. Int J Adv Manuf Technol 74:319–334CrossRefGoogle Scholar
  23. 23.
    Fratini L, Buffa G, Shivpuri R (2010) Mechanical and metallurgical effects of in process cooling during friction stir welding of AA7075-T6 butt joints. Acta Mater 58:2056–2067CrossRefGoogle Scholar
  24. 24.
    Buffa G, Patrinostro G, Fratini L (2014) Using a neural network for qualitative and quantitative predictions of weld integrity in solid bonding dominated processes. Comput Struct 135:1–9CrossRefGoogle Scholar
  25. 25.
    Tutunchilar S, Haghpanahi M, Givi MKB, Asadi P, Bahemmat P (2012) Simulation of material flow in friction stir processing of a cast Al-Si alloy. Mater Des 40:415–426CrossRefGoogle Scholar
  26. 26.
    Gerlich A, Avramovic-Cingara G, North TH (2006) Stir zone microstructure and strain rate during Al 7075-T6 friction stir spot welding. Metall Mater Trans A 37A:2773–2786CrossRefGoogle Scholar
  27. 27.
    Song M, Kovacevic R (2003) Thermal modeling of friction stir welding in a moving coordinate system and its validation. Int J Mach Tools Manuf 43:605–615CrossRefGoogle Scholar
  28. 28.
    Zhao Y, Liu H, Yang T, Lin Z, Hu Y (2015) Study of temperature and material flow during friction spot welding of 7B04-T74 aluminum alloy. Int J Adv Manuf Technol 83:1–9CrossRefGoogle Scholar
  29. 29.
    Gerlich A, Yamamoto M, North TH (2008) Local melting and tool slippage during friction stir spot welding of Al-alloys. J Mater Sci 43:2–11CrossRefGoogle Scholar

Copyright information

© International Institute of Welding 2018

Authors and Affiliations

  1. 1.Guangdong Provincial Key Laboratory of Advanced Welding TechnologyGuangdong Welding Institute (China-Ukaine E.O. Paton Institute of Welding)GuangzhouChina

Personalised recommendations